Glutarate-containing polyesterpolyols, methods of preparation and polyurethane compositions derived therefrom

Claim 3

The method of claim 1, in which the polyol is selected from diols of the class consisting of alkylene diols containing from 2 to not more than 20 carbon atoms, diethylene glycol and higher poly(oxyethylene) glycols containing up to and including 10 oxyethylene groups, dipropylene glycol and higher poly(oxypropylene) glycols containing up to and including 6 oxypropylene groups, cycloalkylene diols containing from 4 to not more than 8 carbon atoms, and bis(hydroxymethyl) benzenes, and polyols of the class consisting of 1,1,1-tris(hydroxymethyl)ethane, 1,1,1-tris(hydroxymethyl)propane, 1,2,4-butanetriol, glycerol, and pentaerythritol, and in which the lower alkanol is methanol.

Claim 4

The method of claim 1, in which said mixture also contains di-ester of adipic acid and a volatile lower monohydric alkanol.

Claim 5

The method of claim 1, in which said mixture contains a di-ester of azelaic acid and a volatile lower monohydric alkanol.

Claim 6

The method of claim 1, in which said mixture contains epsilon-caprolactone.

Claim 7

The method of claim 1, in which said lower monohydric alkanol is methanol and in which the heating is continued until the polyester has an acid number not greater than 3 and not more than 2 percent carbalkoxy groups.

Claim 8

The method of claim 1, in which said lower monohydric alkanol is methanol and in which the heating is continued until the polyester has an acid number not greater than 3 and not more than 2 percent carbomethoxy groups.

Claim 11

The method of claim 8, in which the chain extender is adipic acid.

Claim 12

The method of claim 8, in which the chain extender is azelaic acid.

Claim 13

The method of claim 8, in which the chain extender is epsilon-caprolactone.

Claim 14

A hydroxyl terminated neutral polyester having a dicarboxylic acid moiety of at least 4 and not more than 20 carbon atoms which comprises the glutaric acid moiety and the acid moiety of another dicarboxylic acid having from 4 to not more than 20 carbon atoms prepared by heating a polyol and diloweralkyl esters of said acids and volatile lower monohydric alkanols in the presence of a catalytic amount, up to 150 ppm tin, of stannous salt of a carboxylic acid at a temperature and in proportions sufficient to effect substantially complete transesterification with substantially complete alcoholysis of said diloweralkyl esters and with the distillation of the thus liberated said lower alkanols and without substantial distillation of polyol, said polyester being characterized by a residuum of tin which, due to the processing, no longer has the activity of a catalyst for promoting the reaction of isocyanate with active hydrogen compounds, and a residuum of carbalkoxy groups.

Claim 15

A hydroxyl terminated neutral polyester having a dicarboxylic acid moiety of at least 4 and not more than 20 carbon atoms which comprises the glutaric acid moiety and the acid moiety of another dicarboxylic acid having from 4 to not more than 20 carbon atoms prepared by heating a polyol and diloweralkyl esters of said acids and volatile lower monohydric alkanols in the presence of a catalytic amount, up to 150 ppm tin, of stannous salt of a carboxylic acid at a temperature and in proportions sufficient to effect substantially complete transesterification with substantially complete alcoholysis of said diloweralkyl esters and with the distillation of the thus liberated said lower alkanols and without substantial distillation of polyol, said polyester being characterized by a residuum of tin which, due to the processing, no longer has the activity of a catalyst for promoting the reaction of isocyanate with active hydrogen compounds, and a residuum of carbalkoxy groups.

Claim 16

The polyester of claim 12, in which the polyol is selected from diols of the class consisting of alkylene diols containing from 2 to not more than 20 carbon atoms, diethylene glycol and higher poly(oxyethylene) glycols containing up to and including 10 oxyethylene groups, dipropylene glycol and higher poly(oxypropylene) glycols containing up to and including 6 oxypropylene groups, cycloalkylene diols containing from 4 to not more than 8 carbon atoms, and bis(hydroxymethyl)benzenes; and polyols of the class consisting of 1,1,1-tris(hydroxymethyl)ethane, 1,1,1-tris(hydroxymethyl) propane, 1,2,4-butanetriol, glycerol, and pentaerythritol; and in which the lower alkanol is methanol.

