Green strength of elastomers
Assignee: Goodyear Tire and Rubber Co
•
Filing: 1976-10-22
•
Granted: 1978-06-13
•
Expires: 1996-10-22
Abstract
Abstract The green strength of synthetic elastomers is improved by forming interpolymers from at least one type of various synthetic elastomer forming monomers with an epoxy containing monomer having the formula: ##STR1## where R 1 contains from 0 to 8 carbon atoms and R 2 contains from 1 to 4 carbon atoms. Typical elastomer forming monomers include at least one conjugated diene having from 4 to 10 carbon atoms, olefins having from 2 to 14 carbon atoms along with a diene having from 4 to 6 carbon atoms, and combinations thereof. The interpolymer preferably is blended with synthetic elastomers or natural rubber (cis-1,4-polyisoprene) and utilized for various industrial uses such as tire carcasses including radial truck tire carcasses. The green strength is further improved if a small amount of an epoxy cross-linking agent is utilized. Examples of suitable cross-linking agents include monoamines and polyamines, monoanhydrides and polyanhydrides, and monocarboxylic acids, as well as polycarboxylic acids. Desirably, the interpolymer of the synthetic elastomer forming monomer and the epoxy containing monomer is blended with various types of synthetic elastomers or natural rubber in the presence of an epoxy cross-linking agent in a suitable mixing vessel such as a Banbury.
Inventors
- 👤 Paul H. Sandstrom
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 16:26
CPC Classifications
C; C08; C08F; C08F236/00; C08F236/02; C08F236/04; C08C; C08C19/00; C08C19/30; C08C19/34; C08C19/40; C08F220/00; C08F220/02; C08F220/10; C08F220/26; C08F220/32; C08F220/325; C08F236/06
Claims Analysis
Total Claims: 32
Claim 1
Independent Claim
320 words
A process, comprising: forming a synthetic elastomer interpolymer having improved green strength by reacting at least one type of a synthetic elastomer forming monomer with an epoxy containing monomer, said synthetic elastomer forming monomer selected from the class consisting of at least one type of a conjugated diene monomer having from 4 to 10 carbon atoms, and at least one type of an olefin monomer having from 2 to 14 carbon atoms in combination with at least one type of a conjugated diene monomer having from 4 to 10 carbon atoms, said epoxy containing monomer selected from the class of compounds having the formula ##STR4## where R 2 contains from 1 to 4 carbon atoms and R 1 contains from 0 to 8 carbon atoms, the amount of said epoxy compound in said interpolymer ranging from about 0.5 percent to about 75 percent by weight based upon the total weight of said interpolymer, partially cross-linking said interpolymer to improve the green strength of said interpolymer by adding and reacting from 0.1 to 2.0 parts by weight based upon 100 parts of said interpolymer of an epoxy cross-linking agent, said epoxy cross-linking agent selected from the class consisting of monoamines, polyamines, monoanhydrides, monocarboxylic acids and polycarboxylic acids, said monoamines and said polyamines selected from the class consisting of an aliphatic containing from 1 to 16 carbon atoms, a cycloaliphatic containing from 4 to 6 carbon atoms, an aromatic containing from 6 to 16 carbon atoms, and combinations thereof, said monoanhydrides selected from the class consisting of an aliphatic containing from 1 to 30 carbon atoms, a cycloaliphatic containing from 4 to 30 carbon atoms, an aromatic containing from 6 to 30 carbon atoms, and combinations thereof, and said monocarboxylic acids and said polycarboxylic acids selected from the class consisting of an aliphatic containing from 1 to 30 carbon atoms, an aromatic containing from 6 to 30 carbon atoms, and combinations thereof.
