Double exposure and double etch technique for producing precision parts from crystallizable photosensitive glass
Assignee: International Business Machines Corp
•
Filing: 1976-12-27
•
Granted: 1978-05-30
•
Expires: 1996-12-27
Abstract
Abstract A double exposure and double etch technique for producing precision parts from a photosensitive material is described. The process is described in terms of producing an array of ink jet charge electrodes which comprise a series of small through holes on accurately defined centers. The process comprises the steps of exposing the photosensitive material through a mask to develop an undersized through hole and heat treating the photosensitive material to change its characteristics so that an etchable material is produced in the exposed area. The material is then etched to form the undersized through hole which is substantially tapered. The material is then exposed again with a full sized mask including any conductor patterns and the material is again heat treated. The material is again etched and this etching, in the nature of a surface etch, reduces the taper because of the lower etch rate of the unexposed material as compared to the much higher etch rate of the previously unetched tapered material.
Inventors
- 👤 Carlton Edward Olsen
- 👤 Leroy Jasper Serpa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 18:03
CPC Classifications
G; G03; G03F; G03F7/00; G03F7/20; G03F7/2022; B; B41; B41J; B41J2/00; B41J2/005; B41J2/01; B41J2/07; B41J2/075; B41J2/08; B41J2/085; G03F7/004; G03F7/0042
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
65 words
A process for precision etching a photosensitive glass material comprising the steps of: exposing a selectively crystallizable photosensitive glass substrate through a first mask to a source of radiation to which said photosensitive glass is sensitive; heat treating said substrate by heating to a temperature sufficient to produce a crystalline phase within the part of the substrate exposed through said first mask to said radiation;
Claim 2
Dependent Claim
65 words
A process for precision etching a photosensitive glass material comprising the steps of: exposing a selectively crystallizable photosensitive glass substrate through a first mask to a source of radiation to which said photosensitive glass is sensitive; heat treating said substrate by heating to a temperature sufficient to produce a crystalline phase within the part of the substrate exposed through said first mask to said radiation;
Claim 3
Dependent Claim
131 words
treating the substrate with an etchant to remove the crystalline phase part of said substrate, said treating step producing a taper at the boundary of the crystalline phrase material and the unexposed part of said substrate; exposing the substrate through a second mask to a source of radiation to which said substrate is sensitive; said second mask having an incrementally larger opening than corresponding openings in said first mask; heat treating said substrate by heating to a temperature at which the substrate produces a crystalline phase in the area exposed to said radiation; and treating the substrate with an etchant to remove the crystalline phase material to produce a precision etched part having an etched pattern with substantially reduced taper as compared to the taper resulting from said first treating step.
Claim 4
Dependent Claim
131 words
treating the substrate with an etchant to remove the crystalline phase part of said substrate, said treating step producing a taper at the boundary of the crystalline phrase material and the unexposed part of said substrate; exposing the substrate through a second mask to a source of radiation to which said substrate is sensitive; said second mask having an incrementally larger opening than corresponding openings in said first mask; heat treating said substrate by heating to a temperature at which the substrate produces a crystalline phase in the area exposed to said radiation; and treating the substrate with an etchant to remove the crystalline phase material to produce a precision etched part having an etched pattern with substantially reduced taper as compared to the taper resulting from said first treating step.
Claim 5
Dependent Claim
20 words
The process according to claim 1 in which the exposure step utilizes a source of radiation comprising a mercury/xenon lamp.
Claim 6
Dependent Claim
26 words
The process according to claim 2 wherein said heat treating step comprises heating said substrate to a temperature of about 592° C for about 30 minutes.
Claim 7
Dependent Claim
196 words
A process for precision etching a photosensitive glass material comprising the steps of: exposing a selectively crystallizable photosensitive glass substrate through a first mask to a source of radiation to which said photosensitive glass is sensitive; heat treating said substrate by heating to a temperature sufficient to produce a crystalline phase within the part of the substrate exposed through said first mask to said radiation; exposing the substrate through a second mask to a source of radiation to which said substrate is sensitive; said second mask having an incrementally larger opening than corresponding openings in said first mask; treating the substrate with an etchant to remove the crystalline phase part of said substrate, said treating step producing a taper at the boundary of the crystalline phrase material and the unexposed part of said substrate; heat treating said substrate by heating to a temperature at which the substrate produces a crystalline phase in the area exposed to said radiation; and treating the substrate with an etchant to remove the crystalline phase material to produce a precision etched part having an etched pattern with substantially reduced taper as compared to the taper resulting from said first treating step.
Claim 8
Dependent Claim
196 words
A process for precision etching a photosensitive glass material comprising the steps of: exposing a selectively crystallizable photosensitive glass substrate through a first mask to a source of radiation to which said photosensitive glass is sensitive; heat treating said substrate by heating to a temperature sufficient to produce a crystalline phase within the part of the substrate exposed through said first mask to said radiation; exposing the substrate through a second mask to a source of radiation to which said substrate is sensitive; said second mask having an incrementally larger opening than corresponding openings in said first mask; treating the substrate with an etchant to remove the crystalline phase part of said substrate, said treating step producing a taper at the boundary of the crystalline phrase material and the unexposed part of said substrate; heat treating said substrate by heating to a temperature at which the substrate produces a crystalline phase in the area exposed to said radiation; and treating the substrate with an etchant to remove the crystalline phase material to produce a precision etched part having an etched pattern with substantially reduced taper as compared to the taper resulting from said first treating step.