Claim 17

The polyester of claim 12, in which one component of the other dicarboxylic acid moiety is the adipic acid moiety.

Claim 18

The polyester of claim 12, in which one component of the other dicarboxylic acid moiety is the azelaic acid moiety.

Claim 19

The polyester of claim 12, which has been chain-extended by a chain-extending amount of epsilon-caprolactone.

Claim 20

The polyester of claim 13, in which one component of the other dicarboxylic acid moiety is the adipic acid moiety.

Claim 21

The polyester of claim 13, in which one component of the other dicarboxylic acid moiety is the azelaic acid moiety.

Claim 22

The polyester of claim 13, which has been chain-extended by a chain-extending amount of epsilon-caprolactone.

Claim 23

The polyester of claim 12, having an acid number not greater than 3 and a residuum of carbalkoxy groups not greater than 2 percent.

Claim 24

The polyester of claim 13, in which said lower monohydric alkanol is methanol and in which the polyester has an acid number not greater than 3 and a residuum of carbomethoxy groups not greater than 2 percent.

Claim 25

The isocyanate terminated polyester urethane prepared by the reaction of a molar excess of organic diisocyanate with the hydroxyl terminated polyester of claim 12.

Claim 26

The isocyanate terminated polyester urethane of claim 22, in which the isocyanate is selected from the group consisting of 2,4-tolylene diisocyanate, alone or in admixture with 2,6-tolylene diisocyanate; 4,4'-methylenebis(phenyl isocyanate), alone or in admixture with its 2,4'- and/or 2,2'-isomers; 3,3'-dimethyl-4,4'-diisocyanatobiphenyl; 3,3,'dimethoxy-4,4'-diisocyanatobiphenyl; 4,4'-methylenebis(3-methoxyphenyl isocyanate); 1,5-naphthalene diisocyanate; m-xylylene diisocyanate; p-xylylene diisocyanate; hexamethylene diisocyanate; isophorone diisocyanate; trimethylhexamethylene diisocyanate; methyl-2,4-diisocyanatocyclohexane; 4,4'-methylenebis(cyclohexyl isocyanate); 4,4',-4"-tris(isocyanatophenyl)methane alone or in admixture with other isocyanates obtained by the phosgenation of anilineformaldehyde resins; the triisocyanate obtained by the reaction of 3 mols of tolylene diisocyanate with 1 mol of 1,1,1-tris(hydroxymethyl)propane; and, the triisocyanate obtained by the reaction of 3 mols of hexamethylene diisocyanate with one mol of water.

Claim 27

The isocyanate terminated polyester urethane of claim 23, in which the polyols are the same or different polyols selected from the group consisting of alkylene diols, containing from 2 to not more than 20 carbon atoms, diethylene glycol and higher poly(oxyethylene) glycols containing up to and including 10 oxyethylene groups, dipropylene glycol and higher poly(oxypropylene) glycols containing up to and including 6 oxypropylene groups, cycloalkylene diols containing from 4 to not more than 8 carbon atoms, and bis(hydroxymethyl)benzenes, and polyols of the class consisting of 1,1,1-tris(hydroxymethyl)ethane, 1,1,1-tris(hydroxymethyl) propane, 1,2,4-butanetriol, glycerol, and pentaerythritol.

Claim 28

The isocyanate terminated polyester urethane of claim 24, in which one component of the other carboxylic acid moiety is the adipic acid moiety.

Claim 29

The isocyanate terminated polyester urethane of claim 24, in which one component of the other carboxylic acid moiety is the azelaic acid moiety.

Claim 30

The isocyanate terminated polyester urethane of claim 24, in which the polyester moiety contains a minor amount of pentamethylene carboxy groups derived from epsiloncaprolactone.

Claim 31

The isocyanate terminated polyester urethane of claim 24, in which the hydroxyl terminated polyester has an acid number not greater than 3 and a residuum of carbalkoxy groups not greater than 2 percent.

