Method of improving the diecuttability of polyester urethane foam and the improved diecuttable polyester urethane foams themselves

Claim 2

A process for producing a diecuttable polyester urethane foam, useful in the production of hair curlers, characterized by improved diecuttability characteristics which comprises simultaneously reacting and foaming a reaction mixture consisting essentially of: (a) a polyester polyol reactant containing an average of at least two hydroxyl groups per molecule; (b) a polyisocyanate reactant containing at least two isocyanate groups per molecule; (c) a blowing agent; (d) a catalyst for the reaction of (a) and (b); (e) a foam stabilizer and (f) as a diecuttability enhancing additive, a low molecular weight polyol selected from the groups consisting of (1) an aliphatic alcohol having the following structural formula: ##STR14## wherein R 1 is hydrogen, alkyl (C 1 - C 8 ), or cycloalkyl (C 4 - C 8 ); R 2 is hydrogen or alkyl (C 1 - C 4 ); m and p are zero or integers and the sum of m and p is 8 or less; and n is an integer from 1 to about 4; (2) a low molecular weight polymethylol compound having the following structural formula: ##STR15## wherein R 2 is hydrogen, lower alkyl (C 1 to about C 8 ) or methylol (CH 2 OH); (3) an alkanolamine having the following structural formula: ##STR16## wherein R 3 is H or alkyl (C 1 to about C 4 ) and p and q are zero or integers from 1 to about 4; (4) alkylene oxide adducts having a functionality greater than 2 and a minimum hydroxyl number of about 100, and (5) mixtures thereof.

Claim 3

The process of claim 1 wherein the diecuttability enhancing additive is an aliphatic alcohol selected from the group consisting of glycerol; erythritol; sorbitol; 1, 2, 6 - hexanetriol; 1, 3, 5 - hexanetriol and 1, 2, 4 - butanetriol.

Claim 4

The process of claim 1 wherein the diecuttability enhancing additive is glycerol.

Claim 5

The process of claim 1 wherein the diecuttability enhancing additive is a polymethylol compound selected from the group consisting of trimethylolpropane, trimethylolethane and pentaerythritol.

Claim 6

The process of claim 4 wherein the polymethylol compound is trimethylolpropane.

Claim 7

The process of claim 1 wherein the diecuttability enhancing additive is an alkanolamine selected from the group consisting of diethanolamine, diisopropanolamine and ethanol isopropanol amine.

Claim 8

The process of claim 6 wherein the alkanolamine is diethanolamine.

Claim 9

The process of claim 1 wherein the diecuttability enhancing additive is an alkylene oxide adduct consisting of propylene oxide and a starter selected from the group consisting of glycerol, sucrose, diethylenetriamine and 1, 2, 6 - hexanetriol.

Claim 10

The process of claim 1 wherein the diecuttability enhancing additive is present in the range of from about 0.05 to about 10 parts per 100 parts of the polyester polyol reactant.

Claim 11

The process of claim 1 wherein the diecuttability enhancing additive is present in the range of about 0.1 to 6.0 parts per 100 parts of the polyester polyol reactant.

Claim 12

The process of claim 1 wherein the diecuttability enhancing additive is present in the range about 0.2 to 3.0 parts per 100 parts of the polyester polyol reactant.

Claim 13

The process of claim 1 wherein the polyisocyanate reaction is present in an amount sufficient to provide an isocyanate index of from about 100 to about 125.

Claim 14

The process of claim 1 wherein the foam stabilizer is a silicone surfactant.

Claim 15

The process of claim 36 which includes, cojointly with the diecuttability enhancing additive, a coadditive selected from the group consisting of (1) an alkylene oxide adduct with linear alcohols and phenols, the moles of alkylene oxide, per mole of the linear alcohols or phenols, being from about 3 to about 15, (2) sulfonated petroleum oils, (3) diethylammonium oleate, (4) cyanopropyl-substituted silicone-containing copolymers and (5) mixtures thereof, wherein the combined amount of additive and co-additive is from about 0.05 to about 10 parts per 100 parts by weight of the polyester polyol.

