Continuous measurement of electrolyte parameters in a cell for the electrolysis of a molten charge
Assignee: Rio Tinto Switzerland AG
•
Filing: 1974-12-05
•
Granted: 1978-07-04
•
Expires: 1994-12-05
Abstract
Abstract A process for the continuous measurement of the electrolyte parameters during the electrolysis of metallic compounds in particular aluminium oxide, dissolved in a melt. A measuring current of current density of at least 0.01 A/cm2 with respect to the anodic measuring surface, is passed through an anodically polarized measuring probe which has a measuring surface whch is wet by the corrosive electrolyte and which is made of an inconsumable ceramic oxide material.
Inventors
- 👤 Hanspeter Alder
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 07:11
CPC Classifications
C; C25; C25C; C25C3/00; C25C3/06; C25C3/20; C25C3/08
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
169 words
In a process for the continuous measurement of electrolyte parameters in an electrolysis cell during the production of aluminum therein by electrolysis of a melt containing an aluminum compound such as aluminum oxide, said cell having an anode and counter-electrode which carry the current for said electrolysis, the steps comprising: inserting in said melt the measuring surface of a measuring probe whereof said measuring surface is ceramic oxide, said probe having a coating of an inert refractory electrically non-conductive material around its three-phase zone and over all inward surfaces thereof outside of said measuring surface adapted to prevent contact of said melt with said probe; mantaining said measuring surface at a positive electrical potential with respect to a counter electrode therefor in said cell, said potential providing a current density of at least 0.01 amperes per square centimeter of measuring surface, whereby a measuring current is passed through at least a portion of said melt, and monitoring said measuring current and thereby determining the electrical parameters of said cell.
Claim 2
Dependent Claim
169 words
In a process for the continuous measurement of electrolyte parameters in an electrolysis cell during the production of aluminum therein by electrolysis of a melt containing an aluminum compound such as aluminum oxide, said cell having an anode and counter-electrode which carry the current for said electrolysis, the steps comprising: inserting in said melt the measuring surface of a measuring probe whereof said measuring surface is ceramic oxide, said probe having a coating of an inert refractory electrically non-conductive material around its three-phase zone and over all inward surfaces thereof outside of said measuring surface adapted to prevent contact of said melt with said probe; mantaining said measuring surface at a positive electrical potential with respect to a counter electrode therefor in said cell, said potential providing a current density of at least 0.01 amperes per square centimeter of measuring surface, whereby a measuring current is passed through at least a portion of said melt, and monitoring said measuring current and thereby determining the electrical parameters of said cell.
Claim 3
Dependent Claim
17 words
A process according to claim 1 in which the minimum current density is 0.025 A/cm 2 .
Claim 4
Dependent Claim
16 words
A process according to claim 1 in which the shielding is provided by solidified electrolyte material.
Claim 5
Dependent Claim
16 words
A process according to claim 3 in which the solidification is brought about by localized cooling.
Claim 6
Dependent Claim
37 words
A process according to claim 1 in which the measuring surface of said probe is porous and a stream of gas is passed therethrough in an amount which is sufficient to prevent reduction of said ceramic oxide.
Claim 7
Dependent Claim
19 words
A process according to claim 5 in which the minimum flow of gas amounts to 0.25 mmol/(cm 2 .h).
Claim 8
Dependent Claim
24 words
A process according to claim 1 in which the ceramic oxide material is based upon oxide of tin, iron, chromium, cobalt, nickel or zinc.
Claim 9
Dependent Claim
25 words
A process according to claim 7 in which the base material of one of the oxides is doped with at least one other metallic oxide.
Claim 10
Dependent Claim
33 words
A process according to claim 8 in which the ceramic oxide is SnO 2 doped with at least one other metallic oxide in a concentration of 0.01 - 20% of each dopant oxide.
Claim 11
Dependent Claim
40 words
A process according to claim 9 in which the metallic component of the dopant oxide is selected from the group consisting of Fe, Sb, Cu, Mn, Nb, Zn, Cr, Co, W, Cd, Zr, Ta, In, Ni, Ca, Ba and Bi.
Claim 12
Dependent Claim
13 words
A process according to claim 1 in which the electrolyte is cryolite based.
Claim 13
Dependent Claim
13 words
A process according to claim 1 in which the electrolyte is oxide based.
Claim 14
Dependent Claim
33 words
A process according to claim 1 in which molten aluminum metal as it is formed separates and accumulates at the bottom of the cell; and said counter electrode comprises the said accumulated metal.
Claim 15
Dependent Claim
71 words
A process according to claim 1, wherein said ceramic oxide has a negligible temperature coefficient of electrical resistance with respect to the electrolyte in the temperature range at which the parameters are being determined; said counter electrode is fixed; and the measuring current is monitored to determine changes in the voltage of the measuring current under conditions of constant current in order to determine changes in the resistance of the electrolyte.
Claim 16
Dependent Claim
104 words
A process according to claim 1, wherein aluminum is produced as molten aluminum which subsequently flows to the bottom of the cell where a pool is formed; said ceramic oxide has a negligible temperature coefficient of electrical resistance with respect to the electrolyte in the temperature range at which the parameters are being determined; said counter electrode includes the pool; and monitoring the measuring current to determine changes in the voltage of the measuring current under conditions of constant amperage to indicate the amount of electrolyte separating the probe and the counter electrode in order to determine the change in level of the aluminum.
Claim 17
Dependent Claim
44 words
A process according to claim 14 in which is selected a ceramic oxide material which has a negligible specific electrical resistance compared with that of the electrolyte and which has a negligible temperature coefficient in the specific electrical resistance between 950° and 1000° C.
Claim 18
Dependent Claim
45 words
A process according to claim 16 in which said ceramic oxide consists of the materials SnO 2 + 2% Sb 2 O 3 , SnO 2 + 2% CuO + 1% Sb 2 O 3 or SnO 2 + 2% Nb 2 O 5 .
Claim 19
Dependent Claim
53 words
A process according to claim 1, wherein said ceramic oxide has a relatively high temperature coefficient with respect to the electrolyte and in which the measuring current is monitored to measure a change in voltage over at least a part of the ceramic oxide in order to determine the temperature of the electrolyte.
Claim 20
Dependent Claim
40 words
A process according to claim 18 in which the ceramic oxide is dipped into the electrolyte to a sufficient depth that the whole of that part through which the measuring current flows is completely under the surface of the electrolyte.
Claim 21
Dependent Claim
28 words
A process according to claim 18 in which the side walls of the probe are completely shielded by an inert material which is also a bad electrical conductor.
Claim 22
Dependent Claim
29 words
A process according to claim 1 in which said ceramic oxide consists of the materials SnO 2 + 2% Fe 2 O 3 or SnO 2 + 10% CuO.
Claim 23
Dependent Claim
39 words
A process according to claim 18 in which said ceramic oxide has a large specific electrical resistance compared with that of the electrolyte and has a large temperature coefficient in the specific electrical resistance between 950° and 1000° C.
References Cited (Backward Citations)
US2919234A
Cited
US3034972A
Cited
US3208925A
Cited
US3141835A
Cited
US3345278A
Cited
US3471390A
Cited
US3400062A
Cited
US3712857A
Cited
US3661736A
Cited
US3718550A
Cited
US3829374A
Cited
US3930967A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-07-03 | 1982-01-02 | 1982-07-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-07-03 | 1986-01-02 | 1986-07-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-07-03 | 1990-01-02 | 1990-07-04 | $7700.00 | Window Closed / Lapsed |