Claim 32

A polyurethane elastomer prepared by the chain extension of an isocyanate terminated polyester urethane prepared by reacting said urethane with a curative agent of the group consisting of 1) a hydroxyl terminated polyester urethane having an average molecular weight of less than about 6,000; 2) a solution of a lower molecular weight polyol or an aromatic diamine in a hydroxyl terminated polyester urethane having an average molecular weight of less than about 6,000; 3) a solution of lower molecular weight polyol or an aromatic diamine in a hydroxyl terminated polyester, the polyester moieties of the hydroxyl terminated polyester, the isocyanate terminated polyester urethane, and the hydroxyl terminated polyester urethane, which may have the same or different polyester moieties, being the moieties of those of hydroxyl terminated polyesters prepared by a) heating a polyol and a diloweralkyl ester of glutaric acid and a volatile monohydric alkanol or a mixture of said diloweralkyl ester of glutaric acid and another diloweralkyl ester of a dicarboxylic acid having at least 4 and not more than 20 carbon atoms and a volatile monohydric alkanol in the presence of a catalytic amount, up to 150 ppm tin, of a stannous salt of a carboxylic acid and at a temperature and in proportions sufficient to effect substantially complete transesterification with substantially complete alcoholysis of said diloweralkyl ester and with the distillation of the thus liberated said lower alkanol and without substantial distillation of polyol, said polyester being characterized by a residuum of tin which, due to the processing, no longer has the activity of a catalyst for promoting the reaction of isocyanate with the active hydrogen compounds, and a residuum of carbalkoxy groups, or by b) chain extending the hydroxyl terminated polyester prepared as above, by heating it with a chain-extending amount of a chain extender selected from the group consisting of a dicarboxylic acid of at least 4 carbon atoms and not more than 20 carbon atoms, or an anhydride thereof, and epsiloncaprolactone at a temperature sufficient to distill off any water formed to cause chain extension; 4) said aromatic diamine per se; and 5) said lower molecular weight polyol per se.

Claim 33

A polyurethane elastomer prepared by the chain extension of an isocyanate terminated polyester urethane prepared by reacting said urethane with a curative agent of the group consisting of 1) a hydroxyl terminated polyester urethane having an average molecular weight of less than about 6,000; 2) a solution of a lower molecular weight polyol or an aromatic diamine in a hydroxyl terminated polyester urethane having an average molecular weight of less than about 6,000; 3) a solution of lower molecular weight polyol or an aromatic diamine in a hydroxyl terminated polyester, the polyester moieties of the hydroxyl terminated polyester, the isocyanate terminated polyester urethane, and the hydroxyl terminated polyester urethane, which may have the same or different polyester moieties, being the moieties of those of hydroxyl terminated polyesters prepared by a) heating a polyol and a diloweralkyl ester of glutaric acid and a volatile monohydric alkanol or a mixture of said diloweralkyl ester of glutaric acid and another diloweralkyl ester of a dicarboxylic acid having at least 4 and not more than 20 carbon atoms and a volatile monohydric alkanol in the presence of a catalytic amount, up to 150 ppm tin, of a stannous salt of a carboxylic acid and at a temperature and in proportions sufficient to effect substantially complete transesterification with substantially complete alcoholysis of said diloweralkyl ester and with the distillation of the thus liberated said lower alkanol and without substantial distillation of polyol, said polyester being characterized by a residuum of tin which, due to the processing, no longer has the activity of a catalyst for promoting the reaction of isocyanate with the active hydrogen compounds, and a residuum of carbalkoxy groups, or by b) chain extending the hydroxyl terminated polyester prepared as above, by heating it with a chain-extending amount of a chain extender selected from the group consisting of a dicarboxylic acid of at least 4 carbon atoms and not more than 20 carbon atoms, or an anhydride thereof, and epsiloncaprolactone at a temperature sufficient to distill off any water formed to cause chain extension; 4) said aromatic diamine per se; and 5) said lower molecular weight polyol per se.