Claim 2
Dependent Claim
320 words
A process, comprising: forming a synthetic elastomer interpolymer having improved green strength by reacting at least one type of a synthetic elastomer forming monomer with an epoxy containing monomer, said synthetic elastomer forming monomer selected from the class consisting of at least one type of a conjugated diene monomer having from 4 to 10 carbon atoms, and at least one type of an olefin monomer having from 2 to 14 carbon atoms in combination with at least one type of a conjugated diene monomer having from 4 to 10 carbon atoms, said epoxy containing monomer selected from the class of compounds having the formula ##STR4## where R 2 contains from 1 to 4 carbon atoms and R 1 contains from 0 to 8 carbon atoms, the amount of said epoxy compound in said interpolymer ranging from about 0.5 percent to about 75 percent by weight based upon the total weight of said interpolymer, partially cross-linking said interpolymer to improve the green strength of said interpolymer by adding and reacting from 0.1 to 2.0 parts by weight based upon 100 parts of said interpolymer of an epoxy cross-linking agent, said epoxy cross-linking agent selected from the class consisting of monoamines, polyamines, monoanhydrides, monocarboxylic acids and polycarboxylic acids, said monoamines and said polyamines selected from the class consisting of an aliphatic containing from 1 to 16 carbon atoms, a cycloaliphatic containing from 4 to 6 carbon atoms, an aromatic containing from 6 to 16 carbon atoms, and combinations thereof, said monoanhydrides selected from the class consisting of an aliphatic containing from 1 to 30 carbon atoms, a cycloaliphatic containing from 4 to 30 carbon atoms, an aromatic containing from 6 to 30 carbon atoms, and combinations thereof, and said monocarboxylic acids and said polycarboxylic acids selected from the class consisting of an aliphatic containing from 1 to 30 carbon atoms, an aromatic containing from 6 to 30 carbon atoms, and combinations thereof.
Claim 3
Dependent Claim
25 words
A process according to claim 1, wherein R 2 is 1 or 2 carbon atoms and R 1 is from 0 to 4 carbon atoms.
Claim 4
Dependent Claim
42 words
A process according to claim 2, wherein said synthetic elastomer monomers are selected from the class consisting of butadiene, isoprene, piperylene, mixtures of isoprene and butadiene, mixtures of butadiene and piperylene, mixtures of styrene and butadiene, and mixtures of alpha-methylstyrene and butadiene.
Claim 5
Dependent Claim
23 words
A process according to claim 3, wherein said epoxy cross-linking agent is selected from the class consisting of said monoamines and said polyamines.
Claim 6
Dependent Claim
41 words
A process according to claim 4, wherein the amount of said epoxy compound in said interpolymer ranges from about 1 percent to about 25 percent by weight and R 2 is 1 carbon atom and R 1 is 0 carbon atoms.
Claim 7
Dependent Claim
35 words
A process according to claim 5, wherein said cross-linking agents are selected from the class consisting of pentamethylenediamine, triethylenetetramine, diethylaminopropylamine, tetraethylene pentamine, menthane diamine, 4,4'-diaminodiphenyl sulfone, 4,4'-methylenebis(2-carbomethoxy) aniline, 4,4'-methylenebis aniline, diaminodiphenyldisulfide and benzene tetracarboxylic anhydride.
Claim 8
Dependent Claim
20 words
A process according to claim 6, wherein said amount of cross-linking agent ranges from about 0.1 to about 0.5 parts.
Claim 9
Dependent Claim
12 words
A process according to claim 1, wherein said cross-linked interpolymer is compounded.
Claim 10
Dependent Claim
12 words
A process according to claim 7, wherein said cross-linked interpolymers is compounded.
Claim 11
Dependent Claim
287 words
A process comprising: forming a synthetic elastomer interpolymer having improved green strength from at least one type of a synthetic elastomer forming monomer and from an epoxy containing monomer, said synthetic elastomer forming monomer selected from the class consisting of at least one type of a conjugated diene monomer having from 4 to 10 carbon atoms, and at least one type of an olefin monomer having from 2 to 14 carbon atoms in combination with at least one type of a conjugated diene monomer having from 4 to 10 carbon atons, said epoxy containing monomer selected from the class of compounds having the formula: ##STR5## where R 2 contains from 1 to 4 carbon atoms and R 1 contains from 0 to 8 carbon atoms, the amount of said epoxy compound in said interpolymer ranging from about 0.5 percent to about 75 percent by weight based upon the total weight of said interpolymer, improving the green strength of an elastomer selected from the class consisting of synthetic elastomers and natural rubber by adding said interpolymer to form a blend, the amount of said epoxy containing interpolymer in said blend ranging from about 2 percent to about 98 percent by weight based upon the total weight of said blend, said synthetic elastomers selected from the class consisting of nitrile rubber, butyl rubber, chlorinated butyl rubber brominated butyl rubber, polyalkenylenes, ethylene-propylene-diene rubber, polymers made from at least one type of a conjugated diene monomer having from 4 to 10 carbon atoms, and polymers made from at least one type of an olefin monomer having from 2 to 14 carbon atoms in combination with at least one type of a conjugated diene monomer having from 4 to 10 carbon atoms.
