Process for coating cellulosic plastic articles
Assignee: Nippon Sheet Glass Co Ltd
•
Filing: 1977-03-22
•
Granted: 1978-07-04
•
Expires: 1997-03-22
Abstract
Abstract A cellulosic plastic article, such as an article of cellulose propionate, cellulose acetate butyrate or cellulose butyrate, is coated with good adhesion of an applied coat by pretreating the surface of the article with an aqueous solution containing an alkali metal and an alcohol, then applying a coating composition comprising a thermosetting resin to the treated surface, and curing the coating.
Inventors
- 👤 Motoaki Yoshida
- 👤 Nobuhiro Sakata
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 04:59
CPC Classifications
C; C08; C08J; C08J7/00; C08J7/12; C08J7/04; C08J7/0427; C08J7/043; C08J7/046; C08J2301/00; C08J2301/08; C08J2301/10
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
93 words
A process for coating a cellulosic plastic article which comprises contacting the surface of a cellulosic plastic article with an aqueous solution containing an alkali metal hydroxide or alkoxide in a concentration of 3 to 40% by weight calculated as the hydroxide and an alcohol in a concentration of 3 to 40% by weight, wherein the product of the alkali metal concentration in percent by weight multiplied by the alcohol concentration in percent by weight is 50 to 200; then coating a thermosetting resin on the treated surface and finally curing the coating.
Claim 2
Dependent Claim
93 words
A process for coating a cellulosic plastic article which comprises contacting the surface of a cellulosic plastic article with an aqueous solution containing an alkali metal hydroxide or alkoxide in a concentration of 3 to 40% by weight calculated as the hydroxide and an alcohol in a concentration of 3 to 40% by weight, wherein the product of the alkali metal concentration in percent by weight multiplied by the alcohol concentration in percent by weight is 50 to 200; then coating a thermosetting resin on the treated surface and finally curing the coating.
Claim 3
Dependent Claim
18 words
The process of claim 1 wherein the cellulosic plastic is cellulose propionate, cellulose acetate butyrate, or cellulose butyrate.
Claim 4
Dependent Claim
31 words
The process of claim 1 wherein the contacting of the aqueous solution with the surface of the plastic article is performed at 10° to 40° C. for 3 to 30 minutes.
Claim 5
Dependent Claim
14 words
The process of claim 1 wherein the alkali metal is sodium, potassium, or both.
Claim 6
Dependent Claim
24 words
The process of claim 1 wherein the alcohol is at least one member selected from the group consisting of methanol, ethanol, n-propanol, and iso-propanol.
Claim 7
Dependent Claim
28 words
The process of claim 1 wherein the thermosetting resin is a melamine-type resin, a melamine alkyl resin, a melamine acrylic resin, an epoxy-type resin, or a urea-type resin.
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-07-03 | 1982-01-02 | 1982-07-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-07-03 | 1986-01-02 | 1986-07-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-07-03 | 1990-01-02 | 1990-07-04 | $7700.00 | Window Closed / Lapsed |