Assignee: Union Oil Company of California
•
Filing: 1976-12-17
•
Granted: 1978-06-27
•
Expires: 1996-12-17
Abstract
Abstract Highly active cobalt-molybdenum-alumina desulfurization catalysts containing 18-30 weight-percent of MoO 3 are prepared by first comulling boehmite alumina with aqueous ammonium molybdate solution, drying the resulting mixture, then comulling with a soluble cobalt salt and water, thereafter forming the resulting mixture into extrudates, and finally calcining the extrudates under controlled temperature conditions correlated with the molybdenum content of the catalyst so as to preserve adequate surface area and prevent the formation of large crystallites of cobalt molybdate. This method of preparation permits effective utilization of molybdenum in amounts up to about 30 weight-percent MoO 3 , a result not obtainable by conventional impregnation techniques.
Inventors
- 👤 Howard D. Simpson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 20:22
CPC Classifications
B; B01; B01J; B01J23/00; B01J23/70; B01J23/76; B01J23/84; B01J23/85; B01J23/88; B01J23/882; B01J37/00; B01J37/0009; C; C10; C10G; C10G45/00; C10G45/02; C10G45/04; C10G45/06; C10G45/08
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
164 words
A method for the manufacture of a hydrodesulfurization catalyst which comprises: (1) comulling boehmite alumina with sufficient of an aqueous ammonium molybdate solution to provide about 18-30 weight-percent of Mo0 3 in the finished catalyst; (2) drying the composite from step (1) at temperatures below about 500° F to a water content of between about 20 and 40 weight-percent; (3) intimately admixing the dried composite from step (2) with sufficient of a water-soluble cobalt salt to provide about 4-12 weight-percent of Co0 in the finished catalyst, and with sufficient water to provide an extrudable paste; (4) extruding the paste into extrudates having a diameter between about 1/20 and 1/4 inch; and (5) calcining the extrudates at a temperature which is (a) between about 900° and 1250° F and (b) correlated with the Mo0 3 content of said catalyst so as to give a final surface area of at least M/0.14 m 2 /g, where M is the weight-percent of Mo0 3 in said catalyst.
Claim 2
Independent Claim
164 words
A method for the manufacture of a hydrodesulfurization catalyst which comprises: (1) comulling boehmite alumina with sufficient of an aqueous ammonium molybdate solution to provide about 18-30 weight-percent of Mo0 3 in the finished catalyst; (2) drying the composite from step (1) at temperatures below about 500° F to a water content of between about 20 and 40 weight-percent; (3) intimately admixing the dried composite from step (2) with sufficient of a water-soluble cobalt salt to provide about 4-12 weight-percent of Co0 in the finished catalyst, and with sufficient water to provide an extrudable paste; (4) extruding the paste into extrudates having a diameter between about 1/20 and 1/4 inch; and (5) calcining the extrudates at a temperature which is (a) between about 900° and 1250° F and (b) correlated with the Mo0 3 content of said catalyst so as to give a final surface area of at least M/0.14 m 2 /g, where M is the weight-percent of Mo0 3 in said catalyst.
Claim 3
Dependent Claim
38 words
A method as defined in claim 1 wherein sufficient ammonium molybdate and water-soluble cobalt salt are employed in steps (1) and (3) to provide in the finished catalyst about 22-28 weight-percent Mo0 3 and about 6-10 weight-percent Co0.
Claim 4
Dependent Claim
55 words
A method as defined in claim 1 wherein said calcining in step (5) is carried out at a temperature correlated with the Mo0 3 content of said catalyst so as to give a final surface area of at least about M/0.10 m 2 /g, where M is the weight-percent of Mo0 3 in said catalyst.
Claim 5
Dependent Claim
38 words
A method as defined in claim 3 wherein sufficient ammonium molybdate and water-soluble cobalt salt are employed in steps (1) and (3) to provide in the finished catalyst about 22-28 weight-percent Mo0 3 and about 6-10 weight-percent Co0.
References Cited (Backward Citations)
US2911374A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-06-26 | 1981-12-26 | 1982-06-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-06-26 | 1985-12-26 | 1986-06-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-06-26 | 1989-12-26 | 1990-06-27 | $7700.00 | Window Closed / Lapsed |