Powder coating composition
Assignee: Nippon Paint Co Ltd
•
Filing: 1975-11-05
•
Granted: 1978-06-06
•
Expires: 1995-11-05
Abstract
Abstract A powder coating composition which comprises at least one solid resin and at least one polyisocyanate compound having an average of at least two isocyanate groups per molecule, in a weight ratio of from 99 : 1 to 30 : 70 is provided. The composition has excellent storage stability and affords a coating film with excellent properties.
Inventors
- 👤 Koichi Tsutsui
- 👤 Yoshio Eguchie
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 16:38
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/70; C08G18/72; C08G18/80; C08G18/8003; C08G18/28; C08G18/40; C08G18/42; C08G18/58; C08G18/62; C08G18/6216; C09; C09D; C09D175/00; C08G2150/00; C08G2150/20; Y; Y10; Y10S; Y10S524/00; Y10S524/904
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
115 words
A substantially non-sticky, melt blended, thermosetting powder coating composition in the dry state which comprises at least one solid resin having a glass transition temperature of from 5° to 150° C and an OH content of 1 × 10 -4 to 45 × 10 -4 g equivalent/g, the OH group liberating an active hydrogen atom, and at least one polyisocyanate compound which is solid at room temperature and having at least two isocyanate groups in each molecule in an average weight ratio of about 99 : 1 to 30 : 70 and a molar proportion of the active hydrogen in the former to the isocyanate group in the latter of 1 : 0.2 - 2.
Claim 2
Dependent Claim
115 words
A substantially non-sticky, melt blended, thermosetting powder coating composition in the dry state which comprises at least one solid resin having a glass transition temperature of from 5° to 150° C and an OH content of 1 × 10 -4 to 45 × 10 -4 g equivalent/g, the OH group liberating an active hydrogen atom, and at least one polyisocyanate compound which is solid at room temperature and having at least two isocyanate groups in each molecule in an average weight ratio of about 99 : 1 to 30 : 70 and a molar proportion of the active hydrogen in the former to the isocyanate group in the latter of 1 : 0.2 - 2.
Claim 3
Dependent Claim
32 words
The powder coating composition according to claim 1, wherein the polyisocyanate compound is an addition product of a diisocyanate or triisocyanate and a chain extender having two or more active hydrogen atoms.
Claim 4
Dependent Claim
26 words
The powder coating composition according to claim 1, wherein the polyisocyanate compound is a biuret or allophanate structure polyisocyanate compound derived from a diisocyanate or triisocyanate.
Claim 5
Dependent Claim
41 words
The powder coating composition according to claim 1, wherein the polyisocyanate compound is an addition product of a biuret or allophanate structure polyisocyanate compound derived from a diisocyanate or triisocyanate and a chain extender having two or more active hydrogen atoms.
Claim 6
Dependent Claim
68 words
The powder coating composition according to claim 1, wherein the polyisocyanate compound is the reaction product obtained by reacting a diisocyanate or triisocyanate or a biuret or allophanate structure polyisocyanate compound derived therefrom with a chain extender having two or more active hydrogen atoms in an equivalent ratio of the free isocyanate group in the former to the active hydrogen atom in the latter being more than 1.
Claim 7
Dependent Claim
31 words
The powder coating composition according to claim 5, wherein the equivalent ratio of the free isocyanate group to the active hydrogen atom is from 1.5 : 1 to 10 : 1.
Claim 8
Dependent Claim
44 words
The powder coating composition according to claim 1, wherein the solid resin is an acrylic resin having a number average molecular weight of 1,000 to 30,000 and an active hydrogen atom content of 1 × 10 -4 to 30 × 10 -4 mol equivalent/g.
Claim 9
Dependent Claim
44 words
The powder coating composition according to claim 1, wherein the solid resin is a polyester resin having a number average molecular weight of 500 to 5,000 and an active hydrogen atom content of 3 × 10 -4 to 45 × 10 -4 mol equivalent/g.
Claim 10
Dependent Claim
45 words
The powder coating composition according to claim 1, wherein the solid resin is an acryl-modified polyester resin having a number average molecular weight of 500 to 20,000 and an active hydrogen atom content of 3 × 10 -4 to 45 × 10 -4 mol equivalent/g.
Claim 11
Dependent Claim
23 words
The powder coating composition according to claim 1, wherein the solid resin is an epoxy resin, an amino resin or a polyether resin.
References Cited (Backward Citations)
US3240842A
Cited
US3409461A
Cited
US3647848A
Cited
US3560447A
Cited
US3620680A
Cited
US3676405A
Cited
US3819586A
Cited
US3822240A
Cited
US3663472A
Cited
US3917741A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-06-05 | 1981-12-05 | 1982-06-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-06-05 | 1985-12-05 | 1986-06-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-06-05 | 1989-12-05 | 1990-06-06 | $7700.00 | Window Closed / Lapsed |