Claim 16

The process of claim 14 wherein the co-additive is an ethylene oxide-linear alcohol (C 11 - C 15 mixture) adduct.

Claim 17

The process of claim 14 wherein the co-additive is a sodium petroleum sulfonate anionic surfactant having an average molecular weight of about 420 and a mineral content of about 33 weight percent.

Claim 18

The process of claim 14 wherein the co-additive is a cyanopropyl-substituted polymethylsiloxane hydride having the average composition: ##STR17##

Claim 19

A polyester-based urethane foam, useful in the production of hair curlers, which comprises the product formed by simultaneously reacting and foaming a reaction mixture consisting essentially of: (a) a polyester polyol reactant containing an average of at least two hydroxyl groups per molecule; (b) a polyisocyanate reactant containing at least two isocyanate groups per molecule; (c) a blowing agent; (d) a catalyst for the reaction of (a) and (b); (e) a foam stabilizer and (f) as a diecuttability enhancing additive, a low molecular weight polyol selected from the groups consisting of (1 ) an aliphatic alcohol having the following structural formula: ##STR18## wherein R 1 is hydrogen, alkyl (C 1 - C 8 ), or cycloalkyl (C 4 - C 8 ); R 2 is hydrogen or alkyl (C 1 - C 4 ); m and p are zero or integers and the sum of m and p is 8 or less; and n is an integer from 1 to about 4; (2) a low molecular weight polymethylol compound having the following structural formula: ##STR19## wherein R 2 is hydrogen, lower alkyl (C 1 to about C 8 ) or methylol (CH 2 OH); (3) an alkanolamine having the following structural formula: ##STR20## wherein R 3 is H or alkyl (C 1 to about C 4 ) and p and q are zero or may have integral values from 1 to about 4; (4) alkylene oxide adducts having a functionality greater than 2 and a minimum hydroxyl number of about 100, and (5) mixtures thereof.

Claim 20

A polyester-based urethane foam, useful in the production of hair curlers, which comprises the product formed by simultaneously reacting and foaming a reaction mixture consisting essentially of: (a) a polyester polyol reactant containing an average of at least two hydroxyl groups per molecule; (b) a polyisocyanate reactant containing at least two isocyanate groups per molecule; (c) a blowing agent; (d) a catalyst for the reaction of (a) and (b); (e) a foam stabilizer and (f) as a diecuttability enhancing additive, a low molecular weight polyol selected from the groups consisting of (1 ) an aliphatic alcohol having the following structural formula: ##STR18## wherein R 1 is hydrogen, alkyl (C 1 - C 8 ), or cycloalkyl (C 4 - C 8 ); R 2 is hydrogen or alkyl (C 1 - C 4 ); m and p are zero or integers and the sum of m and p is 8 or less; and n is an integer from 1 to about 4; (2) a low molecular weight polymethylol compound having the following structural formula: ##STR19## wherein R 2 is hydrogen, lower alkyl (C 1 to about C 8 ) or methylol (CH 2 OH); (3) an alkanolamine having the following structural formula: ##STR20## wherein R 3 is H or alkyl (C 1 to about C 4 ) and p and q are zero or may have integral values from 1 to about 4; (4) alkylene oxide adducts having a functionality greater than 2 and a minimum hydroxyl number of about 100, and (5) mixtures thereof.

Claim 21

The polyester-based urethane foam of claim 18 wherein the diecuttability enhancing additive is an alphatic alcohol selected from the group consisting glycerol; erythritol; sorbitol; 1, 2, 6 -hexanetriol; 1, 3, 5 - hexanetriol and 1, 2, 4 - butanetriol.

Claim 22

The polyester-based urethane foam of claim 18 wherein the diecuttability enhancing additive is glycerol.

Claim 23

The polyester-based urethane foam of claim 18 wherein the diecuttability enhancing additive is a polymethylol compound selected from the group consisting of trimethylolpropane, trimethylolethane and pentaerythritol.

