Process for preparing an identification card

Claim 2

A process, utilizing the following raw materials (a) backing means having a heat-sealable surface, (b) a bonding material that is photosensitive and becomes harder upon exposure to light, and (c) a transparent heat-sealable cover, said surface, said bonding material and said cover being compatible in that they may be merged and caused to flow together to form one integral construction when adequate heat and pressure are applied to them, for producing identification cards, comprising: applying said bonding material to said surface of said backing means in a configuration that conforms to the picture to be included as a part of the identification card, the process including applying particulate material to the bonding material, placing the transparent heat-sealable cover over the bonding material and said surface, and applying heat and pressure to cause the materials comprising said surface, said bonding material and said coating to flow together to form an integral identification card with improved alter-proof characteristics.

Claim 3

The process of claim 14 wherein said particulate material includes mildly radioactive isotopes and/or radioactive rare earth metals or compounds thereof.

Claim 4

The process of claim 1 wherein said particulate material includes rare earth materials and/or phosphors emitting infrared light waves.

Claim 5

The process of claim 1 wherein said particulate material includes promethium-147, thorium or thorium oxide.

Claim 6

The process of claim 1 wherein said backing means is made by the steps of providing a cobalt-vanadium-iron alloy magnetic material, coating the alloy with a metallic substance, chemically treating the coated alloy and then coating with an opaque thermoplastic material.

Claim 7

The process of claim 5 which comprises electroplating the cobalt-vanadium-iron alloy with iron, then etching with a strong alkaline solution containing sodium carbonate, and then treating with a solution of iron phosphate, and heating to deposit the iron phosphate on the iron that was electroplated onto said alloy.

Claim 8

The process of claim 1 in which the step of applying heat and pressure comprises laminating the card between flat platens at a pressure of about 750-1000 psi by heating to about 325° F to 350° F and then quenching to room temperature while still under pressure.

Claim 9

A process, utilizing the following raw materials (a) a backing having a heat-sealable surface, (b) a material that is tacky and is photosensitive and becomes harder and non-tacky upon exposure to light, and (c) a transparent heat-sealable cover, said surface, said material and said cover being compatible in that they may be merged and caused to flow together to form one integral construction when adequate heat and pressure are applied to them, for producing an identification card which comprises spreading said material on a substrate to form a coated substrate, placing a transparent protective film over the coated substrate, superposing on the transparent protective film a half-tone photograph having an opaque portion and a transparent portion, exposing said coated substrate to light rays by directing light rays through the photograph to render non-tacky the portions of said material which correspond to those parts of the photograph that are transparent, removing the photograph and the protective film from said coated substrate, spreading particulate material over said first-named material so that the particles stick to the tacky portion of the first-named material, removing the particulate material that did not adhere, placing said coated substrate in contact with said surface of said backing in such a manner so that said first-named material is directly contacting the backing and transfers said tacky portion of the first-named material and the particulate material on said tacky portion to the backing, and removing the coated substrate from said backing whereby the tacky portion of said first-named material remains adhered to said backing, placing said transparent heat-sealable cover over said surface including any of said materials that have adhered to said surface, and applying heat and pressure to the surface, the materials and the transparent cover, to merge them together causing said first-named material to merge into said surface and causing the transparent cover to merge into said surface including such merger in the spaces between half-tone dots, thus to form an identification card in which the backing, the first-named material and said cover have become integral thus improving the alter-proof characteristics of the card.

Claim 10

A process, utilizing the following raw materials (a) a backing having a heat-sealable surface, (b) a material that is tacky and is photosensitive and becomes harder and non-tacky upon exposure to light, and (c) a transparent heat-sealable cover, said surface, said material and said cover being compatible in that they may be merged and caused to flow together to form one integral construction when adequate heat and pressure are applied to them, for producing an identification card which comprises spreading said material on a substrate to form a coated substrate, placing a transparent protective film over the coated substrate, superposing on the transparent protective film a half-tone photograph having an opaque portion and a transparent portion, exposing said coated substrate to light rays by directing light rays through the photograph to render non-tacky the portions of said material which correspond to those parts of the photograph that are transparent, removing the photograph and the protective film from said coated substrate, spreading particulate material over said first-named material so that the particles stick to the tacky portion of the first-named material, removing the particulate material that did not adhere, placing said coated substrate in contact with said surface of said backing in such a manner so that said first-named material is directly contacting the backing and transfers said tacky portion of the first-named material and the particulate material on said tacky portion to the backing, and removing the coated substrate from said backing whereby the tacky portion of said first-named material remains adhered to said backing, placing said transparent heat-sealable cover over said surface including any of said materials that have adhered to said surface, and applying heat and pressure to the surface, the materials and the transparent cover, to merge them together causing said first-named material to merge into said surface and causing the transparent cover to merge into said surface including such merger in the spaces between half-tone dots, thus to form an identification card in which the backing, the first-named material and said cover have become integral thus improving the alter-proof characteristics of the card.

