Methods of fabricating microsponge deuterated hydrocarbon polymer targets which emit neutrons when irradiated by high energy beams
Assignee: University of Rochester
•
Filing: 1976-01-05
•
Granted: 1978-05-30
•
Expires: 1996-01-05
Abstract
Abstract Targets for high energy beams, such as laser beams, produced in laser fusion apparatus are described. The targets are porous spheres of deuterated hydrocarbon material, particularly deuterated polyethylene. The spheres are small and have diameters in the range of 50 to 300 microns. Higher neutron yields are obtained from these targets than from solid targets of similar materials, (viz, spherical targets of much higher density). Methods of fabricating the targets by forming them into solid spheres, cross linking their molecules and causing them to swell such that the resultant targets have a microscopically small sponge-like structure, are also described.
Inventors
- 👤 Gerald M. Halpern
- 👤 Hyogun Kim
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 20:55
CPC Classifications
G; G21; G21B; G21B1/00; G21B1/11; G21B1/19; C; C08; C08J; C08J3/00; C08J3/12; C08J3/122; C08J9/00; C08J9/26; C08J2201/00; C08J2201/04; C08J2201/046; C08J2201/0462; C08J2323/00; C08J2323/02; C08J2323/04; C08J2323/06; Y; Y02; Y02E; Y02E30/00; Y02E30/10; Y10; Y10S; Y10S264/00; Y10S264/13; Y10S376/00; Y10S376/915; Y10S376/916
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
139 words
A method for the fabrication of elements, for use as targets for a high energy beam, and which provide neutrons by interaction with said beam, said method comprising the steps of (a) forming deuterated hydrocarbon polymer material into solid bodies which are of sizes which are less than about 300 microns diametrically, (b) cross-linking the molecules of the material with radiation, and (c) increasing the size of said cross linked bodies while reducing the mass thereof with the aid of a fluid which is a solvent for the un-cross-linked portions of the material and a swelling agent for the cross-linked portions thereof which causes said bodies to partially dissolve and to swell, thereby providing said bodies with a micro-sponge structure of cells of a size which does not exceed about 1 micron, said microsponge structure bodies providing said elements.
Claim 2
Independent Claim
139 words
A method for the fabrication of elements, for use as targets for a high energy beam, and which provide neutrons by interaction with said beam, said method comprising the steps of (a) forming deuterated hydrocarbon polymer material into solid bodies which are of sizes which are less than about 300 microns diametrically, (b) cross-linking the molecules of the material with radiation, and (c) increasing the size of said cross linked bodies while reducing the mass thereof with the aid of a fluid which is a solvent for the un-cross-linked portions of the material and a swelling agent for the cross-linked portions thereof which causes said bodies to partially dissolve and to swell, thereby providing said bodies with a micro-sponge structure of cells of a size which does not exceed about 1 micron, said microsponge structure bodies providing said elements.
Claim 3
Dependent Claim
30 words
The invention as set forth in claim 1 wherein said beam is a beam of laser radiation, and laser fusion reactions with said targets are the source of said neutrons.
Claim 4
Dependent Claim
20 words
The invention as set forth in claim 1 wherein said material of said body is a deuterated ethylenic hydrocarbon polymer.
Claim 5
Dependent Claim
14 words
The invention as set forth in claim 3 wherein said polymer is deuterated polyethylene.
Claim 6
Dependent Claim
28 words
The invention as set forth in claim 4 wherein said polyethylene has a low molecular weight characterized by a melt index of from about 10 to about 15.
Claim 7
Dependent Claim
21 words
The invention as set forth in claim 3 wherein said forming step is carried out by forming said material into spheroids.
Claim 8
Dependent Claim
50 words
The invention as set forth in claim 6 wherein said forming step is carried out by pulverizing said material into powder, and thereafter agitating and melting the individual particles of the powder, and cooling said melted powder particles while continuing to agitate them thereby forming them into hard, dense spheres.
Claim 9
Dependent Claim
79 words
The invention as set forth in claim 7 wherein said material is polyethylene having a melt index of from about 10 to 15 and said agitating and melting steps are carried out by heating said powder particles in a vessel containing silicone oil having a temperature of about 150° C for about 10 minutes while agitating the container sufficiently to prevent agglomeration of the particles, and said cooling step is carried out by quenching the container in wet ice.
Claim 10
Dependent Claim
33 words
The invention as set forth in claim 8 wherein said forming step includes the further steps of filtering said particles from said oil, and washing said filtered particles to remove residual oil therefrom.
Claim 11
Dependent Claim
26 words
The invention as set forth in claim 1 wherein said crosslinking is carried out with the aid of gamma radiation to which said bodies are exposed.
Claim 12
Dependent Claim
16 words
The invention as set forth in claim 10 wherein said material is an ethylenic hydrocarbon polymer.
Claim 13
Dependent Claim
53 words
The invention as set forth in claim 11 wherein the dosage of said radiation to which said polymer is exposed is within the range of dosage greater than that which results in complete dissolution of said bodies by said solvent, and is less than that which results in negligible swelling of said bodies.
Claim 14
Dependent Claim
17 words
The invention as set forth in claim 12 wherein said range is from 10 to 40 MRads.
Claim 15
Dependent Claim
13 words
The invention as set forth in claim 13 wherein said polymer is polyethylene.
Claim 16
Dependent Claim
62 words
The invention as set forth in claim 1 wherein said fluid is a solvent for the un-cross-linked portions of said material and a swelling agent for the cross-linked portions thereof, and said size increasing step is carried out by emersing said cross-linked bodies in a bath of said solvent until they increase in size about 1 and 11/2 to twice in size.
Claim 17
Dependent Claim
20 words
The invention as set forth in claim 15 wherein after said immersing step, said solvent is removed from said bodies.
Claim 18
Dependent Claim
34 words
The invention as set forth in claim 16 wherein said bath is heated, and wherein after said bodies have reached their increased size, said bath is cooled below the crystallization temperature of said material.
Claim 19
Dependent Claim
37 words
The invention as set forth in claim 16 wherein said material is polyethylene, said bodies are formed into spherical shape and said solvent heated to a temperature in the range of from about 100° to 110° C.
Claim 20
Dependent Claim
24 words
The invention as set forth in claim 17 wherein said cooling step is carried out by quenching the container for said bath in ice.
Claim 21
Dependent Claim
20 words
The invention as set forth in claim 18 wherein said immersing step is carried out for at least 1 hour.
Claim 22
Dependent Claim
13 words
The invention as set forth in claim 19 wherein said solvent is para-xylene.
References Cited (Backward Citations)
US2948664A
Cited
US3263980A
Cited
US3452123A
Cited
US3341480A
Cited
US3505434A
Cited
US3558532A
Cited
US3640915A
Cited
US3586654A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-05-29 | 1981-11-28 | 1982-05-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-05-29 | 1985-11-28 | 1986-05-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-05-29 | 1989-11-28 | 1990-05-30 | $7700.00 | Window Closed / Lapsed |