Process for making porous metal containing powder coating compositions

Claim 2

A process for preparing uncured curable porous metal particle-containing powder coating compositions useful in powder coating applications, which process comprises (a) atomizing by spraying a gas which is intermixed with a solution comprising a solvent, a resin which is melt extrudable and which will cure in the presence of a curing agent, a curing agent which will cross-link said resin upon the application of heat, and suspended metal particles to form droplets, and (b) collecting the sprayed droplets in a liquid bath wherein said liquid is miscible with said solvent but said liquid is a non-solvent for the solutes of the solution and wherein said liquid bath is subjected to a radial flow motion whereby said flow motion carries the particles away from one another thereby precipitating said powder coating compositions in substantially non-agglomerated form.

Claim 3

The process of claim 1 wherein the solution of step (a) additionally contains a suspended pigment.

Claim 4

The process of claim 2 wherein the precipitated resin containing entrapped metal particles is further washed, filtered, and dried.

Claim 5

The process of claim 3 wherein said solvent is acetone, said resin is an acrylic, said pigment is phthalocyanine blue pigment, said curing agent is prepared by reacting three moles of 1-isocyanato3-isocyanatomethyl-3,5,5-trimethylcyclohexane with one mole of 1,1,1-tris-(hydroxymethyl) propane in methyl isobutyl ketone followed by blocking with methyl ethyl ketoxime, said metal particles are aluminum flake, and said liquid is water.

Claim 6

A process for preparing uncured curable porous metal particle-containing powder coating compositions useful in powder coating applications, which process comprises (a) atomizing by spraying a gas which is intermixed with a solution comprising from about 25 to about 55% by weight of a solvent, from about 35 to about 75% by weight of a resin which is melt extrudable and which will cure in the presence of a curing agent, from about 2 to about 60% by weight of a curing agent which will cross-link said resin upon the application of heat, and from about 0.5 to about 50% by weight suspended metal particles, to form droplets, and (b) collecting the sprayed droplets in a liquid bath wherein said liquid is miscible with said solvent, but said liquid is a non-solvent for the solutes of the solution and wherein said liquid bath is subjected to a radial flow motion whereby said flow motion carries the particles away from one another thereby precipitating said powder coating compositions in substantially non-agglomerated form, and then (c) washing, (d) filtering, and (e) drying the powder coating compositions.

Claim 7

A process for preparing uncured curable porous metal particle-containing powder coating compositions useful in powder coating applications, which process comprises (a) atomizing by spraying a gas which is intermixed with a solution comprising from about 25 to about 55% by weight of a solvent, from about 35 to about 75% by weight of a resin which is melt extrudable and which will cure in the presence of a curing agent, from about 2 to about 60% by weight of a curing agent which will cross-link said resin upon the application of heat, and from about 0.5 to about 50% by weight suspended metal particles, to form droplets, and (b) collecting the sprayed droplets in a liquid bath wherein said liquid is miscible with said solvent, but said liquid is a non-solvent for the solutes of the solution and wherein said liquid bath is subjected to a radial flow motion whereby said flow motion carries the particles away from one another thereby precipitating said powder coating compositions in substantially non-agglomerated form, and then (c) washing, (d) filtering, and (e) drying the powder coating compositions.

Claim 8

The process of claim 5 wherein said process is carried out at a temperature of from about 0° to about 150° C. and at a substantially atmospheric pressure.

Claim 9

The process of claim 6 wherein the solution of step (a) additionally contains a suspended pigment.

Claim 10

A process for preparing uncured curable porous aluminum flake-containing powder coating compositions useful in powder coating applications, which comprises (a) atomizing by spraying a gas which is intermixed with a solution comprising acetone, an acrylic resin which is melt extrudable and which will cure in the presence of a curing agent, a curing agent prepared by reacting three moles of 1-isocyanato-3-isocyanatomethyl-3,5,5-trimethylcyclohexane with one mole of 1,1,1-tris-(hydroxymethyl) propane in methyl isobutyl ketone followed by blocking with methyl ethyl ketoxime, wherein said curing agent will cross-link said resin upon the application of heat, phthalocyanine blue pigment, and suspended aluminum flakes to form droplets, (b) collecting the sprayed droplets in a water bath wherein said water bath is subjected to a radial flow motion whereby said flow motion carries the particles away from one another thereby precipitating the powder coating compositions in substantially non-agglomerated form, (c) washing the resulting powder coating compositions, (d) filtering, and (e) drying the powder coating compositions.

Claim 11

A process for preparing uncured curable porous aluminum flake-containing powder coating compositions useful in powder coating applications, which comprises (a) atomizing by spraying a gas which is intermixed with a solution comprising acetone, an acrylic resin which is melt extrudable and which will cure in the presence of a curing agent, a curing agent prepared by reacting three moles of 1-isocyanato-3-isocyanatomethyl-3,5,5-trimethylcyclohexane with one mole of 1,1,1-tris-(hydroxymethyl) propane in methyl isobutyl ketone followed by blocking with methyl ethyl ketoxime, wherein said curing agent will cross-link said resin upon the application of heat, phthalocyanine blue pigment, and suspended aluminum flakes to form droplets, (b) collecting the sprayed droplets in a water bath wherein said water bath is subjected to a radial flow motion whereby said flow motion carries the particles away from one another thereby precipitating the powder coating compositions in substantially non-agglomerated form, (c) washing the resulting powder coating compositions, (d) filtering, and (e) drying the powder coating compositions.

Claim 12

The process of claim 8 wherein said powder coating composition comprises from about 30 to about 50% by weight acetone, from about 40 to about 70% by weight acrylic resin, from about 5 to about 40% by weight curing agent, from about 0.2 to about 20% by weight pigment and from about 0.75 to about 0.40% by weight aluminum flake.

Claim 13

The process of claim 9 wherein said powder coating composition comprises from about 35 to about 45% by weight acetone, from about 45 to about 65% by weight acrylic resin, from about 10 to about 35% by weight curing agent, from about 0.4 to about 10% by weight pigment and from about 1 to about 30% by weight aluminum flake.

Claim 14

The process of claim 10 wherein said process is carried out at a temperature of 10° to 100° C. and at substantially atmospheric pressure.

Claim 15

The process of claim 11 wherein said droplets have a diameter of from about 10 to about 200 microns.

Claim 16

The process of claim 8 wherein said powder coating composition has a mean average diameter of from about 20 to about 65 microns.