US4098860A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Production of biaxially drawn film of polyamide blend
Assignee: Toyobo Co Ltd
•
Filing: 1976-08-04
•
Granted: 1978-07-04
•
Expires: 1996-08-04
Abstract
Abstract A process for preparing a biaxially stretched film of polyamide blend, which comprises (1) extruding a polyamide blend in melt to make an unstretched film and (2) stretching the unstretched film first in a machine direction with a stretch speed of about 40,000 to 60,000,000 %/minute in a draw ratio of about 2 to 6 and then in a transverse direction with a stretch speed of about 500 to 100,000 %/minute in a draw ratio of about 2 to 6, or (2') stretching the unstretched film first to make a uniaxially stretched film having a plane orientation index of about 0.6 to 1.5 and then stretching the uniaxially stretched film in a direction being substantially at a right angle to the direction at the previous stretching, said polyamide blend comprising an aliphatic polyamide and a polyamide containing in the molecule at least about 70 mol % of the repeating units constituted with metaxylylenediamine or its mixture with paraxylylenediamine (of which the content is not more than about 30 mol % based on the combined amount of metaxylylenediamine and paraxylylenediamine) and at least one α,ω-aliphatic dicarboxylic acid having 6 to 10 carbon atoms in a proportion of about 97 : 3 to 80 : 20 by weight.
Inventors
- 👤 Yoshitaka Etou
- 👤 Mikio Matsuoka
- 👤 Shizuo Matsumoto
- 👤 Takamichi Zoda
- 👤 Katsumi Gunji
- 👤 Toshihiko Ohta
- 👤 Kazuo Tamaki
- 👤 Koichi Matsunami
- 👤 Tetsushi Murakami
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 21:26
CPC Classifications
B; B29; B29C; B29C55/00; B29C55/02; B29C55/10; B29C55/12; B29C55/14; B29C55/143; B29K; B29K2077/00
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
188 words
A process for preparing a biaxially stretched film of polyamide blend which comprises extruding a polyamide blend in melt to make an unstretched film, stretching the unstretched film in a machine direction with a stretch speed of about 40,000 to 60,000,000%/minute in a draw ratio of about 2 to 6 to make a uniaxially stretched film having a plane orientation index of about 0.6 to 1.5 and then stretching the uniaxially stretched film in a transverse direction with a stretch speed of about 500 to 100,000%/minute in a draw ratio of about 2 to 6, said polyamide blend comprising: (1) an aliphatic polyamide and (2) a polyamide containing in the molecule at least about 70 mol % of the repeating units constituted with metaxylylenediamine or its mixture with paraxylylenediamine, wherein when paraxylylenediamine is present, its amount is not more than about 30 mol % based on the combined amount of metaxylylenediamine or paraxylylenediamine and at least one α,ω-aliphatic dicarboxylic acid having 6 to 10 carbon atoms, said aliphatic polyamide and polyamide (2) being present in a proportion of about 97 : 3 to 80 : 20 by weight.
Claim 2
Dependent Claim
188 words
A process for preparing a biaxially stretched film of polyamide blend which comprises extruding a polyamide blend in melt to make an unstretched film, stretching the unstretched film in a machine direction with a stretch speed of about 40,000 to 60,000,000%/minute in a draw ratio of about 2 to 6 to make a uniaxially stretched film having a plane orientation index of about 0.6 to 1.5 and then stretching the uniaxially stretched film in a transverse direction with a stretch speed of about 500 to 100,000%/minute in a draw ratio of about 2 to 6, said polyamide blend comprising: (1) an aliphatic polyamide and (2) a polyamide containing in the molecule at least about 70 mol % of the repeating units constituted with metaxylylenediamine or its mixture with paraxylylenediamine, wherein when paraxylylenediamine is present, its amount is not more than about 30 mol % based on the combined amount of metaxylylenediamine or paraxylylenediamine and at least one α,ω-aliphatic dicarboxylic acid having 6 to 10 carbon atoms, said aliphatic polyamide and polyamide (2) being present in a proportion of about 97 : 3 to 80 : 20 by weight.
Claim 3
Dependent Claim
18 words
The process according to claim 1, wherein the thickness of the film is about 10 to 500 μ.
Claim 4
Dependent Claim
49 words
The process according to claim 1, wherein the aliphatic polyamide is an aliphatic polyamide selected from the group consisting of nylon 4, nylon 6, nylon 9, nylon 11, nylon 6.6, nylon 6.10 and nylon 10.10 and the copolymers comprising the monomeric constituents of those polymers, which forms α-form crystals.
Claim 5
Dependent Claim
125 words
The process according to claim 1, wherein the polyamide is a polymer selected from the group consisting of polymetaxylylene adipamide, polymetaxylylene pimelamide, polymetaxylylene suberamide, polymetaxylylene azelamide, polymetaxylylene sebacamide, metaxylylene/paraxylylene adipamide copolymer, metaxylylene/paraxylylene pimelamide copolymer, metaxylylene/paraxylylene suberamide copolymer, metaxylylene/paraxylylene azelamide copolymer and metaxylylene/paraxylylene sebacamide copolymer, and a block polyetheramide constituted with metaxylylenediamide or its mixture with paraxylylenediamine having a paraxylylenediamine content of not more than about 30 mol % as the diamine component, an α,ω-aliphatic dicarboxylic acid having 6 to 10 carbon atoms as the dicarboxylic acid component and a polyether residue having a molecular weight of about 2,000 to 20,000, the polyether content being about 0.2 to 10% by weight based on the combined amount of the diamine and dicarboxylic acid components and the polyether.
Claim 6
Dependent Claim
98 words
The process according to claim 4, wherein the block polyetheramide is a copolymer constituted with the monomeric constituents of a polyamide and the residue of a polyether having a molecular weight of about 2,000 to 20,000, said polyamide being a member selected from the group consisting of polymetaxylylene adipamide, polymetaxylylene pimelamide, polymetaxylylene suberamide, polymetaxylylene azelamide, polymetaxylylene sebacamide, metaxylylene/paraxylylene adipamide copolymer, metaxylylene/paraxylylene pimelamide copolymer, metaxylylene/paraxylylene suberamide copolymer, metaxylylene/paraxylylene azelamide copolymer and metaxylylene/paraxylylene sebacamide copolymer and the polyether content in the copolymer being about 0.2 to 10% by weight based on the combined amount of the polyamide and the polyether.
Claim 7
Dependent Claim
12 words
The process according to claim 5, wherein the polyether is polyethylene oxide.
Claim 8
Dependent Claim
52 words
The process according to claim 1, wherein the temperature at the stretching in machine direction is above the glass transition point and below about 130° C. and the temperature at the stretching in transverse direction is higher than the temperature at the stretching in machine direction and lower than about 160° C.
Claim 9
Dependent Claim
51 words
The process according to claim 1, wherein the biaxially stretched film is further subjected to heat treatment at a temperature not less than about 5° C. higher than the higher temperature of the temperatures at the stretching in machine and transverse directions but lower than the melting point of the film.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-07-03 | 1982-01-02 | 1982-07-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-07-03 | 1986-01-02 | 1986-07-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-07-03 | 1990-01-02 | 1990-07-04 | $7700.00 | Window Closed / Lapsed |