Process of producing cross-linked urethane-group comprising foams of open-cell structure
Assignee: Evonik Operations GmbH
•
Filing: 1976-07-13
•
Granted: 1978-07-04
•
Expires: 1996-07-13
Abstract
Abstract In the disclosed process of producing resilient open-celled, cross-linked polyurethane foams, by foaming polyol, a polyisocyanate, catalyst and blowing agent, the foaming is effected in the presence of a cross-linker which is a saturated or unsaturated, aliphatic, cycloaliphatic, heteroaliphatic or arylaliphatic crystalline polyhydroxy compound having at least three hydroxy groups. The crystalline polyhydroxy compound is insoluble or only slightly soluble in the polyl to be foamed and melts within the temperature range of about 60 - 160° C. The amount of crystalline polyhydroxy compound to be used corresponds to about 0.1 - 5.0 hydroxy equivalent weights per 1 hydroxy equivalent weight of the polyol to be foamed. Additionally, a compound that breaks down the association of water molecules can be added.
Inventors
- 👤 Hans-Joachim Kollmeier
- 👤 Gerd Rossmy
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 12:23
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/65; C08G18/66; C08G18/6666; C08G18/667; C08G18/6674; C08G18/6677; C08G18/08; C08G18/16; C08G18/166; C08G18/168; C08G18/18; C08G18/1875; C08G18/30; C08G18/38; C08G18/3819; C08G18/3842; C08G18/3851; C08G18/6681; C08G18/6688; C08G2110/00; C08G2110/0041; C08G2110/005
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
164 words
A process for producing cross-linked, resilient, urethane-group comprising foams of open-cell structure which comprises foaming a system of (a) di or trifunctional active hydrogen atom comprising a polyetherpolyol of hydroxy equivalent weights of between about 700 -5,000; (b) a di or trifunctional polyisocyanate; (c) catalyst; (d) blowing agent; and (e) a cross-linker, said cross-linker being a crystalline saturated or unsaturated, aliphatic, cycloaliphatic, heteroaliphatic or arylaliphatic polyhydroxy compound having at least three hydroxy groups which, at room temperature, is insoluble or only slightly soluble in the system to be foamed and which melts in a temperature range of about 60° to 160° C., said cross-linker being used in quantities of 0.1 to 5.0 hydroxy equivalent weights calculated on one hydroxy equivalent weight of the polyol in the system, and wherein about 0.5 to 50% by weight, based on the amount of water in the foaming system, of compounds which break down the association of water molecules, are added to the foaming system prior to foaming.
Claim 2
Dependent Claim
164 words
A process for producing cross-linked, resilient, urethane-group comprising foams of open-cell structure which comprises foaming a system of (a) di or trifunctional active hydrogen atom comprising a polyetherpolyol of hydroxy equivalent weights of between about 700 -5,000; (b) a di or trifunctional polyisocyanate; (c) catalyst; (d) blowing agent; and (e) a cross-linker, said cross-linker being a crystalline saturated or unsaturated, aliphatic, cycloaliphatic, heteroaliphatic or arylaliphatic polyhydroxy compound having at least three hydroxy groups which, at room temperature, is insoluble or only slightly soluble in the system to be foamed and which melts in a temperature range of about 60° to 160° C., said cross-linker being used in quantities of 0.1 to 5.0 hydroxy equivalent weights calculated on one hydroxy equivalent weight of the polyol in the system, and wherein about 0.5 to 50% by weight, based on the amount of water in the foaming system, of compounds which break down the association of water molecules, are added to the foaming system prior to foaming.
Claim 3
Dependent Claim
15 words
The process of claim 1 wherein said polyhydroxy compound has primary and/or secondary hydroxy groups.
Claim 4
Dependent Claim
18 words
The process of claim 1 wherein the polyhydroxy compound contains 3 to 8 primary or secondary hydroxy groups.
Claim 5
Dependent Claim
18 words
The process of claim 1 wherein said polyhydroxy compound melts in a range of 80° to 130° C.
Claim 6
Dependent Claim
34 words
The process of claim 1 wherein said cross-linker is present in the system in amounts of 0.2 to 3.0 hydroxy equivalent weights, calculated on one hydroxy equivalent weight of the polyol to be foamed.
Claim 7
Dependent Claim
18 words
The process of claim 1 wherein said cross-linker is dispersed in the polyol used in the foaming system.
Claim 8
Dependent Claim
15 words
The process of claim 1 wherein said cross-linker is sorbite, trimethylolmelamine, hexamethylolmelamine, glucose, or erythrite.
Claim 9
Dependent Claim
13 words
The process of claim 1 wherein said system comprises additionally emulsifier or stabilizer.
Claim 10
Dependent Claim
35 words
The process of claim 1 wherein the cross-linker is first dispersed in a polyol which is identical with or different from the polyol to be foamed, whereafter the dispersion is added to the foaming system.
Claim 11
Dependent Claim
33 words
The process of claim 1 wherein first a dispersion of the cross-linker in a suitable dispersion agent compatible with the foaming system is formed, whereafter the dispersion is added to the foaming system.
Claim 12
Dependent Claim
39 words
The process of claim 1 wherein all or a portion of the compounds which break down the association of water molecules, is dissolved in the polyol solutions which are dispersed, with precipitation of the polyol, in the polyether polyol.
Claim 13
Dependent Claim
68 words
The process of claim 1 wherein the compound which breaks down the association of water molecules has the general formula ##STR3## wherein R 1 is a CH 3 --, NH 2 --, NHR 3 -- or NR 2 3 -- group, R 3 is an alkyl group with 1 to 4 carbon atoms and R 2 is hydrogen or an alkyl group with 1 to 4 carbon atoms.
Claim 14
Dependent Claim
10 words
The process of claim 12 wherein the compound is urea.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-07-03 | 1982-01-02 | 1982-07-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-07-03 | 1986-01-02 | 1986-07-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-07-03 | 1990-01-02 | 1990-07-04 | $7700.00 | Window Closed / Lapsed |