Process for the production of spherical silica gel

Claim 2

A process for the production of spherical silica gel which comprises emulsifying water glass in a dispersion medium composed of a mixture of, by volume, 20-60% n-hexanol as polar solvent and 40-80% liquid paraffin as non-polar solvent, said water glass being present in an amount of 0.01-20 parts by weight per 100 parts by weight of said dispersion medium, based on its silica content, to form a spherical silica sol; and thereafter gelling said sol while maintaining it in an emulsified state.

Claim 3

A process according to claim 1 wherein said water glass is a concentrated aqueous solution of a glass of alkali-silicic acid series containing about 1-50% by weight of silica.

Claim 4

A process according to claim 1 wherein said sperhical silica gel is separated from said dispersion medium and thereafter moisture contained in the said spherical silica gel is removed by evaporation to make the said spherical silica gel porous.

Claim 5

A process according to claim 1 wherein said spherical silica gel is made porous by heating it at a temperature of 500°-800° C.

Claim 6

In the process for the production of spherical silica gel by emulsifying water glass in a dispersion medium composed of a mixture of polar and non-polar solvents to form a spherical silica sol and thereafter gelling said sol while maintaining it in an emulsified state, the improvement which comprises employing as the dispersion medium a mixture of, by volume, 20-60% n-hexanol as polar solvent and 40-80% liquid paraffin as non-polar solvent, said water glass being present in an amount of 0.01-20 parts by weight per 100 parts by weight of said dispersion medium, based on its silica content; adding to the dispersion medium a foaming agent selected from the group consisting of methane, ethanol, acetone and methyl ethyl ketone and subsequently removing said forming agent from the produced sperhical silica gel by evaporation, so as to obtain a porous spherical silica gel.

Claim 7

In the process for the production of spherical silica gel by emulsifying water glass in a dispersion medium composed of a mixture of polar and non-polar solvents to form a spherical silica sol and thereafter gelling said sol while maintaining it in an emulsified state, the improvement which comprises employing as the dispersion medium a mixture of, by volume, 20-60% n-hexanol as polar solvent and 40-80% liquid paraffin as non-polar solvent, said water glass being present in an amount of 0.01-20 parts by weight per 100 parts by weight of said dispersion medium, based on its silica content; adding to the dispersion medium a foaming agent selected from the group consisting of methane, ethanol, acetone and methyl ethyl ketone and subsequently removing said forming agent from the produced sperhical silica gel by evaporation, so as to obtain a porous spherical silica gel.

Claim 8

A process according to claim 5 wherein said spherical silica gel is made porous by a lyophilizing treatment.

Claim 9

A process according to claim 5 wherein said water glass is a concentrated aqueous solution of a glass of alkali-silicic acid series containing about 1-50% by weight of silica.

Claim 10

A process according to claim 5 wherein said foaming agent is a polar solvent with 1-4 carbon atoms.

Claim 11

A process according to claim 5 wherein said foaming agent is methanol or ethanol.

Claim 12

A process according to claim 5 wherein said foaming agent is acetone or methyl ethyl ketone.