Process for the production of nickel clad steel coinage blank
Assignee: Viridian Inc Canada
•
Filing: 1976-11-18
•
Granted: 1978-05-16
•
Expires: 1996-11-18
Abstract
Abstract A process for the production of coin blanks suitable for minting into coins includes providing metallic core pieces, each core piece having opposed, substantially planar faces and a common side edge. The core pieces are loaded into a perforated container which is placed in an electroplating bath. A metallic cladding is placed on the core pieces, while moving the container angularly about a horizontal axis, until the metallic cladding has a thickness of at least about 0.05 mm on each face of each core piece and a thickness of at least 2 to 4 times the face thickness on the side edge of each core.
Inventors
- 👤 Arthur G. McMullen
- 👤 Michael J. H. Ruscoe
- 👤 Maurice A. Clegg
- 👤 Ronald L. Prowse
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 21:20
CPC Classifications
B; B32; B32B; B32B15/00; B32B15/01; B32B15/013; B32B15/015
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
151 words
A process for the production of coin blanks suitable for minting into coins, including providing metallic core pieces, each core piece having opposed, substantially planar faces and a common side edge, loading said core pieces into a perforated container, placing the container in an electroplating bath, electroplating a metallic cladding on the core pieces, while moving the container angularly about a horizontal axis, until the metallic cladding has a thickness of at least about 0.05 mm on each face of each core piece and a thickness of at least 2 to 4 times the face thickness on the side edge of each core piece, removing the cladded core piece from the container, and heating the cladded core pieces to produce a metallurgical bond between the metallic cladding and core piece of each cladded core piece and to decrease their hardness to less than about 65 on the Rockwell 30T hardness scale.
Claim 2
Dependent Claim
151 words
A process for the production of coin blanks suitable for minting into coins, including providing metallic core pieces, each core piece having opposed, substantially planar faces and a common side edge, loading said core pieces into a perforated container, placing the container in an electroplating bath, electroplating a metallic cladding on the core pieces, while moving the container angularly about a horizontal axis, until the metallic cladding has a thickness of at least about 0.05 mm on each face of each core piece and a thickness of at least 2 to 4 times the face thickness on the side edge of each core piece, removing the cladded core piece from the container, and heating the cladded core pieces to produce a metallurgical bond between the metallic cladding and core piece of each cladded core piece and to decrease their hardness to less than about 65 on the Rockwell 30T hardness scale.
Claim 3
Dependent Claim
26 words
A process according to claim 1 including producing raised rims around the faces of the core pieces before loading the core pieces into the perforated container.
Claim 4
Dependent Claim
15 words
A process according to claim 1 wherein the core pieces are of low carbon steel.
Claim 5
Dependent Claim
14 words
A process according to claim 1 wherein the metallic cladding is a nickel cladding.
Claim 6
Dependent Claim
23 words
A process according to claim 1 wherein the metallic cladding is a nickel cladding and the core pieces are of low carbon steel.
Claim 7
Dependent Claim
168 words
A process for the production of coin blanks suitable for minting into coins, including providing core pieces of low carbon steel, each core piece having opposed, substantially planar faces and a common side edge, each core piece also having raised rims around the faces, loading said core pieces into a perforated container, placing the container in a nickel electroplating bath, electroplating a nickel cladding on the core pieces while moving the container angularly about a horizontal axis, until the nickel cladding has a thickness of at least about 0.05 mm on each face of each core piece and a thickness of at least 2 to 4 times the face thickness on the side edge of each core piece, removing the nickel cladded core pieces from the container, and heating the nickel cladded core pieces to produce a metallurgical bond between the nickel cladding and core piece of each nickel cladded core piece and to decrease their hardness to less than about 65 on the Rockwell 30T hardness scale.
Claim 8
Dependent Claim
168 words
A process for the production of coin blanks suitable for minting into coins, including providing core pieces of low carbon steel, each core piece having opposed, substantially planar faces and a common side edge, each core piece also having raised rims around the faces, loading said core pieces into a perforated container, placing the container in a nickel electroplating bath, electroplating a nickel cladding on the core pieces while moving the container angularly about a horizontal axis, until the nickel cladding has a thickness of at least about 0.05 mm on each face of each core piece and a thickness of at least 2 to 4 times the face thickness on the side edge of each core piece, removing the nickel cladded core pieces from the container, and heating the nickel cladded core pieces to produce a metallurgical bond between the nickel cladding and core piece of each nickel cladded core piece and to decrease their hardness to less than about 65 on the Rockwell 30T hardness scale.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-05-15 | 1981-11-14 | 1982-05-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-05-15 | 1985-11-14 | 1986-05-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-05-15 | 1989-11-14 | 1990-05-16 | $7700.00 | Window Closed / Lapsed |