Claim 12
Dependent Claim
287 words
A process comprising: forming a synthetic elastomer interpolymer having improved green strength from at least one type of a synthetic elastomer forming monomer and from an epoxy containing monomer, said synthetic elastomer forming monomer selected from the class consisting of at least one type of a conjugated diene monomer having from 4 to 10 carbon atoms, and at least one type of an olefin monomer having from 2 to 14 carbon atoms in combination with at least one type of a conjugated diene monomer having from 4 to 10 carbon atons, said epoxy containing monomer selected from the class of compounds having the formula: ##STR5## where R 2 contains from 1 to 4 carbon atoms and R 1 contains from 0 to 8 carbon atoms, the amount of said epoxy compound in said interpolymer ranging from about 0.5 percent to about 75 percent by weight based upon the total weight of said interpolymer, improving the green strength of an elastomer selected from the class consisting of synthetic elastomers and natural rubber by adding said interpolymer to form a blend, the amount of said epoxy containing interpolymer in said blend ranging from about 2 percent to about 98 percent by weight based upon the total weight of said blend, said synthetic elastomers selected from the class consisting of nitrile rubber, butyl rubber, chlorinated butyl rubber brominated butyl rubber, polyalkenylenes, ethylene-propylene-diene rubber, polymers made from at least one type of a conjugated diene monomer having from 4 to 10 carbon atoms, and polymers made from at least one type of an olefin monomer having from 2 to 14 carbon atoms in combination with at least one type of a conjugated diene monomer having from 4 to 10 carbon atoms.
Claim 13
Dependent Claim
173 words
A process according to claim 1, including further improving green strength by adding from about 0.5 to about 10 parts by weight based upon 100 parts of said interpolymer of an epoxy cross-linking agent to selectively cross-link said interpolymer blend, said epoxy cross-linking agent is selected from the class consisting of monoamines, polyamines monoanhydrides, monocarboxylic acids and polycarboxylic acids, said monoamines and said polyamines selected from the class consisting of an aliphatic containing from 1 to 16 carbon atoms, a cycloaliphatic containing from 4 to 6 carbon atoms, an aromatic containing from 6 to 16 carbon atoms and combinations thereof, said monoanhydrides selected from the class consisting of an aliphatic containing from 1 to 30 carbon atoms, a cycloaliphatic containing from 4 to 30 carbon atoms, an aromatic containing from 6 to 30 carbon atoms and combinations thereof, and said monocarboxylic acids and said polycarboxylic acids selected from the class consisting of an aliphatic containing from 1 to 30 carbon atons, an aromatic containing from 6 to 30 carbon atoms and combinations thereof.
Claim 14
Dependent Claim
25 words
A process according to claim 11, wherein R 2 is 1 or 2 carbon atoms and R 1 is from 0 to 8 carbon atoms.
Claim 15
Dependent Claim
45 words
A process according to claim 12, wherein said synthetic elastomer monomers forming said interpolymer are selected from the class consisting of butadiene, isoprene, piperylene, mixtures of isoprene and butadiene, mixtures of butadiene and piperylene, mixtures of styrene and butadiene, and mixtures of alpha-methylstyrene and butadiene.
Claim 16
Dependent Claim
52 words
A process according to claim 13, wherein the amount of epoxy containing compound in said interpolymer ranges from about 1 percent to about 25 percent by weight and wherein the amount of said epoxy cross-linking agent ranges from about 0.5 to about 2 parts by weight per 100 parts of said interpolymer.
Claim 17
Dependent Claim
72 words
A process according to claim 14, wherein R 2 is 1 carbon atom and R 1 is hydrogen, said epoxy containing interpolymer ranges from about 2 percent to about 50 percent by weight based upon the total weight of said blend and said epoxy cross-linking agents are selected from the class consisting of pentamethylenediamine, triethylenetetramine, diethylaminopropylamine, tetraethylene pentamine, menthane diamine, 4,4'-diaminodiphenyl sulfone, 4,4'-methylenebis (2-carbomethoxy) aniline, 4,4'-methylenebis aniline, diaminodiphenyldisulfide and benzene tetracarboxylic anhydride.
