Production of p-phenylene sulfide polymers
Assignee: Phillips Petroleum Co
•
Filing: 1975-05-27
•
Granted: 1978-06-20
•
Expires: 1995-05-27
Abstract
Abstract A method is provided for producing a p-phenylene sulfide polymer by contacting at least one p-dihalobenzene, at least one alkali metal sulfide, at least one alkali metal carboxylate, at least one organic amide and at least one alkali metal hydroxide to form a composition at polymerization conditions. The use of an alkali metal hydroxide in addition to the other compounds used in the reaction mixture results in p-phenylene sulfide polymers of higher molecular weight than produced without the alkali metal hydroxide, as evidenced by lower melt flow of the polymer than produced by the compared methods.
Inventors
- 👤 James T. Edmonds, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 19:19
CPC Classifications
C; C08; C08G; C08G75/00; C08G75/02; C08G75/0204; C08G75/025; C08G75/0254; C08G75/0209; C08G75/0213
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
78 words
In a method for producing polymers by: a. forming a composition consisting essentially of at least one p-dihalobenzene, at least one alkali metal sulfide, at least one alkali metal carboxylate, and at least one organic amide, and b. maintaining at least a portion of said composition at polymerization conditions to produce a polymer, the improvement of admixing at least one alkali metal hydroxide into said composition of (a) thereby effectively lowering the melt flow of the polymer produced.
Claim 2
Dependent Claim
78 words
In a method for producing polymers by: a. forming a composition consisting essentially of at least one p-dihalobenzene, at least one alkali metal sulfide, at least one alkali metal carboxylate, and at least one organic amide, and b. maintaining at least a portion of said composition at polymerization conditions to produce a polymer, the improvement of admixing at least one alkali metal hydroxide into said composition of (a) thereby effectively lowering the melt flow of the polymer produced.
Claim 3
Dependent Claim
71 words
A method of claim 1 wherein a first composition comprising: a. a mixture of at least one alkali metal sulfide, at least one alkali metal carboxylate, at least one alkali metal hydroxide, and at least one organic amide is formed, and b. at least a portion of said mixture is contacted with at least one p-dihalobenzene under polymerization conditions for a period of time sufficient to form a p-phenylene sulfide polymer.
Claim 4
Dependent Claim
92 words
A method of claim 1 wherein said p-dihalobenzene is represented by the formula ##STR5## where each X is selected from the group consisting of chlorine, bromine, and iodine, and each R is selected from the group consisting of hydrogen and hydrocarbyl in which the hydrocarbyl is an alkyl, cycloalkyl, or aryl radical or combination thereof, the total number of carbon atoms in each molecule being within the range of 6 to about 24, with the proviso that in at least 50 mole percent of the p-dihalobenzene employed each R must be hydrogen.
Claim 5
Dependent Claim
92 words
A method of claim 2 wherein the p-dihalobenzene is represented by the formula ##STR6## where each X is selected from the group consisting of chlorine, bromine, and iodine, and each R is selected from the group consisting of hydrogen and hydrocarbyl in which the hydrocarbyl is an alkyl, cycloalkyl, or aryl radical or combination thereof, the total number of carbon atoms in each molecule being within the range of 6 to about 24, with the proviso that in at least 50 mole percent of the p-dihalobenzene employed each R must be hydrogen.
Claim 6
Dependent Claim
68 words
A method of claim 3 wherein the mole ratio of p-dihalobenzene to alkali metal sulfide is within the range of about 0.9:1 to about 2:1, the mole ratio of alkali metal carboxylate to alkali metal sulfide is within the range of about 0.05:1 to about 4:1, and the mole ratio of alkali metal hydroxide to alkali metal sulfide is within the range of about 0.008:1 to about 0.8:1.
Claim 7
Dependent Claim
68 words
A method of claim 4 wherein the mole ratio of p-dihalobenzene to alkali metal sulfide is within the range of about 0.9:1 to about 2:1, the mole ratio of alkali metal carboxylate to alkali metal sulfide is within the range of about 0.05:1 to about 4:1, and the mole ratio of alkali metal hydroxide to alkali metal sulfide is within the range of about 0.008:1 to about 0.8:1.
Claim 8
Dependent Claim
56 words
A method of claim 5 wherein the polymerization conditions present comprise a reaction temperature within the range of about 125° C to about 450° C, a pressure sufficient to maintain the p-dihalobenzene and organic amide substantially in the liquid phase and the reaction time is in the range of about 10 minutes to about 72 hours.
Claim 9
Dependent Claim
56 words
A method of claim 6 wherein the polymerization conditions present comprise a reaction temperature within the range of about 125° C to about 450° C, a pressure sufficient to maintain the p-dihalobenzene and organic amide substantially in the liquid phase and the reaction time is in the range of about 10 minutes to about 72 hours.
Claim 10
Dependent Claim
26 words
A method of claim 7 wherein said alkali metal hydroxide is chosen from lithium hydroxide, sodium hydroxide, potassium hydroxide, rubidium hydroxide, cesium hydroxide, and mixtures thereof.
Claim 11
Dependent Claim
26 words
The method of claim 8 wherein said alkali metal hydroxide is chosen from lithium hydroxide, sodium hydroxide, potassium hydroxide, rubidium hydroxide, cesium hydroxide, and mixtures thereof.
Claim 12
Dependent Claim
70 words
The method of claim 10 wherein said p-dihalobenzene is p-dichlorobenzene, said alkali metal sulfide is sodium sulfide, said alkali metal carboxylate is lithium acetate dihydrate, said organic amide is N-methyl-2-pyrrolidone, and said alkali metal hydroxide is sodium hydroxide, and the reaction temperature is within the range of about 175° C to about 350° C and the reaction time is within the range of about 1 hour to about 8 hours.
Claim 13
Dependent Claim
86 words
The method of claim 10 wherein said alkali metal sulfide is sodium sulfide, said alkali metal carboxylate is lithium acetate dihydrate, said organic amide is N-methyl-2-pyrrolidone, said alkali metal hydroxide is sodium hydroxide and said p-dihalobenzene is a mixture of p-dichlorobenzene and 2,5-dichloro-p-xylene, and the reaction temperature is within the range of about 175° C to about 350° C and the reaction time is within the range of about 1 hour to about 8 hours to produce a polymer comprising a copolymer containing the units ##STR7##
References Cited (Backward Citations)
US3562199A
Cited
US3607843A
Cited
US3725362A
Cited
US3763124A
Cited
US3786035A
Cited
US3919177A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-06-19 | 1981-12-19 | 1982-06-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-06-19 | 1985-12-19 | 1986-06-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-06-19 | 1989-12-19 | 1990-06-20 | $7700.00 | Window Closed / Lapsed |