US4098753A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Ester-plasticized polyvinyl chloride resin composition containing molybdenum flame retardant and smoke suppressant agent
Assignee: Cyprus Amax Minerals Co
•
Filing: 1976-08-16
•
Granted: 1978-07-04
•
Expires: 1996-08-16
Abstract
Abstract A flame resistant and smoke suppressed plasticized polyvinyl chloride polymer containing from about 20 to about 80 parts per hundred resin (phr) of an ester-type plasticizer and an effective amount of a flame retardant and smoke suppressant agent comprising an inorganic molybdenum compound such as molybdenum oxides and metal molybdates. In accordance with a preferred embodiment, the flame retardant and smoke suppressant agent further includes a controlled effective amount of an antimony compound such as antimony oxide in combination with the molybdenum compound imparting synergistic flame retardancy and smoke suppressing characteristics to the plasticized polyvinyl chloride resin formulation.
Inventors
- 👤 George A. Tsigdinos
- 👤 Fred W. Moore
- 👤 Valerie J. Kuck
- 👤 Emanuele Scalco
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 12:55
CPC Classifications
C; C08; C08K; C08K3/00; C08K3/18; C08K3/24; C08K5/00; C08K5/04; C08K5/10; C08K9/00; C08K9/02; Y; Y10; Y10S; Y10S260/00; Y10S260/24
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
124 words
A flame resistant and smoke suppressed plasticized polyvinyl chloride polymer composition consisting essentially of a polyvinyl chloride polymer, from about 20 phr to about 80 phr of an ester-type plasticizer selected from the group consisting of phthalates, azelates, adipates, trimellitates, and mixtures thereof, and a flame retardant and smoke suppressant agent consisting of a mixture of a molybdenum compound selected from the group consisting of molybdenum oxides and molybdate salts and an antimony compound selected from the group consisting of antimony oxide, sodium antimonate, potassium antimonate, and mixtures thereof present in an amount of about 1 phr to about 8 phr, said antimony compound present in an amount of about 0.5 parts up to about 2 parts per part of said molybdenum compound present.
Claim 2
Dependent Claim
124 words
A flame resistant and smoke suppressed plasticized polyvinyl chloride polymer composition consisting essentially of a polyvinyl chloride polymer, from about 20 phr to about 80 phr of an ester-type plasticizer selected from the group consisting of phthalates, azelates, adipates, trimellitates, and mixtures thereof, and a flame retardant and smoke suppressant agent consisting of a mixture of a molybdenum compound selected from the group consisting of molybdenum oxides and molybdate salts and an antimony compound selected from the group consisting of antimony oxide, sodium antimonate, potassium antimonate, and mixtures thereof present in an amount of about 1 phr to about 8 phr, said antimony compound present in an amount of about 0.5 parts up to about 2 parts per part of said molybdenum compound present.
Claim 3
Dependent Claim
30 words
The polymer composition as defined in claim 1, in which said flame retardant and smoke suppressant agent is present in an amount of about 2 phr to about 4 phr.
Claim 4
Dependent Claim
41 words
The polymer composition as defined in claim 1, in which said flame retardant and said smoke suppressant agent is present in the form of particles of an average size of less than 20 mesh and distributed substantially uniformly throughout said composition.
Claim 5
Dependent Claim
41 words
The polymer composition as defined in claim 1, wherein said flame retardant and smoke suppressant agent is present in the form of particles of an average particle size of less than about 10 microns and distributed substantially uniformly throughout said composition.
Claim 6
Dependent Claim
15 words
The polymer composition as defined in claim 1, wherein said molybdenum compound comprises molybdenum trioxide.
Claim 7
Dependent Claim
15 words
The polymer composition as defined in claim 1, wherein said molybdenum compound comprises molybdenum dioxide.
Claim 8
Dependent Claim
17 words
The polymer composition as defined in claim 1, wherein said molybdenum compound comprises an ammonium molybdate salt.
Claim 9
Dependent Claim
15 words
The polymer composition as defined in claim 1, wherein said molybdenum compound comprises calcium molybdate.
Claim 10
Dependent Claim
15 words
The polymer composition as defined in claim 1, wherein said molybdenum compound comprises sodium molybdate.
Claim 11
Dependent Claim
15 words
The polymer composition as defined in claim 1, wherein said molybdenum compound comprises zinc molybdate.
Claim 12
Dependent Claim
32 words
The polymer composition as defined in claim 1, wherein at least a portion of said molybdenum compound is present in the form of a coating on the surfaces of an extender filler.
Claim 13
Dependent Claim
26 words
The polymer composition as defined in claim 11, in which the coated said extender filler contains from about 1% to about 20% of said molybdenum compound.
Claim 14
Dependent Claim
33 words
The polymer composition as defined in claim 1, in which at least a portion of said antimony compound is present in the form of a coating on the surfaces of an extender filler.
References Cited (Backward Citations)
US3014000A
Cited
US3892667A
Cited
US3741893A
Cited
US3845001A
Cited
US3870679A
Cited
US3900441A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-07-03 | 1982-01-02 | 1982-07-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-07-03 | 1986-01-02 | 1986-07-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-07-03 | 1990-01-02 | 1990-07-04 | $7700.00 | Window Closed / Lapsed |