Codeposition of a metal and fluorocarbon resin particles
Assignee: Akzo NV
•
Filing: 1976-09-30
•
Granted: 1978-07-04
•
Expires: 1996-09-30
Abstract
Abstract Polyfluorocarbon resin particles and metals are codeposition from electroplating baths to form coating layers of a very homogeneous structure, when said positively charged resin particles having a particle size of less than about 10 mu m are kept dispersed in said baths in the presence of both a cationic and a nonionic fluorocarbon surfactant in a molar ratio between 25:1 and 1:3.5 and in a total amount of at least 3 x 10-3 millimoles per m2 of surface area of said particles.
Inventors
- 👤 Kees Helle
- 👤 Robert Cornelis Groot
- 👤 Andries Kamp
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 19:07
CPC Classifications
C; C25; C25D; C25D15/00; C25D15/02
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
134 words
In a process for applying to an electrically conductive substrate acting as a cathode a composite coating made up of a polyfluorocarbon resin and a metal, wherein the resinous particles have an average particle size of less than about 10 μm and are kept dispersed in a concentration of about 3 to 150 grammes per liter of bath solution in the presence of a cationic fluorocarbon surfactant and a nonionic surfactant, the improvement comprising: a. using for the nonionic surface active compound a fluorocarbon compound; b. maintaining the molar ratio between the cationic surface active compound and the nonionic surface active fluorocarbon compound between 25:1 and 1:3.5; and c. maintaining the total amount of surface active fluorocarbon compounds above 3 × 10 -3 mmoles per m 2 of surface area of the polyfluorocarbon particles.
Claim 2
Dependent Claim
134 words
In a process for applying to an electrically conductive substrate acting as a cathode a composite coating made up of a polyfluorocarbon resin and a metal, wherein the resinous particles have an average particle size of less than about 10 μm and are kept dispersed in a concentration of about 3 to 150 grammes per liter of bath solution in the presence of a cationic fluorocarbon surfactant and a nonionic surfactant, the improvement comprising: a. using for the nonionic surface active compound a fluorocarbon compound; b. maintaining the molar ratio between the cationic surface active compound and the nonionic surface active fluorocarbon compound between 25:1 and 1:3.5; and c. maintaining the total amount of surface active fluorocarbon compounds above 3 × 10 -3 mmoles per m 2 of surface area of the polyfluorocarbon particles.
Claim 3
Dependent Claim
34 words
The process of claim 1 wherein the surface active fluorocarbon compounds are present in an amount of 6.10 -3 to 12.10 -3 mmoles per m 2 of the surface area of the resin particles.
Claim 4
Dependent Claim
41 words
The process of claim 1 wherein the nonionic surface active fluorocarbon compound is present in an amount of about 17 to 36 mole percent of the total amount of surface active fluorocarbon compounds used for the dispersion of the resin particles.
Claim 5
Dependent Claim
37 words
The process of claim 1, wherein the nonionic fluorocarbon compound is present in an amount of about 26 mole percent of the total amount of surface active fluorocarbon compounds used for the dispersion of the resin particles.
Claim 6
Dependent Claim
30 words
The process of claim 1 wherein said nonionic fluorocarbon compound is a wetting agent which satisfies the following structural formula: ##STR13## where C 8 F 17 represents a straight-chain fluorocarbon.
Claim 7
Dependent Claim
69 words
The process of claim 1 in which to an electrically conductive substrate there is applied a composite coating made up of a polyfluorocarbon resin, a metal and, if desired particles of a different material, the improvement comprising in that on to the resulting coating serving as cathode there is subsequently deposited from an electroplating bath of a different composition a metal and, if desired, particles of a different material.
Claim 8
Dependent Claim
19 words
The process of claim 6 wherein said cationic surface active fluorocarbon compound is a compound with an acid proton.
Claim 9
Dependent Claim
17 words
The process of claim 6 wherein said cationic fluorocarbon-containing wetting agent is a compound with an ##STR14##
Claim 10
Dependent Claim
42 words
The process of claim 6 wherein said cationic fluorocarbon-containing wetting agent is a compound having the formula: ##STR15## represents an anion which does not interfere with the electrolysis, such as SO 4 2- , Cl - or CH 3 SO 4 .sup.⊖
Claim 11
Dependent Claim
29 words
The process of claim 1 wherein the coating thus obtained is subjected to a sintering treatment after impregnation or not with a dispersion of particles of a different material.
Claim 12
Dependent Claim
26 words
The process of claim 10 wherein the average particle size of the particles of said different material in the dispersion is not more than 10 μm.
Claim 13
Dependent Claim
25 words
The process of claim 10 wherein for said different material use is made of a metal salt which hydrolyses in the pores of the coating.
Claim 14
Dependent Claim
8 words
The product of the process of claim 1.
Claim 15
Dependent Claim
15 words
The process of claim 1, wherein the coating also contains particles of a different material.
Claim 16
Dependent Claim
92 words
A metal plating bath, comprising an aqueous solution of a metal or metals to be electroplated and containing dispersed therein fine fluorocarbon resin particles having an average size less than about 10 μm in a concentration of about 3 to 150 grammes per liter of bath liquid, and having dissolved in said plating bath a cationic and a nonionic surface active fluorocarbon compound, in a molar ratio between 25:1 and 1:3.5 and in an amount which is at least 3.10 -3 mmoles per m 2 of surface area of the polyfluorocarbon particles.
Claim 17
Dependent Claim
92 words
A metal plating bath, comprising an aqueous solution of a metal or metals to be electroplated and containing dispersed therein fine fluorocarbon resin particles having an average size less than about 10 μm in a concentration of about 3 to 150 grammes per liter of bath liquid, and having dissolved in said plating bath a cationic and a nonionic surface active fluorocarbon compound, in a molar ratio between 25:1 and 1:3.5 and in an amount which is at least 3.10 -3 mmoles per m 2 of surface area of the polyfluorocarbon particles.
Claim 18
Dependent Claim
34 words
A metal plating bath according to claim 15 wherein the total amount of fluorocarbon surfactants is between about 6.10 -3 and 12.10 -3 mmoles per m 2 of surface area of the polyfluorocarbon particles.
Claim 19
Dependent Claim
40 words
A metal plating bath according to claim 15 wherein the nonionic fluorocarbon surfactant is present in an amount of about 17 to 36 mole percent of the total amount of fluorocarbon surfactants used for the dispersion of the resin particles.
Claim 20
Dependent Claim
34 words
A metal plating bath according to claim 15 wherein the nonionic fluorocarbon surfactant is present in an amount of about 26 mole percent calculated on the total amount of fluorocarbon surfactants in said bath.
Claim 21
Dependent Claim
20 words
A metal plating bath according to claim 15 wherein said nonionic fluorocarbon surfactant is a compound having the formula: ##STR16##
References Cited (Backward Citations)
US2559752A
Cited
US2820752A
Cited
US3677907A
Cited
GB1355601A
Cited
US3787294A
Cited
GB1366823A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-07-03 | 1982-01-02 | 1982-07-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-07-03 | 1986-01-02 | 1986-07-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-07-03 | 1990-01-02 | 1990-07-04 | $7700.00 | Window Closed / Lapsed |