Rubber modified dicarboxylic acid copolymer blends
Assignee: Atlantic Richfield Co
•
Filing: 1976-12-20
•
Granted: 1978-06-27
•
Expires: 1996-12-20
Abstract
Abstract A rubber-modified copolymer blend having enhanced toughness is prepared from a block copolymer rubber and a rubber-modified non-equimolar copolymer of ethylenically unsaturated dicarboxylic acids, or their derivatives, with one or more copolymerizable monomers.
Inventors
- 👤 Adolph V. DiGiulio
- 👤 Jack N. Bauer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 17:17
CPC Classifications
C; C08; C08F; C08F291/00; C08F291/02; C08L; C08L51/00; C08L51/04
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
153 words
A thermoplastic molding composition consisting essentially of a blend of a. 5-15% by weight, based on total molding composition, of a block copolymer of A. 2-50% by weight, based on block copolymer, of monovinyl aromatic monomer and B. 50-98% by weight, based on block copolymer, of a conjugated diene monomer, and b. 85-95% by weight, based on total molding composition, of a copolymer made by polymerizing A. 60-95% by weight, based on copolymer (b), of a mixture of (1) 4-35% by weight of an ethylenically unsaturated dicarboxylic acid moiety and (2) 65-96% by weight of one or more monomers copolymerizable therewith selected from the group consisting of monovinyl aryl monomers, unsaturated nitriles, and acrylic monomers, in the presence of B. 5-40% by weight, based on copolymer (b), of a diene rubber; whereby the sum of the block copolymer (a) and the diene rubber (bB) is 9-50% by weight of the total molding composition.
Claim 2
Dependent Claim
153 words
A thermoplastic molding composition consisting essentially of a blend of a. 5-15% by weight, based on total molding composition, of a block copolymer of A. 2-50% by weight, based on block copolymer, of monovinyl aromatic monomer and B. 50-98% by weight, based on block copolymer, of a conjugated diene monomer, and b. 85-95% by weight, based on total molding composition, of a copolymer made by polymerizing A. 60-95% by weight, based on copolymer (b), of a mixture of (1) 4-35% by weight of an ethylenically unsaturated dicarboxylic acid moiety and (2) 65-96% by weight of one or more monomers copolymerizable therewith selected from the group consisting of monovinyl aryl monomers, unsaturated nitriles, and acrylic monomers, in the presence of B. 5-40% by weight, based on copolymer (b), of a diene rubber; whereby the sum of the block copolymer (a) and the diene rubber (bB) is 9-50% by weight of the total molding composition.
Claim 3
Dependent Claim
137 words
A thermoplastic molding composition consisting essentially of a blend of a. 5-15% by weight, based on total molding composition, of a block copolymer of A. 2-50% by weight, based on block copolymer, of monovinyl aromatic monomer and B. 50-98% by weight, based on block copolymer, of a conjugated diene monomer, and b. 85-95% by weight, based on total molding composition, of a copolymer made by polymerizing A. 60-95% by weight, based on copolymer (b), of a mixture of (1) 4-35% by weight of an ethylenically unsaturated dicarboxylic acid moiety and (2) 65-96% by weight of a monovinyl aromatic monomer in the presence of B. 5-40% by weight, based on copolymer (b), of a diene rubber; whereby the sum of the block copolymer (a) and the diene rubber (bB) is 9-50% by weight of the total molding composition.
Claim 4
Dependent Claim
137 words
A thermoplastic molding composition consisting essentially of a blend of a. 5-15% by weight, based on total molding composition, of a block copolymer of A. 2-50% by weight, based on block copolymer, of monovinyl aromatic monomer and B. 50-98% by weight, based on block copolymer, of a conjugated diene monomer, and b. 85-95% by weight, based on total molding composition, of a copolymer made by polymerizing A. 60-95% by weight, based on copolymer (b), of a mixture of (1) 4-35% by weight of an ethylenically unsaturated dicarboxylic acid moiety and (2) 65-96% by weight of a monovinyl aromatic monomer in the presence of B. 5-40% by weight, based on copolymer (b), of a diene rubber; whereby the sum of the block copolymer (a) and the diene rubber (bB) is 9-50% by weight of the total molding composition.
Claim 5
Dependent Claim
125 words
A thermoplastic molding composition consisting essentially of a blend of a. 5-15% by weight, based on total molding composition, of a block copolymer of A. 2-50% by weight, based on block copolymer, of styrene and B. 50-98% by weight, based on block copolymer, of butadiene, and b. 85-95% by weight, based on total molding composition, of a copolymer made by polymerizing A. 60-95% by weight, based on copolymer (b), of a mixture of (1) 4-35% by weight of maleic anhydride and (2) 65-96% by weight of stryene in the presence of B. 5-40% by weight, based on copolymer (b), of a diene rubber; whereby the sum of the block copolymer (a) and the diene rubber (bB) is 9-50% by weight of the total molding composition.
Claim 6
Dependent Claim
125 words
A thermoplastic molding composition consisting essentially of a blend of a. 5-15% by weight, based on total molding composition, of a block copolymer of A. 2-50% by weight, based on block copolymer, of styrene and B. 50-98% by weight, based on block copolymer, of butadiene, and b. 85-95% by weight, based on total molding composition, of a copolymer made by polymerizing A. 60-95% by weight, based on copolymer (b), of a mixture of (1) 4-35% by weight of maleic anhydride and (2) 65-96% by weight of stryene in the presence of B. 5-40% by weight, based on copolymer (b), of a diene rubber; whereby the sum of the block copolymer (a) and the diene rubber (bB) is 9-50% by weight of the total molding composition.
