Abstract
Abstract A process for purifying a hydrogen sulfide containing gas, which comprises absorbing said hydrogen sulfide onto a mass comprising zinc oxide, alumina and a group II A metal oxide, a large proportion of the group II A metal oxide being in the form of aluminate or silicoaluminate; then regenerating the mass by passing an oxygen containing gas therethrough.
Inventors
- 👤 Philippe Courty
- 👤 Andre Deschamps
- 👤 Sigismond Franckowiak
- 👤 Andre Sugier
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 19:14
CPC Classifications
B; B01; B01D; B01D53/00; B01D53/34; B01D53/46; B01D53/48; B01D53/52; C; C01; C01B; C01B3/00; C01B3/50; C01B3/56; C01B2203/00; C01B2203/04; C01B2203/042; C01B2203/0465; C01B2203/0485
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
150 words
A process for purifying a hydrogen sulfide containing gas, characterized in that said gas is passed in contact with an adsorption material comprising a shaped, substantially homogeneous intimate mixture providing by weight, 20-85% of zinc oxide, 0.9-50% of alumina, 0-30% of silica, and 2-45% of group IIA metal oxide, said mixture having been roasted at 500°-1000° C. for a stability increasing time so that at least 50% of said group IIA metal oxide is combined with alumina as metal IIA aluminate or silico-aluminate, and the major portion of said zinc oxide is uncombined with the other components of the absorption material, to absorb hydrogen sulfide, then the contact of the gas with the material is interrupted and an oxygen containing gas is passed in contact with the material for regeneration thereof, the passage is interrupted and a hydrogen sulfide containing gas is passed again in contact with the regenerated material.
Claim 2
Dependent Claim
150 words
A process for purifying a hydrogen sulfide containing gas, characterized in that said gas is passed in contact with an adsorption material comprising a shaped, substantially homogeneous intimate mixture providing by weight, 20-85% of zinc oxide, 0.9-50% of alumina, 0-30% of silica, and 2-45% of group IIA metal oxide, said mixture having been roasted at 500°-1000° C. for a stability increasing time so that at least 50% of said group IIA metal oxide is combined with alumina as metal IIA aluminate or silico-aluminate, and the major portion of said zinc oxide is uncombined with the other components of the absorption material, to absorb hydrogen sulfide, then the contact of the gas with the material is interrupted and an oxygen containing gas is passed in contact with the material for regeneration thereof, the passage is interrupted and a hydrogen sulfide containing gas is passed again in contact with the regenerated material.
Claim 3
Dependent Claim
16 words
A process according to claim 1, wherein the zinc oxide content is 25 - 80% b.w.
Claim 4
Dependent Claim
44 words
A process according to claim 1, wherein the absorption material also contains 0.1 - 10% b.w. as oxide, of at least one oxide of at least one metal M which is copper, cadmium, titanium, zirconium, vanadium, chromium, molybdenum, tungsten, manganese, iron, cobalt or nickel.
Claim 5
Dependent Claim
65 words
A process according to claim 1, wherein the material consists essentially of, by weight, 25 - 80% zinc oxide, 9 - 50% aluminum oxide, 0.02 - 6% silica and 3.5 - 26% of a group II A metal oxide, the molar ratio of the group II A metal oxide to both the aluminum and silicon oxides being from 0.3 : 1 to 2 : 1.
Claim 6
Dependent Claim
35 words
A process according to claim 4, wherein the material also contains 0.1 - 10% b.w. of metal M oxide, and M is copper, cadmium, titanium, zirconium, vanadium, chromium, molybdenum, tungsten, manganese, iron, cobalt or nickel.
Claim 7
Dependent Claim
69 words
A process according to claim 1, wherein the material consists essentially of: ZnO: 25 - 80% CaO 3 - 30% Al 2 O 3 : 2 - 24% oxides of metals M: 0.01 - 10% SiO 2 : 5 - 30% Al 2 O 3 + SiO 2 + CaO = 15 - 60% M is copper, cadmium, titanium, zirconium, vanadium, chromium, molybdenum, tungsten, manganese, iron, cobalt or nickel.
Claim 8
Dependent Claim
77 words
A process according to claim 1, wherein the material is in the form of grains of 3 - 8 mm diameter, its filling density in an industrial reactor is 0.8 - 1.4 metric ton/m3, its crushing strength, is higher than 1 kg/mm, its porosity, as determined by mercury porosimetry, is 15 - 50 ml/kg, its average pore diameter is 1000 - 10,000 A and its specific surface ranges from 1 to 60 m 2 g -1 .
Claim 9
Dependent Claim
39 words
A process according to any of claims 1, wherein the gas containing hydrogen sulfide is contacted with the material at 300° - 650° C and the gas containing oxygen is contacted with the material at 450° - 900° C.
Claim 10
Dependent Claim
21 words
A process according to any of claims 1, wherein the gas containing hydrogen sulfide also contains carbon sulfide and carbon oxysulfide.
Claim 11
Dependent Claim
27 words
A process according to any of claims 1, wherein the gas containing hydrogen sulfide is an effluent from a unit for gasifying solid, liquid or gaseous combustibles.
Claim 12
Dependent Claim
65 words
A process according to any of claims 1, wherein the gas to be treated contains sulfur compounds and at least 10% by mole of hydrogen and/or carbon monoxide, the gas discharged from the absorption step for the sulfur compounds is admixed with the gas discharged from the regeneration step, passed to a catalyst for SO 2 reduction and treated in a plant for sulfur production.
Claim 13
Dependent Claim
90 words
Contact material to carry out hhe process of claim 1, comprising a shaped, substantially homogeneous intimate mixture providing by weight, 20-85% zinc oxide, 0.9-50% of alumina, 0-30% of silica, and 2-45% of a group IIA metal oxide, said mixture having been roasted at 500°-1000° C. for a stability increasing time so that at least 50% of said group IIA metal oxide is combined with alumina as a metal IIA aluminate or silico-aluminate, and the major portion of said zinc oxide is uncombined with the other components of the contact material.
Claim 14
Dependent Claim
141 words
Contact material according to claim 12, wherein the material consists essentially of by weight: ZnO: 25 - 80% CaO 3 - 30% Al 2 O 3 : 2 - 24% oxides of metals M: 0.01 - 10% SiO 2 : 5 - 30% Al 2 O 3 + SiO 2 + CaO = 15 - 60% M is copper, cadmium, titanium, zirconium, vanadium, chromium, molybdenum, tungsten, manganese, iron, cobalt or nickel, and wherein the material is in the form of grains of 3-8 mm diameter, its filling density in an industrial reactor is 0.8 - 1.4 metric ton/m3, its crushing strength is higher than 1 kg/mm, its porosity, as determined by mercury porosimetry, is 15 - 50 ml/kg, its average pore diameter is 1000 - 10,000 A and its specific surface ranges from 1 to 60 m 2 g -1 .
Claim 15
Dependent Claim
24 words
A process according to claim 1, wherein said adsorption material contains metal IIA aluminate or silico-aluminate prior to roasting the mixture at 500°-1000° C.
Claim 16
Dependent Claim
25 words
A contact material according to claim 12, wherein the contact material contains metal IIA aluminate or silico-aluminate prior to roasting the mixture at 500°-1000° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-05-08 | 1981-11-07 | 1982-05-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-05-08 | 1985-11-07 | 1986-05-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-05-08 | 1989-11-07 | 1990-05-09 | $7700.00 | Window Closed / Lapsed |