US4097401A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Thermodynamically stable product for permanent storage and disposal of highly radioactive liquid wastes
Assignee: Gesellschaft fuer Kernforschung mbH
•
Filing: 1975-10-30
•
Granted: 1978-06-27
•
Expires: 1995-10-30
Abstract
Abstract Highly radioactive liquid wastes are permanently stored in a solidification matrix containing the components of a known borosilicate glass together with nucleation agents selected from the group consisting of oxides of Li, K, Mg, Mo and Cr, fluorides of those metals and of Al, and pure noble metals in the elemental form with particles with sizes smaller than 0.1 mu m in diameter, and up to 35% by weight of waste fission and corrosion products or waste fission and corrosion products and gadolinium oxide. The product is produced by denitrating and calcining the radioactive waste solution, melting the calcined waste product together with a borosilicate frit containing nucleation agents at a temperature of between 1,050 DEG and 1,200 DEG C, and maintaining it in its melted state for 3 to 5 hours, subsequently cooling the resulting mixture until to a given temperature and maintaining it at this temperature for a given time period to permit nucleation to occur, then elevating the temperature of the mixture with an constant heating rate until to a given higher temperature, maintaining it at this higher temperature for about 24 hours, and finally cooling it with a constant cooling rate to ambient temperature.
Inventors
- 👤 Walter Guber
- 👤 Jaroslav Saidl
- 👤 Paul Daruschy
- 👤 Werner Hild
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 03:08
CPC Classifications
C; C03; C03C; C03C10/00; C03C10/0036; G; G21; G21F; G21F9/00; G21F9/28; G21F9/30; G21F9/301; G21F9/302; G21F9/305
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
142 words
A thermodynamically stable microcrystalline glass ceramic or glass ceramic-like product for permanent disposal and storage of highly radioactive wastes in a manner harmless to the environment or the biocycle, comprising: (a) a solidifying matrix containing the components of a borosilicate glass including, by weight of the thermodynamically stable product, 35 to 50% SiO 2 , 3 to 6% TiO 2 , 5 to 10% Al 2 O 3 , 3 to 6% B 2 O 3 , 0 to 5% Na 2 O; (b) a plurality of nucleation agents, including, by weight, 3 to 6% MgO, 8 to 10% Li 2 O and 3 to 6% K 2 O; and (c) 20 to 30% by weight of waste fission and corrosion products; said thermodynamically stable product is producible by a process with a highest process temperature used of 1200° C or less.
Claim 2
Dependent Claim
142 words
A thermodynamically stable microcrystalline glass ceramic or glass ceramic-like product for permanent disposal and storage of highly radioactive wastes in a manner harmless to the environment or the biocycle, comprising: (a) a solidifying matrix containing the components of a borosilicate glass including, by weight of the thermodynamically stable product, 35 to 50% SiO 2 , 3 to 6% TiO 2 , 5 to 10% Al 2 O 3 , 3 to 6% B 2 O 3 , 0 to 5% Na 2 O; (b) a plurality of nucleation agents, including, by weight, 3 to 6% MgO, 8 to 10% Li 2 O and 3 to 6% K 2 O; and (c) 20 to 30% by weight of waste fission and corrosion products; said thermodynamically stable product is producible by a process with a highest process temperature used of 1200° C or less.
Claim 3
Dependent Claim
55 words
A product as defined in claim 1, which contains at least one further nucleation agent, selected from the group consisting of oxides of Mo and Cr, fluorides of the metals Li, K, Mg, Mo, Cr and Al, and pure noble metals in the form of particles with sizes between 0.01 and 0.1 μm in diameter.
Claim 4
Dependent Claim
39 words
A product as defined in claim 1, which further contains 0 to 11% Gd 2 O 3 , where the sum of the fission and corrosion products and Gd 2 O 3 is not more than 35% by weight.
Claim 5
Dependent Claim
168 words
A thermodynamically stable microcrystalline glass ceramic or glass ceramic-like product for permanent disposal and storage of highly radioactive wastes in a manner harmless to the environment or the biocycle, comprising: (a) a solidifying matrix containing the components of a borosilicate glass including, by weight of the thermodynamically stable product, 35 to 50% SiO 2 , 3 to 6% TiO 2 , 5 to 10% Al 2 O 3 , 3 to 6% B 2 O 3 , 0 to 5% Na 2 O; (b) a mixture of nucleation agents consisting of, by weight, 8 to 10% Li 2 O, 3 to 6% K 2 O, 3 to 6% MgO and 1 to 1.5% noble metal fission products in elemental form with particle sizes between 0.01 and 0.1 μm in diameter; and (c) 20 to 30% by weight of waste fission and corrosion products excluding Ru, Rh, and Pd; said glass ceramic or glass ceramic-like product is producible with a highest process temperature used of 1200° C or less.
Claim 6
Dependent Claim
168 words
A thermodynamically stable microcrystalline glass ceramic or glass ceramic-like product for permanent disposal and storage of highly radioactive wastes in a manner harmless to the environment or the biocycle, comprising: (a) a solidifying matrix containing the components of a borosilicate glass including, by weight of the thermodynamically stable product, 35 to 50% SiO 2 , 3 to 6% TiO 2 , 5 to 10% Al 2 O 3 , 3 to 6% B 2 O 3 , 0 to 5% Na 2 O; (b) a mixture of nucleation agents consisting of, by weight, 8 to 10% Li 2 O, 3 to 6% K 2 O, 3 to 6% MgO and 1 to 1.5% noble metal fission products in elemental form with particle sizes between 0.01 and 0.1 μm in diameter; and (c) 20 to 30% by weight of waste fission and corrosion products excluding Ru, Rh, and Pd; said glass ceramic or glass ceramic-like product is producible with a highest process temperature used of 1200° C or less.
Claim 7
Dependent Claim
39 words
A product as defined in claim 4, which further contains 0 to 11% Gd 2 O 3 , where the sum of the fission and corrosion products and Gd 2 O 3 is not more than 35% by weight.
Claim 8
Dependent Claim
17 words
A product as defined in claim 1 in which the glass further includes 3 to 6% CaO.
Claim 9
Dependent Claim
17 words
A product as defined in claim 4 in which the glass further includes 3 to 6% CaO.
References Cited (Backward Citations)
US2920971A
Cited
US3110557A
Cited
US3303140A
Cited
US3489577A
Cited
US3856497A
Cited
US3849330A
Cited
US3940255A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-06-26 | 1981-12-26 | 1982-06-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-06-26 | 1985-12-26 | 1986-06-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-06-26 | 1989-12-26 | 1990-06-27 | $7700.00 | Window Closed / Lapsed |