Claim 34

The polyester urethane elastomer of claim 29, in which the polyol moieties of the polyester and the polyester urethane are the same or different and are derived from polyols selected from the group consisting of alkylene diols containing from 2 to not more than 20 carbon atoms, diethylene glycol and higher poly(oxyethylene) glycols containing up to and including 10 oxyethylene groups, dipropylene glycol and higher poly(oxypropylene) glycols containing up to and including 6 oxypropylene groups, and cycloalkylene diols containing from 4 to not more than 8 carbon atoms, and bis(hydroxymethyl)benzenes, and polyols of the class consisting of 1,1,1-tris(hydroxymethyl)ethane, 1,1,1-tris(hydroxymethyl)propane, 1,2,4-butanetriol, glycerol, and pentaerythritol; in which the isocyanate moieties of the polyester urethane are all the same or different and are derived from isocyanates of the group consisting of 2,4-ditolylene isocyanate, alone or in admixture with 2,6-tolylene diisocyanate; 4,4'-methylenebis(phenyl isocyanate), alone or in admixture with its 2,4'- and/or 2,2'-isomers; 3,3'-dimethyl-4,4'-diisocyanatobiphenyl; 3,3'dimethoxy-4,4'-diisocyanatobiphenyl; 4,4'-methylenebis(3-methoxyphenyl isocyanate); 1,5-naphthalene diisocyanate; m-xylylene diisocyanate; p-xylylene diisocyanate; hexamethylene diisocyanate; isophorone diisocyanate; trimethylhexamethylene diisocyanate; methyl-2,4-diisocyanatocyclohexane; 4,4'-methylenebis(cyclohexyl isocyanate); 4,4',4"-tris(isocyanatophenyl)methane alone or in admixture with other isocyanates obtained by the phosgenation of aniline-formaldehyde resins; the triisocyanate obtained by the reaction of 3 mols of tolylene diisocyanate with 1 mol of 1,1,1-tris(hydroxymethyl)propane; and, the triisocyanate obtained by the reaction of 3 mols of hexamethylene diisocyanate with one mol of water; in which the aromatic diamine is selected from the group consisting of 4,4'-methylenebis(2-chloroaniline), 4,4'-methylenebis(2-methoxycarbonylaniline), 4,4'-methylenebis(2-methylaniline), 4,4'-methylenebis(2-methoxyaniline), 4,4'-methylenedianiline, alone or in admixture with its 2,4'- and/or 2,2'-isomers, 2,2'-thiodianiline, and mixed diamines obtained by the acid-catalyzed condensation of a mixture of aniline and/or aniline substituted in the ortho position by loweralkyl, lower-alkoxy, lower-alkoxycarbonyl, chloro, or bromo; in which the lower molecular weight polyol is selected from the group consisting of polymethylene glycols up to and including hexane-1,6-diol, diethylene glycol, triethylene glycol, propylene glycol, dipropylene glycol, 1,1,1-tris(hydroxymethyl)ethane, 1,1,1-tris(hydroxymethyl) propane, 1,2,4-butanetriol, 1,2,6-hexanetriol, and glycerol.

Claim 35

The polyester urethane elastomer of claim 30, in which the other dicarboxylic acid is adipic acid.

Claim 36

The polyester urethane elastomer of claim 30, in which the other dicarboxylic acid is azelaic acid.

Claim 37

The polyester urethane elastomer of claim 30, in which the polyester moiety contains a minor amount of pentamethylenecarboxy groups derived from epsilon-carprolactone.

Claim 38

The elastomer of claim 30, in which the curative agent is the aromatic diamine and the isocyanate is 2,4-tolylene diisocyanate.

Claim 39

The elastomer of claim 30, in which the curative agent is a solution of aromatic diamine in the hydroxyl terminated polyester or the hydroxyl terminated polyester urethane and the isocyanate is 2,4-tolylene diisocyanate.

Claim 40

The elastomer of claim 30, in which the curative agent is the aromatic diamine per se, or the lower molecular weight polyol per se.

Claim 41

The elastomer of claim 30, in which the agent is the lower molecular weight polyol curative and the isocyanate is 4,4'-methylenebis(phenyl isocyanate).

Claim 42

The elastomer of claim 30, in which the curative agent is a solution of the lower molecular weight polyol in the hydroxyl terminated polyester or the hydroxyl terminated polyester urethane and the isocyanate is 4,4'-methylenebis(phenyl isocyanate).