Claim 24

The polyester-based urethane foam of claim 18 wherein the polymethylol compound is trimethylolpropane.

Claim 25

The polyester-based urethane foam of claim 18 wherein the diecuttability enhancing additive is an alkanolamine selected from the group consisting of diethanolamine, diisopropanolamine and ethanol isopropanol amine.

Claim 26

The polyester-based urethane foam of claim 18 wherein the alkanolamine is diethanolamine.

Claim 27

The polyester-based urethane foam of claim 18 wherein the diecuttability enhancing additive is an alkylene oxide adduct consisting of propylene oxide and a starter selected from the group consisting of glycerol, sucrose, diethylenetriamine and 1, 2, 6 - hexanetriol.

Claim 28

The polyester-based urethane foam of claim 18 wherein the diecuttability enhancing additive is present in the range of about 0.05 to about 10 parts per 100 parts of the polyester polyol reactant.

Claim 29

The polyester-based urethane foam of claim 18 wherein the diecuttability enhancing additive is present in the range about 0.1 to 6.0 parts per 100 parts of the polyester polyol reactant.

Claim 30

The polyester-based urethane foam of claim 18 wherein the diecuttability enhancing additive is present in the range about 0.2 to 3.0 parts per 100 parts of the polyester polyol reactant.

Claim 31

The polyester-based urethane foam of claim 37 which includes, cojointly with the diecuttability enhancing additive, a co-additive selected from the group consisting of (1) alkylene oxide adduct with linear alcohols and phenols, the moles of alkylene oxide, per mole of the linear alcohols and phenols, being from about 3 to about 15, (2) sulfonated petroleum oils, (3) diethylammonium oleate, (4) cyanopropyl-substituted silicone-containing polymers and (5) mixtures thereof, wherein the amount of co-additive is from about 0 to about 9.95 parts per 100 parts by weight of the polyester polyol with the proviso that the combined amount of additive and co-additive be between about 0.15 and about 10 parts per 100 parts by weight of the polyester polyol.

Claim 32

The polyester-based urethane foam of claim 29 wherein the co-additive is an ethylene oxide-linear alcohol (C 11 - C 15 mixture) adduct.

Claim 33

The polyester-based urethane foam of claim 29 wherein the co-additive is a sodium petroleum sulfonate anionic surfactant having an average molecular weight of about 420 and a mineral content of about 33 weight percent.

Claim 34

The polyester-based urethane foam of claim 29 wherein the co-additive is a cyanopropyl-substituted polymethylsiloxane hydride having the average composition: ##STR21##

Claim 35

A process for producing a diecuttable polyester urethane foam characterized by improved diecuttability characteristics which comprises simultaneously reacting and foaming a reaction mixture containing: (a) a polyester polyol reactant containing an average of at least two hydroxyl groups per molecule; (b) a polyisocyanate reactant containing at least two isocyanate groups per molecule; (c) a blowing agent; (d) a catalyst for the reaction of (a) and (b); (e) a foam stabilizer and (f) as a diecuttability enhancing additive, a low molecular weight polyol selected from the groups consisting of (1) an aliphatic alcohol having the following structural formula: ##STR22## wherein R 1 is hydrogen, alkyl (C 1 - C 8 ), or cycloalkyl (C 4 - C 8 ); R 2 is hydrogen or alkyl (C 1 - C 4 ); m and p are integers and the sum of m and p is 8 or less; and n is an integer from 1 to about 4; (2) a low molecular weight polymethylol compound having the following structural formula: ##STR23## wherein R 2 is hydrogen, lower alkyl (C 1 to about C 8 ) or methylol (CH 2 OH); (3) an alkanolamine having the following structural formula: ##STR24## wherein R 3 is H or alkyl (C 1 to about C 4 ) and p and q are zero or integers from 1 to about 4; (4) alkylene oxide adducts having a functionality greater than 2 and a minimum hydroxyl number of about 100, and (5) mixtures thereof.

