Resist mask formation process with haloalkyl methacrylate copolymers
Assignee: International Business Machines Corp
•
Filing: 1976-10-04
•
Granted: 1978-06-20
•
Expires: 1996-10-04
Abstract
Abstract A positive relief image is produced by coating a substrate with a layer of a copolymer containing about 90-98 mole percent of polymerized lower alkyl methacrylate units and about 2-10 mole percent of polymerized lower haloalkyl methacrylate units, heating the layer to cause cross-linking between polymer chains by removal of hydrogen halide, patternwise exposing the layer with high energy radiation such as a scanning electron beam, and removing the exposed portion of the layer with a solvent developer. The purpose of this abstract is to enable the public and the Patents and Trademark Office to rapidly determine the subject matter of the technical disclosure of the application. This abstract is neither intended to define the invention of the application nor is it intended to be limiting as to the scope thereof.
Inventors
- 👤 Edward Carmine Fredericks
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 07:13
CPC Classifications
G; G03; G03F; G03F7/00; G03F7/004; G03F7/039; C; C09; C09D; C09D133/00; C09D133/04; C09D133/06; C09D133/10
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
159 words
A process for producing a positive relief image comprising coating a substrate with a layer consisting essentially of a copolymer containing about 90 to 98 mole percent of polymerized lower alkyl methacrylate units and about 2 to 10 mole percent of polymerized lower haloalkyl methacrylate units, wherein the copolymer has the general formula: ##STR2## where n1 and n2 are integers equal to one or more; where Y is a lower alkyl having 1-6 carbons; where Z is CH 2 X, C 2 H 4 X, C 2 H 3 X 2 , C 3 H 6 X, C 3 H 5 X 2 , C 4 H 8 X, C 4 H 7 X 2 and where X is CL, Br, I or a mixture, heating the layer to cause cross-linking between polymer chains with removal of hydrogen halide, patternwise exposing the layer with high energy radiation, and removing the exposed portion of the layer with a solvent developer.
Claim 2
Dependent Claim
159 words
A process for producing a positive relief image comprising coating a substrate with a layer consisting essentially of a copolymer containing about 90 to 98 mole percent of polymerized lower alkyl methacrylate units and about 2 to 10 mole percent of polymerized lower haloalkyl methacrylate units, wherein the copolymer has the general formula: ##STR2## where n1 and n2 are integers equal to one or more; where Y is a lower alkyl having 1-6 carbons; where Z is CH 2 X, C 2 H 4 X, C 2 H 3 X 2 , C 3 H 6 X, C 3 H 5 X 2 , C 4 H 8 X, C 4 H 7 X 2 and where X is CL, Br, I or a mixture, heating the layer to cause cross-linking between polymer chains with removal of hydrogen halide, patternwise exposing the layer with high energy radiation, and removing the exposed portion of the layer with a solvent developer.
Claim 3
Dependent Claim
17 words
The process of claim 1 including the step of removing the cross-linked layer with an organic solvent.
Claim 4
Dependent Claim
20 words
The process of claim 1 wherein the alkyl group of the lower alkyl methacrylate contains 1 to 6 carbon atoms.
Claim 5
Dependent Claim
29 words
The process of claim 1 wherein the lower haloalkyl methacrylate contains 1-4 carbons and the halogen is selected from the group consisting of Cl, Br, I and mixtures thereof.
Claim 6
Dependent Claim
25 words
The process of claim 1 wherein the heating is carried out at a temperature of from about 180°-210° C for from 30 to 60 minutes.
Claim 7
Dependent Claim
83 words
A process for producing a positive resist mask on a substrate comprising coating the substrate with a layer consisting essentially of a copolymer containing about 90 to 98 mole percent of polymerized methyl methacrylate units and about 2 to 10 mole percent of polymerized 2-chloroethyl methacrylate units, heating the layer to cause cross-linking between polymer chains with removal of hydrogen chloride, patternwise exposing the layer with a focussed, scanning electron beam, and removing the exposed portion of the layer with a solvent developer.
Claim 8
Dependent Claim
83 words
A process for producing a positive resist mask on a substrate comprising coating the substrate with a layer consisting essentially of a copolymer containing about 90 to 98 mole percent of polymerized methyl methacrylate units and about 2 to 10 mole percent of polymerized 2-chloroethyl methacrylate units, heating the layer to cause cross-linking between polymer chains with removal of hydrogen chloride, patternwise exposing the layer with a focussed, scanning electron beam, and removing the exposed portion of the layer with a solvent developer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-06-19 | 1981-12-19 | 1982-06-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-06-19 | 1985-12-19 | 1986-06-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-06-19 | 1989-12-19 | 1990-06-20 | $7700.00 | Window Closed / Lapsed |