Claim 43

A curative agent for the chain extension of isocyanate terminated polyester urethanes which is a homogeneous liquid at room temperature and comprises a member of the group consisting of 1) a hydroxyl terminated polyester urethane having an average molecular weight of less than about 6,000, 2) a true solution of a lower molecular weight polyol or an aromatic diamine in a hydroxyl terminated polyester urethane having an average molecular weight of les than about 6,000, and 3) a true solution of lower molecular weight polyol or an aromatic diamine in a hydroxyl terminated polyester, the polyester moieties of the hydroxyl terminated polyester and the hydroxyl terminated polyester urethane, which may have the same or different polyester moieties, being those of hydroxyl terminated polyesters prepared by a) heating a polyol and a diloweralkyl ester of glutaric acid and a volatile lower monohydric alkanol or a mixture of said diloweralkyl ester of glutaric acid and another diloweralkyl ester of a dicarboxylic acid having at least 4 and not more than 20 carbon atoms and a volatile monohydric alkanol in the presence of a catalytic amount, up to 150 ppm tin, of a stannous salt of a carboxylic acid and at a temperature and in proportions sufficient to effect substantially complete transesterification with substantially complete alcoholysis of said diloweralkyl ester and with the distillation of the thus liberated said lower alkanol and without substantial distillation of polyol, said polyester being characterized by a residuum of tin which, due to the processing, no longer has the activity of a catalyst for promoting the reaction of isocyanate with active hydrogen compounds, and a residuum of carbalkoxy groups, or by b) subsequent reaction of a hydroxyl terminated polyester prepared as above, with or without additional polyol, with a dicarboxylic acid of at least 4 carbon atoms and not more than 20 carbon atoms, or an anhydride thereof, or epsilon-caprolactone.

Claim 44

A curative agent for the chain extension of isocyanate terminated polyester urethanes which is a homogeneous liquid at room temperature and comprises a member of the group consisting of 1) a hydroxyl terminated polyester urethane having an average molecular weight of less than about 6,000, 2) a true solution of a lower molecular weight polyol or an aromatic diamine in a hydroxyl terminated polyester urethane having an average molecular weight of les than about 6,000, and 3) a true solution of lower molecular weight polyol or an aromatic diamine in a hydroxyl terminated polyester, the polyester moieties of the hydroxyl terminated polyester and the hydroxyl terminated polyester urethane, which may have the same or different polyester moieties, being those of hydroxyl terminated polyesters prepared by a) heating a polyol and a diloweralkyl ester of glutaric acid and a volatile lower monohydric alkanol or a mixture of said diloweralkyl ester of glutaric acid and another diloweralkyl ester of a dicarboxylic acid having at least 4 and not more than 20 carbon atoms and a volatile monohydric alkanol in the presence of a catalytic amount, up to 150 ppm tin, of a stannous salt of a carboxylic acid and at a temperature and in proportions sufficient to effect substantially complete transesterification with substantially complete alcoholysis of said diloweralkyl ester and with the distillation of the thus liberated said lower alkanol and without substantial distillation of polyol, said polyester being characterized by a residuum of tin which, due to the processing, no longer has the activity of a catalyst for promoting the reaction of isocyanate with active hydrogen compounds, and a residuum of carbalkoxy groups, or by b) subsequent reaction of a hydroxyl terminated polyester prepared as above, with or without additional polyol, with a dicarboxylic acid of at least 4 carbon atoms and not more than 20 carbon atoms, or an anhydride thereof, or epsilon-caprolactone.

Claim 45

The curative agent of claim 39, in which the polyol used in said transesterification is selected from the group consisting of alkylene diols containing from 2 to not more than 20 carbon atoms, diethylene glycol and higher poly(oxyethylene) glycols containing up to and including 10 oxyethylene groups, dipropylene glycol and higher poly(oxypropylene) glycols containing up to and including 6 oxypropylene groups, cycloalkylene diols, containing from 4 to not more than 8 carbon atoms, and bis(hydroxymethyl)benzenes, and polyols of the class consisting of 1,1,1-tris(hydroxymethyl)ethane, 1,1,1-tris(hydroxymethyl) propane, 1,2,4-butanetriol, glycerol, and pentaerythritol.

Claim 46

The curative agent of claim 39, in which the other dicarboxylic acid is adipic acid.

