Method for controlling the shape of a molten pool in gas shield arc welding
Assignee: National Institute for Materials Science
•
Filing: 1976-09-17
•
Granted: 1978-05-16
•
Expires: 1996-09-17
Abstract
Abstract A method is disclosed in which gas shield arc welding is carried out while applying a gas at a higher pressure than the shield gas to the rear part of the surface of molten metal during welding. By this method, welding proceeds while the molten pool is being maintained in the desirable shape, and the welding can be performed at high currents and speeds without causing bead defects such as undercut formation or humping.
Inventors
- 👤 Akira Okada
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 22:56
CPC Classifications
B; B23; B23K; B23K9/00; B23K9/16; B23K9/167
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
227 words
In a method of gas shield arc welding a metal workpiece with a gas shield arc welding torch which includes a shield gas nozzle surrounding a metal electrode wherein welding is performed while a shield gas flows from the shield gas nozzle and surrounds the arc generated between the electrode and the metal workpiece, said arc locally melting and gouging the metal workpiece, whereby a molten pool of molten metal gathers in said gouging, the improvement comprising, providing a control gas nozzle in parallel with the axis of said electrode in the space between said electrode and the inner wall of said shield gas nozzle, said control gas nozzle being located in said space at a position which is rearward of said electrode with regard to the welding direction, said control gas nozzle having a tip whose gas flow outlet opens toward the molten pool during welding; and performing gas shield arc welding while applying a control gas stream, through said control gas nozzle, at a pressure higher than the pressure of said shield gas, to the surface of said molten pool rearward of the position at which the molten pool attains its maximum width, thereby pressurizing and cooling the molten metal in said molten pool and deflecting the arc in the welding direction. whereby the shape of the molten pool is controlled to prevent bead defects.
Claim 2
Dependent Claim
227 words
In a method of gas shield arc welding a metal workpiece with a gas shield arc welding torch which includes a shield gas nozzle surrounding a metal electrode wherein welding is performed while a shield gas flows from the shield gas nozzle and surrounds the arc generated between the electrode and the metal workpiece, said arc locally melting and gouging the metal workpiece, whereby a molten pool of molten metal gathers in said gouging, the improvement comprising, providing a control gas nozzle in parallel with the axis of said electrode in the space between said electrode and the inner wall of said shield gas nozzle, said control gas nozzle being located in said space at a position which is rearward of said electrode with regard to the welding direction, said control gas nozzle having a tip whose gas flow outlet opens toward the molten pool during welding; and performing gas shield arc welding while applying a control gas stream, through said control gas nozzle, at a pressure higher than the pressure of said shield gas, to the surface of said molten pool rearward of the position at which the molten pool attains its maximum width, thereby pressurizing and cooling the molten metal in said molten pool and deflecting the arc in the welding direction. whereby the shape of the molten pool is controlled to prevent bead defects.
Claim 3
Dependent Claim
16 words
The method of claim 1 wherein said metal electrode is nonconsumable and has a wedge-shaped tip.
Claim 4
Dependent Claim
20 words
The method of claim 1 wherein the control gas stream is applied intermittently to the surface of said molten metal.
Claim 5
Dependent Claim
25 words
The method according to claim 3 wherein the period of changing the flow rate of said control gas stream is about 10 to 50 Hz.
Claim 6
Dependent Claim
22 words
The method of claim 1 wherein the inside diameter of said control gas nozzle is from about 1 to about 4 mm.
Claim 7
Dependent Claim
43 words
The method according to claim 5 wherein said control gas stream flows at a flow rate sufficient to provide a dynamic pressure on the rear part of said molten metal in the range of about 100 mm Aq to about 300 mm Aq.
Claim 8
Dependent Claim
21 words
The process according to claim 6 wherein said dynamic pressure is from about 40 mm Aq to about 100 mm Aq.
Claim 9
Dependent Claim
30 words
The method according to claim 1 wherein welding is performed at a welding current of DC 100 A to 500 A and at welding speeds of at least 10 cm/min.
Claim 10
Dependent Claim
29 words
The method according to claim 1 wherein welding is performed at a current of at least DC 200 A and at a welding speed of at least 60 cm/min.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-05-15 | 1981-11-14 | 1982-05-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-05-15 | 1985-11-14 | 1986-05-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-05-15 | 1989-11-14 | 1990-05-16 | $7700.00 | Window Closed / Lapsed |