Cathode ray tube having amorphous resistive film on internal surfaces and method of forming the film
Assignee: Verizon Laboratories Inc
•
Filing: 1975-11-24
•
Granted: 1978-05-30
•
Expires: 1995-11-24
Abstract
Abstract An amorphous, resistive thin film is deposited on internal surfaces of portions of a cathode ray tube by the pyrolysis of a liquid mixture of colloidal graphite and a heavy metal resinate to produce a film which is a mixture of graphite and the oxide of the metal. The metal resinate is a combination of tin and antimony resinate. The film is deposited on the tube neck in the region of the G3 and G4 electrodes to impede arcing. The amorphous film is also deposited on the tube funnel in the region extending from the snubber contact locations up to the anode voltage terminal. The pyrolysis of the heavy metal resinate and colloidal graphite results in a film having a resistance ranging from 10 3 to 10 8 ohms point to point. The amorphous film which does not require a binder, has good adhesion and scratch resistance characteristics, thereby reducing conductive particle contamination.
Inventors
- 👤 Kurt B. Kilichowski
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 17:52
CPC Classifications
H; H01; H01J; H01J9/00; H01J9/20
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
87 words
A method of forming a resistive thin film on an internal portion of a cathode ray tube to reduce arcing comprising the steps of: a. coating the internal portion with a liquid consisting of graphite in a carrier of isopropyl alcohol and effective proportions of a heavy metal resinate selected from the group consisting of antimony and tin resinates and combinations thereof,; and b. heating the coated liquid to produce an amorphous resistive thin film which is a mixture of graphite and oxides of the heavy metal.
Claim 2
Independent Claim
87 words
A method of forming a resistive thin film on an internal portion of a cathode ray tube to reduce arcing comprising the steps of: a. coating the internal portion with a liquid consisting of graphite in a carrier of isopropyl alcohol and effective proportions of a heavy metal resinate selected from the group consisting of antimony and tin resinates and combinations thereof,; and b. heating the coated liquid to produce an amorphous resistive thin film which is a mixture of graphite and oxides of the heavy metal.
Claim 3
Dependent Claim
20 words
The method according to claim 1 wherein the heavy metal resinate is a mixture of tin resinate and antimony resinate.
Claim 4
Dependent Claim
11 words
The method according to claim 1 wherein the resinate is 2-ethylhexanate.
Claim 5
Dependent Claim
39 words
The method according to claim 1 wherein the step of heating includes heating the coated liquid to a temperature and for a time interval in the range of 325° C for 10 hours to 475° C for 0.5 hours.
Claim 6
Dependent Claim
23 words
The method according to claim 4 wherein the coated liquid is heated to about a temperature of 430° C for about 2 hours.
Claim 7
Dependent Claim
19 words
The method according to claim 1 wherein the step of coating includes spraying the liquid onto the internal portion.
Claim 8
Dependent Claim
20 words
The method according to claim 1 wherein the step of coating includes brush coating the liquid onto the internal portion.
Claim 9
Dependent Claim
28 words
The method according to claim 2 wherein the liquid contains concentrations of the resinates effective to produce substantially equal percentages of oxides of tin and antimony by weight.
Claim 10
Independent Claim
92 words
A method of forming a resistive thin film on an internal portion of a cathode ray tube to reduce arcing comprising the steps of: a. spraying the internal portion with a liquid consisting of effective proportions of tin resinate, antimony resinate and graphite in an isopropyl alcohol carrier, and b. heating the sprayed liquid to produce an amorphous resistive thin film which is a mixture of graphite and oxides of tin and antimony, the liquid containing concentrations of the resinates effective to produce substantially equal percentages of tin and antimony be weight.
Claim 11
Independent Claim
92 words
A method of forming a resistive thin film on an internal portion of a cathode ray tube to reduce arcing comprising the steps of: a. spraying the internal portion with a liquid consisting of effective proportions of tin resinate, antimony resinate and graphite in an isopropyl alcohol carrier, and b. heating the sprayed liquid to produce an amorphous resistive thin film which is a mixture of graphite and oxides of tin and antimony, the liquid containing concentrations of the resinates effective to produce substantially equal percentages of tin and antimony be weight.
Claim 12
Dependent Claim
23 words
The method according to claim 9 wherein the sprayed liquid is heated to a temperature of about 430° C for about 2 hours.
References Cited (Backward Citations)
US2836754A
Cited
US2818355A
Cited
US2934736A
Cited
US3355617A
Cited
US3539392A
Cited
US3655440A
Cited
US3791546A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-05-29 | 1981-11-28 | 1982-05-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-05-29 | 1985-11-28 | 1986-05-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-05-29 | 1989-11-28 | 1990-05-30 | $7700.00 | Window Closed / Lapsed |