Claim 11

The process of claim 8 wherein the said particulate material includes promethium-147, thorium or thorium oxide.

Claim 12

The process of claim 8 wherein said particulate material includes mildly radioactive isotopes and/or radioactive rare earth metals or compounds thereof.

Claim 13

The process of claim 8 wherein said particulate material includes rare earth materials and/or phosphors emitting infrared light waves.

Claim 14

The process of claim 8 wherein said backing is cobalt-iron alloy magnetic material which is obtained by electroplating the cobalt-iron alloy with a metallic substance, chemically treating the plated alloy and then coating with an opaque thermoplastic material.

Claim 15

The process of claim 8 in which the backing is a cobalt-iron alloy, comprising electroplating the cobalt-iron alloy with iron, then etching with a phosphoric acid solution or a strong alkaline solution containing sodium carbonate and then treating with a bath of iron phosphate.

Claim 16

The process of claim 8 in which the step of applying heat pressure comprises pressing the card between flat plates at a pressure of about 750-1000 psi, heating to about 325° F to 350° F and then quenching with a cold liquid to room temperature while still under pressure.

Claim 17

The process of claim 8 wherein said backing is obtained by coating a steel containing 38% by weight of iron, 10% by weight of vanadium, and 52% by weight of cobalt with a vinyl polymer.

Claim 18

A process for producing an identification card which comprises spreading bonding material that is hardened by light on a substrate, placing a transparent protective film over the coated substrate, superposing on the transparent protective film a half-tone photograph having an opaque portion and a transparent portion, exposing said coated substrate to light rays by directing light rays through the photograph to harden the portions of the bonding material which correspond to those parts of the photograph that are transparent, removing the photographic image and the protective film from said coated substrate, spreading particulate material over said bonding material so that the particles stick to the unhardened portion of the bonding material, removing the particulate material that has not adhered, and thereby obtaining the photographic image, providing a backing and a transparent cover which are compatible with each other and with said bonding material in the sense that they merge together under heat and pressure, placing said coated substrate with said image thereon in contact with a backing in such a manner so that the image is directly contacting the backing, removing the coated substrate from said backing whereby the image remains adhered to the backing, and sealing a transparent covering to the backing by heat and pressure to join the backing and the covering not only between the dots of particulate material but outside the boundary of the picture formed on the backing.

Claim 19

A process for producing an identification card which comprises spreading bonding material that is hardened by light on a substrate, placing a transparent protective film over the coated substrate, superposing on the transparent protective film a half-tone photograph having an opaque portion and a transparent portion, exposing said coated substrate to light rays by directing light rays through the photograph to harden the portions of the bonding material which correspond to those parts of the photograph that are transparent, removing the photographic image and the protective film from said coated substrate, spreading particulate material over said bonding material so that the particles stick to the unhardened portion of the bonding material, removing the particulate material that has not adhered, and thereby obtaining the photographic image, providing a backing and a transparent cover which are compatible with each other and with said bonding material in the sense that they merge together under heat and pressure, placing said coated substrate with said image thereon in contact with a backing in such a manner so that the image is directly contacting the backing, removing the coated substrate from said backing whereby the image remains adhered to the backing, and sealing a transparent covering to the backing by heat and pressure to join the backing and the covering not only between the dots of particulate material but outside the boundary of the picture formed on the backing.

Claim 20

The process of claim 11 wherein said backing means comprises a steel sheet with a thermoplastic coating to on at least one surface thereof and wherein the coated substrate with the image thereon and backing means are contacted under pressure and a temperature of between about 225° F to 240° F and then contacted again under increased pressure at a higher temperature of between about 275° F to 300° F to cause the image to fuse into the coating on the backing means.

Claim 21

The process of claim 17 wherein said steel sheet is cobalt-iron alloy magnetic material electro-plated with a metallic substance and chemically treated.

Claim 22

The process of claim 17 wherein said backing means comprises a steel sheet containing 38% by weight of iron, 10% by weight of vanadium and 52% by weight of cobalt with a thermoplastic vinyl polymer coating on at least one surface thereof.

Claim 23

The identification card of claim 16 wherein said particles include mildly radioactive isotopes and/or radioactive rare earth metals or compounds thereof.