Claim 47

The curative agent of claim 39, in which the other dicarboxylic acid is azelaic acid.

Claim 48

The curative agent of claim 39, in which the polyester moiety contains a minor amount of pentamethylenecarboxy groups derived from epilson-caprolactone.

Claim 49

The curative agent of claim 40, which comprises the solution of aromatic diamine in the hydroxyl terminated polyester of member 3.

Claim 50

The curative agent of claim 40, which comprises the solution of aromatic diamine in the hydroxyl terminated polyester urethane of member 2 and the isocyanate moiety of which is 2,4-tolylene diisocyanate.

Claim 51

The curative agent of claim 40, which comprises the hydroxyl terminated polyester urethane of member 1.

Claim 52

The curative agent of claim 40, which comprises the solution of the lower molecular weight polyol in the hydroxyl terminated polyester of member 3.

Claim 53

The curative agent of claim 40, which comprises the solution in the hydroxyl terminated polyester urethane of a lower molecular weight polyol of member 2 in which the polyol is selected from the group consisting of polymethylene glycols up to and including hexane-1,6-diol, diethylene glycol, triethylene glycol, propylene glycol, dipropylene glycol, 1,1,1-tris(hydroxymethyl)ethane, 1,1,1-tris(hydroxymethyl)propane, 1,2,4-butanetriol, 1,2,6-hexanetriol, and glycerol, and in which the isocyanate moiety is that of 4,4'-methylenebis(phenyl isocyanate).

Claim 54

The hydroxyl terminated polyester urethane prepared by the reaction of organic diisocyanate with a molar excess of hydroxyl terminated polyester which has a dicarboxylic acid moiety of at least 4 and not more than 20 carbon atoms which consists predominantly of the glutaric acid moiety prepared by heating a polyol and a diloweralkyl ester of the acid or acids and a volatile lower monohydric alkanol in the presence of a catalytic amount, up to 150 ppm tin, of a stannous salt of carboxylic acid and at a temperature and in proportions sufficient to effect substantially complete transesterification with substantially complete alcoholysis of said diloweralkyl ester and with the distillation of the thus liberated said lower alkanol and without substantial distillation of polyol, said polyester having a residuum of tin which, due to the processing, no longer has the activity of a catalyst for promoting the reaction of isocyanate with active hydrogen compounds, and a residuum of carbalkoxy groups.

Claim 55

The hydroxyl terminated polyester urethane prepared by the reaction of organic diisocyanate with a molar excess of hydroxyl terminated polyester which has a dicarboxylic acid moiety of at least 4 and not more than 20 carbon atoms which consists predominantly of the glutaric acid moiety prepared by heating a polyol and a diloweralkyl ester of the acid or acids and a volatile lower monohydric alkanol in the presence of a catalytic amount, up to 150 ppm tin, of a stannous salt of carboxylic acid and at a temperature and in proportions sufficient to effect substantially complete transesterification with substantially complete alcoholysis of said diloweralkyl ester and with the distillation of the thus liberated said lower alkanol and without substantial distillation of polyol, said polyester having a residuum of tin which, due to the processing, no longer has the activity of a catalyst for promoting the reaction of isocyanate with active hydrogen compounds, and a residuum of carbalkoxy groups.

Claim 56

The hydroxyl terminated polyester urethane of claim 49, in which the isocyanate is selected from the group consisting of 2,4-tolylene diisocyanate, alone or in admixture with 2,6-tolylene diisocyanate; 4,4'-methylenebis(phenyl isocyanate), alone or in admixture with its 2,4'- and/or 2,2'-isomers; 3,3'-dimethyl-4,4'-diisocyanatobiphenyl; 3,3'dimethoxy-4,4'-diisocyanatobiphenyl; 4,4'-methylenebis(3-methoxyphenyl isocyanate); 1,5-naphthalene diisocyanate; m-xylylene diisocyanate; p-xylylene diisocyanate; hexamethylene diisocyanate; isophorone diisocyanate; trimethylhexamethylene diisocyanate; methyl-2,4-diisocyanatocyclohexane; 4,4'-methylenebis(cyclohexyl isocyanate); 4,4',4"-tris(isocyanatophenyl)methane; poly-isocyanates obtained by the phosgenation of of aniline-formaldehyde resins; the triisocyanate obtained by the reaction of 3 mols of tolylene diisocyanate with 1 mol of 1,1,1-tris(hydroxymethyl)propane; and, the triisocyanate obtained by the reaction of 3 mols of hexamethylene diisocyanate with one mol of water.

