US4098737A Expired / Lapsed US ⏱️ 0.0 years remaining

Treatment of vulcanized rubber

Assignee: NRI Pennsylvania Inc
•
Filing: 1975-12-09
•
Granted: 1978-07-04
•
Expires: 1995-12-09
📄 Original PDF 🌐 Google Patents 🔄 Sync Now

Abstract

Abstract The invention provides finely divided vulcanized rubber having a particle size of generally less than 20 microns for re-use in the rubber industry. Vulcanizates produced from compositions containing the finely divided vulcanized rubber, either as the sole rubber component or in admixture with unvulcanized rubber, have properties significantly better than those of vulcanizates of similar compositions containing conventional reclaimed rubbers. Vulcanized rubber is converted into the finely divided rubber by the steps of (1) contacting vulcanized rubber with a fatty acid, (2) contacting the product of step (1) with a solid alkali and (3) forming a dispersion of the product of step (2) with a liquid which dissolves the alkali but does not affect the rubber. Alternatively, the finely divided vulcanized rubber results from the steps of (1) contacting the vulcanized rubber with a liquid effective to swell the rubber and thereby weaken it e.g. tetrahydrofuran, (2) comminuting the weakened material and (3) removing the liquid from the comminuted material.

Inventors

  • 👤 Timothy Charles Philip Lee
  • 👤 William Millns

Bibliographic Details

Application Number —
Jurisdiction US
Data Source google_patents
Last Synchronized 2026-10-30 23:40
CPC Classifications
C; C08; C08J; C08J11/00; C08J11/04; C08J11/06; C08J3/00; C08J3/12; C08L; C08L19/00; C08L19/003; C08J2321/00; Y; Y02; Y02W; Y02W30/00; Y02W30/50; Y02W30/62

Claims Analysis

Total Claims: 13
Claim 1
Independent Claim 67 words
A method of converting vulcanised rubber into finely-divided vulcanised rubber which comprises the steps: (1) contacting vulcanised rubber with a fatty acid, (2) contacting the product of step (1) with a solid alkali, (3) forming a dispersion of the product of step (2) by passing the product of step (2) together with water through an abrasive disc mill, and (4) removing the finely-divided rubber from the dispersion.
Claim 2
Independent Claim 67 words
A method of converting vulcanised rubber into finely-divided vulcanised rubber which comprises the steps: (1) contacting vulcanised rubber with a fatty acid, (2) contacting the product of step (1) with a solid alkali, (3) forming a dispersion of the product of step (2) by passing the product of step (2) together with water through an abrasive disc mill, and (4) removing the finely-divided rubber from the dispersion.
Claim 3
Dependent Claim 27 words
A method as claimed in claim 1 wherein in step (1) the vulcanised rubber is allowed to absorb up to 15% by weight of the fatty acid.
Claim 4
Dependent Claim 15 words
A method as claimed in claim 2 in which the fatty acid is oleic acid.
Claim 5
Dependent Claim 24 words
A method as claimed in claim 2, in which the fatty acid/rubber composition is formed into friable sheets prior to formation of the dispersion.
Claim 6
Dependent Claim 23 words
A method as claimed in claim 1 in step (2) of which the product of step (1) is dusted with the solid alkali.
Claim 7
Dependent Claim 14 words
A method as claimed in claim 5 in which the alkali is sodium hydroxide.
Claim 8
Dependent Claim 28 words
A method as claimed in claim 5 in which the amount of alkali used is 2 to 25 parts by weight per 100 parts by weight of rubber.
Claim 9
Dependent Claim 34 words
The method of claim 1 wherein the product of step (2) is comminuted in said disc mill into particles and at least 90% of said particles have a particle size less than 20 microns.
Claim 10
Dependent Claim 19 words
The method of claim 1, wherein the discs of said disc mill are 46 grit silicon carbide abrasive stones.
Claim 11
Dependent Claim 49 words
The method of claim 8 wherein the finely-divided rubber of step (4) is further characterized by yielding a vulcanizate having a tensile strength of above 9 MN/m 2 and a tear strength above 55 N/Std. when a rubber composition containing said particles as the sole rubber component is vulcanized.
Claim 12
Dependent Claim 99 words
The process of claim 8 wherein the finely-divided rubber of step (4) is further characterized by yielding a vulcanizate having a tensile strength of above 9 MN/m 2 and a tear strength above 55 N/Std. when a rubber composition containing said particles as the sole rubber component is vulcanised by compounding 100 parts by weight of said particles with 2 parts of zinc oxide, 1 part of stearic acid, 1 part of polymerized 1,2-dihydro-2,2,4-trimethyl quinoline rubber antioxidant, 0.27 parts of cyclohexyl-benzthiazyl-sulphenamide, 0.24 parts of diphenylguanine and 0.53 parts of sulfur, and press molded to optimum cure at 150° C.
Claim 13
Dependent Claim 15 words
The process of claim 1 wherein the product of step (2) is dry and friable.

References Cited (Backward Citations)

US1680915A Cited
US1932661A Cited
US2096336A Cited
US2853742A Cited
US3790511A Cited

USPTO Annuity & Maintenance Windows

Annuity Stage Window Opens Payment Deadline Surcharge Period Until Estimated Fee Status
3.5 Years (Year 4) 1981-07-03 1982-01-02 1982-07-04 $2000.00 Window Closed / Lapsed
7.5 Years (Year 8) 1985-07-03 1986-01-02 1986-07-04 $3760.00 Window Closed / Lapsed
11.5 Years (Year 12) 1989-07-03 1990-01-02 1990-07-04 $7700.00 Window Closed / Lapsed

Assigned Categories & Tags

No categories assigned to this patent yet.

Assign Category Tag