Claim 24

The process of claim 16 wherein said particulate material includes rare earth materials and/or phosphors emitting infrared light waves.

Claim 25

The process of claim 17 wherein said steel sheet is cobalt-iron alloy magnetic material containing about 36 to 62% by weight of cobalt, about 30 to 52% by weight of iron, and up to about 16% by weight of a metal selected from the group consisting of vanadium, nickel, carbon, silicon, molybdenum, praseodymium, samarium, lanthanum, cerium, mischmetal and mixtures thereof.

Claim 26

The process of claim 17 wherein said steel sheet is cobalt-iron alloy containing about 36 to 62% by weight of cobalt, about 30 to 52% by weight of iron and about 6 to 16% by weight of a mixture of a member selected from the group consisting of vanadium, nickel, molybdenum and mixtures thereof, and a member selected from the group consisting of praseodymium, samarium, lanthananum, cerium, mischmetal and mixtures thereof.

Claim 27

The process of claim 17 wherein said steel sheet is cobalt-iron alloy magnetic material containing about 55 to 60% cobalt, about 25 to 30% iron, about 5 to 8% praseodymium, samarium, lanthanum, cerium or mischmetal, and about 10 to 15% vanadium.

Claim 28

The process of claim 17 wherein said particulate material includes promethium-147, thorium or thorium oxide.

Claim 29

The process of claim 17 wherein said backing means is cobalt-iron alloy magnetic material which is obtained by electro-plating the cobalt-iron alloy with a metallic substance, chemically treating the plated alloy and then coating with an opaque thermoplastic material.

Claim 30

The process of claim 17 which comprises electro-plating the cobalt-iron alloy with iron, then etching with a phosphoric acid solution or a strong alkaline solution containing sodium carbonate.

Claim 31

The process of claim 17 which comprises laminating the card between flat-platens at a pressure of about 750-1000 psi by heating to about 325° F to 350° F and then quenching to room temperature under high pressure with a zero degree liquid while still under pressure.

Claim 32

The process of claim 17 wherein said particulate material includes mildly radioactive isotopes and/or radioactive rare earth metals or compounds thereof.

Claim 33

The process of claim 17 wherein said particulate material includes rare earth materials and/or phosphors emitting infrared light waves.

Claim 34

The process of claim 17 wherein said backing means is obtained by coating a steel containing 38% by weight of iron, 10% by weight of vanadium, and 52% by weight of cobalt with a vinyl polymer.

Claim 35

The identification card of claim 17 wherein said sheet steel is a cobalt alloy containing 50 to 60% by weight of cobalt, 10 to 12% by weight of rare earth metals praseodymium, samarium, lanthanum, mischmetal or cerium, 20 to 30% by weight of iron and 8 to 10% by weight of vanadium.

Claim 36

The process claim 1 wherein said backing means is a cobalt alloy containing 50 to 60% by weight of cobalt, 10 to 12% by weight of rare earth metals praseodymium, samarium, lanthanum, mischmetal or cerium, 20 to 30% by weight of iron and 8 to 10% by weight of vanadium.

Claim 37

The process claim 8 wherein said backing means is a cobalt alloy containing 50 to 60% by weight of cobalt, 10 to 12% by weight of rare earth metals praseodymium, samarium, lanthanum, mischmetal or cerium, 20 to 30% by weight of iron and 8 to 10% by weight of vanadium.

Claim 38

The process claim 16 wherein said backing means is a cobalt alloy containing 50 to 60% by weight of cobalt, 10 to 12% by weight of rare earth metals praseodymium, samarium, lanthanum, mischmetal or cerium, 20 to 30% by weight of iron and 8 to 10% by weight of vanadium.

Claim 39

The process claim 17 wherein said backing means is a cobalt alloy containing 50 to 60% by weight of cobalt, 10 to 12% by weight of rare earth metals praseodymium, samarium, lanthanum, mischmetal or cerium, 20 to 30% by weight of iron and 8 to 10% by weight of vanadium.

Claim 42

The method of claim 37 in which said metal is iron.

Claim 43

The method of claim 37 in which said coating step comprises electroplating the metal on the magnetic material.

Claim 44

The method of claim 37 in which prior to the coating step some of one surface of the sheet of magnetizable material is electrolytically removed, said coating step comprising electroplating said metal on said surface.

Claim 45

The method of claim 37 in which an iron electrode is provided comprising: removing, prior to said coating step, some of one surface of said sheet of magnetic material, by a process step comprising applying an electric potential between the magnetizable material and the electrode, to thus prepare said surface to receive an iron coating, and reversing the polarity between the electrode and the magnetizable material to electroplate an iron coating on said magnetizable material.