Claim 57

The hydroxyl terminated polyester urethane of claim 50, in which the polyols are the same or different polyols selected from the group consisting of alkylene diols, containing from 2 to not more than 20 carbon atoms, diethylene glycol and higher poly(oxyethylene) glycols containing up to and including 10 oxyethylene groups, dipropylene glycol and higher poly(oxypropylene) glycols containing up to and including 6 oxypropylene groups, al-cycloalkylene diols, ac-cycloalkylene diols, and al- ac-cycloalkylene diols containing from 4 to not more than 8 carbon atoms, and bis(hydroxymethyl)benzenes, and polyols of the class consisting of 1,1,1-tris(hydroxymethyl)ethane, 1,1,1-tris(hydroxymethyl)propane, 1,2,4-butanetriol, glycerol, and pentaerythritol.

Claim 58

The hydroxyl terminated polyester urethane of claim 51, in which a minor component of the carboxylic acid moiety is the adipic acid moiety.

Claim 59

The hydroxyl terminated polyester urethane of claim 51, in which a minor component of the carboxylic acid moiety is the azelaic acid moiety.

Claim 60

The hydroxyl terminated polyester urethane of claim 51, in which the polyester moiety contains a minor amount of pentamethylene carboxy groups derived from epsilon-caprolactone.

Claim 61

The hydroxyl terminated polyester urethane of claim 51, having an acid number not greater than 3 and a residuum of carbalkoxy groups not greater than 2 percent.

Claim 62

The curvature agent of claim 40, in which the isocyanate moiety of the hydroxyl terminated polyester urthane is derived from an isocyanate of the group consisting of 2,4-tolylene diisocyanate, alone or in admixture with 2,6-tolylene diisocyanate; 4,4'-methylenebis(phenyl isocyanate), alone or in admixture with its 2,4'-and/or 2,2'-isomers; 3,3'-dimethyl-4,4'-diisocyanatobiphenyl; 3,3'-dimethoxy-4,4'-diisocyanatobiphenyl; 4,4'-methylenebis(3-methoxyphenyl isocyanate); 1,5naphthalene diisocyanate; m-xylylene diisocyanate; p-xylylene diisocyanate; hexamethylene diisocyanate; isophorone diisocyanate; trimethylhexamethylene diisocyanate; methyl-2,4-diisocyanatocyclohexane; 4,4'-methylenebis(cyclohexyl isocyanate); 4,4',4"-tris(isocyanatophenyl) methane; polyisocyanates obtained by the phosgenation of aniline-formaldehyde resins; the triisocyanate obtained by the reaction of 3 mols of tolylene diisocyanate with 1 mol of 1,1,1-tris(hydroxymethyl)propane; and, the triisocyanate obtained by the reaction of 3 mols of hexamethylene diisocyanate with one mol of water; in which the aromatic diamine curative is selected from the group consisting of 4,4'-methylenebis(2-chloroaniline), 4,4'-methylenebis(2methoxycarbonylaniline), 4,4'-methylenebis(2-methylaniline), 4,4'-methylenebis(2methoxyaniline), 4,4'-methylenedianiline, alone or in admixture with its 2,4'-and/or 2,2'-isomers, 2,2'-thiodianiline, and mixed diamines obtained by the acid-catalyzed condensation of formaldehyde with aniline and/or aniline substituted in the ortho position by chlorine or bromine.

Claim 63

The curative agent of claim 40, in which the lower molecular weight polyol is selected from the group consisting of polymethylene glycols up to and including hexane-1,6-diol, diethylene glycol, triethylene glycol, propylene glycol, dipropylene glycol, 1,1,1-tris(hydroxymethyl)ethane, 1,1,1-tris(hydroxymethyl)propane, 1,2,4-butanetriol, 1,2,6-hexanetriol, and glycerol, and the isocyanate moiety is that of 4,4'-methylenebis(phenyl isocyanate).