Ductile tungsten-nickel-alloy and method for manufacturing same
Assignee: United States Department of Energy
•
Filing: 1973-10-01
•
Granted: 1978-05-23
•
Expires: 1993-10-01
Abstract
Abstract The tensile elongation of a tungsten-nickel-iron alloy containing essentially 95 weight percent reprocessed tungsten, 3.5 weight percent nickel, and 1.5 weight percent iron is increased from a value of less than about 1 percent up to about 23 percent by the addition of less than 0.5 weight percent of a reactive metal consisting of niobium and zirconium.
Inventors
- 👤 Robert L. Ludwig
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 15:09
CPC Classifications
C; C22; C22C; C22C27/00; C22C27/04
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
79 words
A tungsten-base alloy consisting of about 95 weight percent reprocessed tungsten having an oxygen content in the range of about 500 to 2000 ppm, 3.5 weight percent nickel, 1.5 weight percent iron, and a metal selected from the group consisting of niobium and zirconium in a concentration of about 0.05 to 0.5 weight percent for increasing the tensile elongation of the alloy by a factor of at least about 9 over that obtainable without the addition of said metal.
Claim 2
Dependent Claim
79 words
A tungsten-base alloy consisting of about 95 weight percent reprocessed tungsten having an oxygen content in the range of about 500 to 2000 ppm, 3.5 weight percent nickel, 1.5 weight percent iron, and a metal selected from the group consisting of niobium and zirconium in a concentration of about 0.05 to 0.5 weight percent for increasing the tensile elongation of the alloy by a factor of at least about 9 over that obtainable without the addition of said metal.
Claim 3
Independent Claim
174 words
The method of manufacturing a tungsten-nickel-iron alloy which includes the steps of preparing a mixture consisting of about 95 weight percent tungsten powder characterized by being reprocessed and containing an oxygen concentration in the range of about 500 to 2000 ppm, 3.5 weight percent nickel powder, 1.5 weight percent iron powder, mixing said powder mixture with a metal powder selected from the group consisting of niobium and zirconium with said metal powder being in an amount in the range of 0.05 to 0.5 weight percent for increasing the tensile elongation of the alloy over that obtainable without the addition of said metal powder, isostatically pressing the resulting mixture at a pressure in the range of 10 to 15 tons per square inch, heating the pressed mixture in a hydrogen atmosphere to a temperature in the range of 1440° to 1470° C. for a duration adequate to sinter the mixture, and thereafter annealing the resulting sintered compact in vacuum at a temperature in the range of 700° to 1300° C. for 2 to 50 hours.
Claim 4
Independent Claim
174 words
The method of manufacturing a tungsten-nickel-iron alloy which includes the steps of preparing a mixture consisting of about 95 weight percent tungsten powder characterized by being reprocessed and containing an oxygen concentration in the range of about 500 to 2000 ppm, 3.5 weight percent nickel powder, 1.5 weight percent iron powder, mixing said powder mixture with a metal powder selected from the group consisting of niobium and zirconium with said metal powder being in an amount in the range of 0.05 to 0.5 weight percent for increasing the tensile elongation of the alloy over that obtainable without the addition of said metal powder, isostatically pressing the resulting mixture at a pressure in the range of 10 to 15 tons per square inch, heating the pressed mixture in a hydrogen atmosphere to a temperature in the range of 1440° to 1470° C. for a duration adequate to sinter the mixture, and thereafter annealing the resulting sintered compact in vacuum at a temperature in the range of 700° to 1300° C. for 2 to 50 hours.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-05-22 | 1981-11-21 | 1982-05-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-05-22 | 1985-11-21 | 1986-05-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-05-22 | 1989-11-21 | 1990-05-23 | $7700.00 | Window Closed / Lapsed |