Claim 9
Dependent Claim
20 words
The process according to claim 4 in which the exposure step utilizes a source of radiation comprising a mercury/xenon lamp.
Claim 10
Dependent Claim
26 words
The process according to claim 5 wherein said heat treating step comprises heating said substrate to a temperature of about 592° C for about 30 minutes.
Claim 11
Dependent Claim
224 words
A process for precision etching from a photosensitive glass material an ink jet charge electrode substrate having a plurality of small openings therein comprising the steps of: exposing a selectively crystallizable photosensitive glass substrate through a first mask defining a plurality of undersize openings to a source of radiation to which said photosensitive glass is sensitive; heat treating said substrate by heating to a temperature sufficient to produce a crystalline phase within the part of the substrate exposed through said first mask to said radiation; treating the substrate with an etchant to remove the crystalline phase part of said substrate, said treating step producing a taper at the boundary of the crystalline phrase material and the unexposed part of said substrate; exposing the substrate through a second mask defining a plurality of full-size openings and a plurality of conductor paths to a source of radiation to which said substrate is sensitive; heat treating said substrate by heating to a temperature at which the substrate produces a crystalline phase in the area exposed to said radiation; and treating the substrate with an etchant to remove the crystalline phase material to produce a precision etched part having an etched pattern comprising a plurality of conductor slots and a plurality of openings with substantially reduced taper as compared to the taper resulting from said first treating step.
Claim 12
Dependent Claim
224 words
A process for precision etching from a photosensitive glass material an ink jet charge electrode substrate having a plurality of small openings therein comprising the steps of: exposing a selectively crystallizable photosensitive glass substrate through a first mask defining a plurality of undersize openings to a source of radiation to which said photosensitive glass is sensitive; heat treating said substrate by heating to a temperature sufficient to produce a crystalline phase within the part of the substrate exposed through said first mask to said radiation; treating the substrate with an etchant to remove the crystalline phase part of said substrate, said treating step producing a taper at the boundary of the crystalline phrase material and the unexposed part of said substrate; exposing the substrate through a second mask defining a plurality of full-size openings and a plurality of conductor paths to a source of radiation to which said substrate is sensitive; heat treating said substrate by heating to a temperature at which the substrate produces a crystalline phase in the area exposed to said radiation; and treating the substrate with an etchant to remove the crystalline phase material to produce a precision etched part having an etched pattern comprising a plurality of conductor slots and a plurality of openings with substantially reduced taper as compared to the taper resulting from said first treating step.
Claim 13
Dependent Claim
20 words
The process according to claim 7 in which the exposure step utilizes a source of radiation comprising a mercury/xenon lamp.
Claim 14
Dependent Claim
26 words
The process according to claim 8 wherein said heat treating step comprises heating said substrate to a temperature of about 592° C for about 30 minutes.
Claim 15
Dependent Claim
224 words
A process for precision etching from a photosensitive glass material an ink jet charge electrode substrate having a plurality of small openings therein comprising the steps of: exposing a selectively crystallizable photosensitive glass substrate through a first mask defining a plurality of undersize openings to a source of radiation to which said photosensitive glass is sensitive; heat treating said substrate by heating to a temperature sufficient to produce a crystalline phase within the part of the substrate exposed through said first mask to said radiation; exposing the substrate through a second mask defining a plurality of full-size openings and a plurality of conductor slots to a source of radiation to which said substrate is sensitive; treating the substrate with an etchant to remove the crystalline phase part of said substrate, said treating step producing a taper at the boundary of the crystalline phrase material and the unexposed part of said substrate; heat treating said substrate by heating to a temperature at which the substrate produces a crystalline phase in the area exposed to said radiation; and treating the substrate with an etchant to remove the crystalline phase material to produce a precision etched part having an etched pattern comprising a plurality of conductor slots and a plurality of openings with substantially reduced taper as compared to the taper resulting from said first treating step.
Claim 16
Dependent Claim
224 words
A process for precision etching from a photosensitive glass material an ink jet charge electrode substrate having a plurality of small openings therein comprising the steps of: exposing a selectively crystallizable photosensitive glass substrate through a first mask defining a plurality of undersize openings to a source of radiation to which said photosensitive glass is sensitive; heat treating said substrate by heating to a temperature sufficient to produce a crystalline phase within the part of the substrate exposed through said first mask to said radiation; exposing the substrate through a second mask defining a plurality of full-size openings and a plurality of conductor slots to a source of radiation to which said substrate is sensitive; treating the substrate with an etchant to remove the crystalline phase part of said substrate, said treating step producing a taper at the boundary of the crystalline phrase material and the unexposed part of said substrate; heat treating said substrate by heating to a temperature at which the substrate produces a crystalline phase in the area exposed to said radiation; and treating the substrate with an etchant to remove the crystalline phase material to produce a precision etched part having an etched pattern comprising a plurality of conductor slots and a plurality of openings with substantially reduced taper as compared to the taper resulting from said first treating step.
Claim 17
Dependent Claim
20 words
The process according to claim 10 in which the exposure step utilizes a source of radiation comprising a mercury/xenon lamp.
Claim 18
Dependent Claim
26 words
The process according to claim 11 wherein said heat treating step comprises heating said substrate to a temperature of about 592° C for about 30 minutes.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-05-29 | 1981-11-28 | 1982-05-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-05-29 | 1985-11-28 | 1986-05-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-05-29 | 1989-11-28 | 1990-05-30 | $7700.00 | Window Closed / Lapsed |