Claim 7
Independent Claim
136 words
A method for preparing thermoplastic molding compositions having greater toughness and flexibility comprising the steps of a. forming a rubber-modified, non-equimolar copolymer by polymerizing 1. 60-95% by weight, based on rubber-modified copolymer, of a mixture of an ethylenically unsaturated dicarboxylic acid moiety and one or more monomers copolymerizable therewith in the presence of 2. 5-40% by weight, based on rubber-modified copolymer, of a diene rubber; said mixture (al) having A. 4-35% by weight, based on total mixture, of ethylenically unsaturated dicarboxylic acid moiety and B. 65-96% by weight, based on total mixture, of the copolymerizable monomers; said copolymerizable monomers being selected from the group consisting of monovinyl aromatic monomers, unsaturated nitriles, acrylic monomers, and mixtures thereof; and b. blending into said rubber-modified copolymer 5-15% by weight, based on total blend, of a block copolymer rubber having
Claim 8
Independent Claim
136 words
A method for preparing thermoplastic molding compositions having greater toughness and flexibility comprising the steps of a. forming a rubber-modified, non-equimolar copolymer by polymerizing 1. 60-95% by weight, based on rubber-modified copolymer, of a mixture of an ethylenically unsaturated dicarboxylic acid moiety and one or more monomers copolymerizable therewith in the presence of 2. 5-40% by weight, based on rubber-modified copolymer, of a diene rubber; said mixture (al) having A. 4-35% by weight, based on total mixture, of ethylenically unsaturated dicarboxylic acid moiety and B. 65-96% by weight, based on total mixture, of the copolymerizable monomers; said copolymerizable monomers being selected from the group consisting of monovinyl aromatic monomers, unsaturated nitriles, acrylic monomers, and mixtures thereof; and b. blending into said rubber-modified copolymer 5-15% by weight, based on total blend, of a block copolymer rubber having
Claim 9
Dependent Claim
25 words
2-50% by weight, based on block copolymer, of monovinyl aromatic monomer and 2. 50-98% by weight, based on block copolymer, of a conjugated diene monomer.
Claim 10
Dependent Claim
25 words
2-50% by weight, based on block copolymer, of monovinyl aromatic monomer and 2. 50-98% by weight, based on block copolymer, of a conjugated diene monomer.
Claim 11
Independent Claim
140 words
A method for preparing thermoplastic molding compositions having greater toughness and flexibility comprising the steps of a. forming a rubber-modified, non-equimolar copolymer by polymerizing 1. 60-95% by weight, based on rubber-modified copolymer, of a mixture of an ethylenically unsaturated dicarboxylic acid moiety and a monovinyl aromatic monomer in the presence of 2. 5-40% by weight, based on rubber-modified copolymer, of a diene rubber; said mixture (al) having A. 4-35% by weight, based on total mixture, of ethylenically unsaturated dicarboxylic acid moiety and B. 65-96% by weight, based on total mixture, of monovinyl aromatic monomer; and b. blending into said rubber-modified copolymer 5-15% by weight, based on total blend, of a block copolymer rubber having 1. 2-50% by weight, based on block copolymer, of monovinyl aromatic monomer and 2. 50-98% by weight, based on block copolymer, of a conjugated diene monomer.
Claim 12
Independent Claim
140 words
A method for preparing thermoplastic molding compositions having greater toughness and flexibility comprising the steps of a. forming a rubber-modified, non-equimolar copolymer by polymerizing 1. 60-95% by weight, based on rubber-modified copolymer, of a mixture of an ethylenically unsaturated dicarboxylic acid moiety and a monovinyl aromatic monomer in the presence of 2. 5-40% by weight, based on rubber-modified copolymer, of a diene rubber; said mixture (al) having A. 4-35% by weight, based on total mixture, of ethylenically unsaturated dicarboxylic acid moiety and B. 65-96% by weight, based on total mixture, of monovinyl aromatic monomer; and b. blending into said rubber-modified copolymer 5-15% by weight, based on total blend, of a block copolymer rubber having 1. 2-50% by weight, based on block copolymer, of monovinyl aromatic monomer and 2. 50-98% by weight, based on block copolymer, of a conjugated diene monomer.
Claim 13
Dependent Claim
62 words
The composition of claim 1 wherein the block copolymer is selected from the group consisting of A-B diblock, A-B graded diblock, A-B star or radial block, A-B-A triblock, and A-B-A hydrogenated triblock copolymer rubbers wherein A represents a monovinyl aromatic monomer block, B represents a conjugated diene monomer block, and the B blocks represent 50-98% by weight of the total block copolymer.
Claim 14
Dependent Claim
47 words
The composition of claim 1 wherein the diene rubber (bB) contains at least 50% by weight of a conjugated 1,3-diene and is selected from the group consisting of conjugated 1,3-diene rubbers, styrene-diene copolymer rubber, acrylonitrile-diene copolymer rubbers, ethylene-propylene-diene terpolymer rubbers, acrylatediene copolymer rubbers, and block copolymer rubbers.
Claim 15
Dependent Claim
53 words
The composition of claim 1 wherein the ethylenically unsaturated dicarboxylic acid moiety is selected from the group consisting of an ethylenically unsaturated dicarboxylic acid, an ethylenically unsaturated dicarboxylic acid anhydride, an ethylenically unsaturated dicarboxylic acid imide, an N-substituted ethylenically unsaturated dicarboxylic acid imide, an ethylenically unsaturated dicarboxylic acid half ester, and mixtures thereof.
References Cited (Backward Citations)
GB1077769A
Cited
US3637554A
Cited
US3873645A
Cited
US3919354A
Cited
US3919354B1
Cited
US4017436A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-06-26 | 1981-12-26 | 1982-06-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-06-26 | 1985-12-26 | 1986-06-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-06-26 | 1989-12-26 | 1990-06-27 | $7700.00 | Window Closed / Lapsed |