Chemical fabrication of overhanging ledges and reflection gratings for surface wave devices
Assignee: Texas Instruments Inc
•
Filing: 1973-12-28
•
Granted: 1978-06-13
•
Expires: 1993-12-28
Abstract
Abstract A method is described of etching structures into α quartz and LiNbO 3 , two materials widely used in surface wave devices and which heretofore have not been found suitable for use with chemical etching techniques, in which concentrated HF acid at a predetermined temperature is used as an etchant, and the formation of overhanging ledges accomplished through a specific crystal orientation. Steps are shown which avoid the problems associated with suitable masking of the surface, which problems were encountered in the prior art, a primary step being one of a mechanical-chemical polishing to assure that the resist mask adheres to the surface properly.
Inventors
- 👤 Donald F. Weirauch
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 03:19
CPC Classifications
C; C09; C09K; C09K13/00; C09K13/04; C09K13/08; G; G02; G02B; G02B6/00; G02B6/10; G02B6/12; G02B6/13; G02B6/136; G03; G03F; G03F7/00; G03F7/0005
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
287 words
A method of etching a surface of a substrate to be employed in an acoustic surface wave device, wherein the pattern to be etched into the substrate surface produces an overhanging ledge structure and the substrate is made of a piezoelectric material of ST cut α quartz, said method comprising: chemically polishing the surface of the substrate by applying a chemical mixture to the substrate surface effective to remove amorphous material from the substrate surface for providing a polished crystalline finish to the substrate surface, applying a layer of chromium over the polished substrate surface, applying a layer of gold over the chromium layer, applying a layer of photoresist material over the gold layer, photographically exposing the layer of photoresist material to a pattern of a desired image wherein the pattern is oriented so that its major axis is perpendicular to a line which falls within boundaries estabished by a first line making an angle of 30° with the -X axis of the crystal lattice of said ST cut α quartz material and another line making an angle of 40° with the +X axis of the said crystal lattice, developing the photoresist layer to produce the pattern therein, etching the pattern into the gold layer from the patterned photoresist layer, etching the pattern into the chromium layer, etching the pattern into said substrate surface by immersing the substrate surface with the patterned layers of chromium and gold thereon in a solution of hydrofluoric acid maintained at a temperature of approximately 25° C, removing the etched substrate surface with the patterned layers of chromium and gold thereon from the solution of hydrofluoric acid, and stripping off the patterned layers of gold and chromium from the etched substrate surface.
Claim 2
Independent Claim
287 words
A method of etching a surface of a substrate to be employed in an acoustic surface wave device, wherein the pattern to be etched into the substrate surface produces an overhanging ledge structure and the substrate is made of a piezoelectric material of ST cut α quartz, said method comprising: chemically polishing the surface of the substrate by applying a chemical mixture to the substrate surface effective to remove amorphous material from the substrate surface for providing a polished crystalline finish to the substrate surface, applying a layer of chromium over the polished substrate surface, applying a layer of gold over the chromium layer, applying a layer of photoresist material over the gold layer, photographically exposing the layer of photoresist material to a pattern of a desired image wherein the pattern is oriented so that its major axis is perpendicular to a line which falls within boundaries estabished by a first line making an angle of 30° with the -X axis of the crystal lattice of said ST cut α quartz material and another line making an angle of 40° with the +X axis of the said crystal lattice, developing the photoresist layer to produce the pattern therein, etching the pattern into the gold layer from the patterned photoresist layer, etching the pattern into the chromium layer, etching the pattern into said substrate surface by immersing the substrate surface with the patterned layers of chromium and gold thereon in a solution of hydrofluoric acid maintained at a temperature of approximately 25° C, removing the etched substrate surface with the patterned layers of chromium and gold thereon from the solution of hydrofluoric acid, and stripping off the patterned layers of gold and chromium from the etched substrate surface.
Claim 3
Independent Claim
294 words
A method of etching a surface of a substrate to be employed in an acoustic surface wave device, wherein the pattern to be etched into the substrate surface produces an overhanging ledge structure and the substrate is made of a piezoelectric material of Y-cut lithium niobate, said method comprising: chemically polishing the surface of the substrate by applying a chemical mixture to the substrate surface effective to remove amorphous material from the substrate surface for providing a polished cyrstalline finish to the substrate surface, applying a layer of chromium over the polished substrate surface, applying a layer of gold over the chromium layer, applying a layer of photoresist material over the gold layer, photographically exposing the layer of photoresist material to a pattern of a desired image wherein the pattern is oriented so that its major axis is perpendicular to a line which falls within boundaries established by a first line making an angle of 30° with the -X axis and 60° with the -Z axis and a second line making an angle of 30° with the +X axis and 60° with the -Z axis of the crystal lattice of said Y-cut lithium niobate material, developing the photoresist layer to produce the pattern therein, etching the pattern into the gold layer from the patterned photoresist layer, etching the pattern into the chromium layer, etching the pattern into said substrate surface by immersing the substrate surface with the patterned layers of chromium and gold thereon in a solution of hydrofluoric acid maintained at a temperature of greater than 100° C, removing the etched substrate surface with the patterned layers of chromium and gold thereon from the solution of hydrofluoric acid, and stripping off the patterned layers of gold and chromium from the etched substrate surface.
Claim 4
Independent Claim
294 words
A method of etching a surface of a substrate to be employed in an acoustic surface wave device, wherein the pattern to be etched into the substrate surface produces an overhanging ledge structure and the substrate is made of a piezoelectric material of Y-cut lithium niobate, said method comprising: chemically polishing the surface of the substrate by applying a chemical mixture to the substrate surface effective to remove amorphous material from the substrate surface for providing a polished cyrstalline finish to the substrate surface, applying a layer of chromium over the polished substrate surface, applying a layer of gold over the chromium layer, applying a layer of photoresist material over the gold layer, photographically exposing the layer of photoresist material to a pattern of a desired image wherein the pattern is oriented so that its major axis is perpendicular to a line which falls within boundaries established by a first line making an angle of 30° with the -X axis and 60° with the -Z axis and a second line making an angle of 30° with the +X axis and 60° with the -Z axis of the crystal lattice of said Y-cut lithium niobate material, developing the photoresist layer to produce the pattern therein, etching the pattern into the gold layer from the patterned photoresist layer, etching the pattern into the chromium layer, etching the pattern into said substrate surface by immersing the substrate surface with the patterned layers of chromium and gold thereon in a solution of hydrofluoric acid maintained at a temperature of greater than 100° C, removing the etched substrate surface with the patterned layers of chromium and gold thereon from the solution of hydrofluoric acid, and stripping off the patterned layers of gold and chromium from the etched substrate surface.
References Cited (Backward Citations)
US3657029A
Cited
US3634159A
Cited
US3756887A
Cited
US3816194A
Cited
US3785892A
Cited
US3799642A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-06-12 | 1981-12-12 | 1982-06-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-06-12 | 1985-12-12 | 1986-06-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-06-12 | 1989-12-12 | 1990-06-13 | $7700.00 | Window Closed / Lapsed |