Claim 18
Dependent Claim
20 words
A process according to claim 15, wherein said blend polymers are selected from the class consisting of high cis-1,4-polyisoprene, high
Claim 19
Dependent Claim
8 words
cis-1,4-polybutadiene, EPDM, and styrene-butadiene rubber. 17. A process
Claim 20
Dependent Claim
8 words
cis-1,4-polybutadiene, EPDM, and styrene-butadiene rubber. 17. A process
Claim 21
Dependent Claim
12 words
according to claim 10, wherein said blend is compounded. 18. A process
Claim 22
Dependent Claim
12 words
according to claim 11, wherein said blend is compounded. 19. A process
Claim 23
Dependent Claim
203 words
according to claim 16, wherein said blend is compounded. 20. A process comprising: forming an interpolymer synthetic elastomer having improved green strength from at least one type of a synthetic elastomer forming monomer and from an epoxy containing monomer, said synthetic elastomer forming monomer selected from the class consisting of at least one type of a conjugated diene monomer having from 4 to 10 carbon atoms, and at least one type of an olefin monomer having from 2 to 14 carbon atoms in combination with at least one type of a conjugated diene monomer having from 4 to 10 carbon atoms, said epoxy containing monomer selected from the class of compounds having the formula: ##STR6## where R 2 contains from 1 to 4 carbon atoms and R 1 contains from 0 to 8 carbon atoms, the amount of said epoxy compound in said interpolymer ranges from about 0.5 percent to about 75 percent by weight based upon the total weight of said interpolymer, improving the green strength of an elastomer selected from the class consisting of synthetic elastomers and natural rubber by adding said interpolymer to form a blend, and said synthetic elastomer being polymers made from at least one type of a
Claim 24
Dependent Claim
184 words
conjugated diene monomer having from 4 to 10 carbon atoms. 21. A process according to claim 20, including further improving green strength by adding from about 0.5 to about 10 parts by weight based upon 100 parts of said interpolymer of an epoxy cross-linking agent to selectively cross-link said interpolymer blend, said epoxy cross-linking agent is selected from the class consisting of monoamines, polyamines, monoanhydrides, monocarboxylic acids and polycarboxylic acids, said monoamines and said polyamines selected from the class consisting of an aliphatic containing from 1 to 16 carbon atoms, a cycloaliphatic containing from 4 to 6 carbon atoms, an aromatic containing from 6 to 16 carbon atoms and combinations thereof, said monoanhydrides selected from the class consisting of an aliphatic containing from 1 to 30 carbon atoms, a cycloaliphatic containing from 4 to 30 carbon atoms, an aromatic containing from 6 to 30 carbon atoms and combinations thereof, and said monocarboxylic acids and said polycarboxylic acids selected from the class consisting of an aliphatic containing from 1 to 30 carbon atoms, an aromatic containing from 6 to 30 carbon atoms and combinations thereof.
Claim 25
Dependent Claim
14 words
A process according to claim 21, wherein R 2 is 1 or 2 carbon
Claim 26
Dependent Claim
55 words
atoms and R 1 is from 0 to 8 atoms. 23. A process according to claim 22, wherein said synthetic elastomer monomers forming said interpolymers are selected from the class consisting of butadiene, isoprene, piperylene, mixtures of isoprene and butadiene, mixtures of butadiene and piperylene, mixtures of styrene and butadiene, and mixtures of alpha-methylstyrene and
Claim 27
Dependent Claim
49 words
butadiene. 24. A process according to claim 23, wherein the amount of epoxy containing compound in said interpolymer ranges from about 1 percent to about 25 percent by weight and wherein the amount of said epoxy cross-linking agent ranges from about 0.5 to about 2 parts by weight per
Claim 28
Dependent Claim
73 words
100 parts of said interpolymer. 25. A process according to claim 24, wherein R 2 is 1 carbon atom and R 1 is hydrogen, said epoxy containing interpolymer ranges from about 2 percent to about 50 percent by weight based upon the total weight of said blend and said epoxy crosslinking agents are selected from the class consisting of pentamethylenediamine, triethylenetetramine, diethylaminopropylamine, tetraethylene, pentamine, methane diamine, 4,4 '-diaminodiphenyl sulfone, 4,4'-methylenebis(2-carbomethoxy) aniline, 4,4'-methylenebis aniline,
Claim 29
Dependent Claim
27 words
diaminodiphenyldisulfide and benzene tetracarboxylic anhydride. 26. A process according to claim 25, wherein said blend polymers are selected from the class consisting of high cis-1,4-polyisoprene and high
Claim 30
Dependent Claim
10 words
cis-1,4-polybutadiene. 27. A process according to claim 20, wherein said
Claim 31
Dependent Claim
12 words
blend is compounded. 28. A process according to claim 21, wherein said
Claim 32
Dependent Claim
15 words
blend is compounded. 29. A process according to claim 26, wherein said blend is compounded.
References Cited (Backward Citations)
US2839514A
Cited
US3166609A
Cited
US3947523A
Cited
US3383372A
Cited
US3872036A
Cited
US3652523A
Cited
US3652476A
Cited
US3935375A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-06-12 | 1981-12-12 | 1982-06-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-06-12 | 1985-12-12 | 1986-06-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-06-12 | 1989-12-12 | 1990-06-13 | $7700.00 | Window Closed / Lapsed |