Claim 36

A process for producing a diecuttable polyester urethane foam characterized by improved diecuttability characteristics which comprises simultaneously reacting and foaming a reaction mixture containing: (a) a polyester polyol reactant containing an average of at least two hydroxyl groups per molecule; (b) a polyisocyanate reactant containing at least two isocyanate groups per molecule; (c) a blowing agent; (d) a catalyst for the reaction of (a) and (b); (e) a foam stabilizer and (f) as a diecuttability enhancing additive, a low molecular weight polyol selected from the groups consisting of (1) an aliphatic alcohol having the following structural formula: ##STR22## wherein R 1 is hydrogen, alkyl (C 1 - C 8 ), or cycloalkyl (C 4 - C 8 ); R 2 is hydrogen or alkyl (C 1 - C 4 ); m and p are integers and the sum of m and p is 8 or less; and n is an integer from 1 to about 4; (2) a low molecular weight polymethylol compound having the following structural formula: ##STR23## wherein R 2 is hydrogen, lower alkyl (C 1 to about C 8 ) or methylol (CH 2 OH); (3) an alkanolamine having the following structural formula: ##STR24## wherein R 3 is H or alkyl (C 1 to about C 4 ) and p and q are zero or integers from 1 to about 4; (4) alkylene oxide adducts having a functionality greater than 2 and a minimum hydroxyl number of about 100, and (5) mixtures thereof.

Claim 37

A polyester-based urethane foam which comprises the product formed by simultaneously reacting and foaming a reaction mixture containing: (a) a polyester polyol reactant containing an average of at least two hydroxyl groups per molecule; (b) a polyisocyanate reactant containing at least two isocyanate groups per molecule; (c) a blowing agent; (d) a catalyst for the reaction of (a) and (b); (e) a foam stabilizer and (f) as a diecuttability enhancing additive, a low molecular weight polyol selected from the groups consisting of (1) an aliphatic alcohol having the following structural formula: ##STR25## wherein R 1 is hydrogen, alkyl (C 1 - C 8 ), or cycloalkyl (C 4 - C 8 ); R 2 is hydrogen or alkyl (C 1 - C 4 ); m and p are integers and the sum of m and p is 8 or less; and n is an integer from 1 to about 4; (a) a low molecular weight polymethylol compound having the following structural formula: ##STR26## wherein R 2 is hydrogen, lower alkyl (C 1 to about C 8 ) or methylol (CH 2 OH); (3) an alkanolamine having the following structural formula: ##STR27## wherein R 3 is H or alkyl (C 1 to about C 4 ) and p and q are zero or may have integral values from 1 to about 4; (4) alkylene oxide adducts having a functionality greater than 2 and a minimum hydroxyl number of about 100, and (5) mixtures thereof.

Claim 38

A polyester-based urethane foam which comprises the product formed by simultaneously reacting and foaming a reaction mixture containing: (a) a polyester polyol reactant containing an average of at least two hydroxyl groups per molecule; (b) a polyisocyanate reactant containing at least two isocyanate groups per molecule; (c) a blowing agent; (d) a catalyst for the reaction of (a) and (b); (e) a foam stabilizer and (f) as a diecuttability enhancing additive, a low molecular weight polyol selected from the groups consisting of (1) an aliphatic alcohol having the following structural formula: ##STR25## wherein R 1 is hydrogen, alkyl (C 1 - C 8 ), or cycloalkyl (C 4 - C 8 ); R 2 is hydrogen or alkyl (C 1 - C 4 ); m and p are integers and the sum of m and p is 8 or less; and n is an integer from 1 to about 4; (a) a low molecular weight polymethylol compound having the following structural formula: ##STR26## wherein R 2 is hydrogen, lower alkyl (C 1 to about C 8 ) or methylol (CH 2 OH); (3) an alkanolamine having the following structural formula: ##STR27## wherein R 3 is H or alkyl (C 1 to about C 4 ) and p and q are zero or may have integral values from 1 to about 4; (4) alkylene oxide adducts having a functionality greater than 2 and a minimum hydroxyl number of about 100, and (5) mixtures thereof.

Claim 39

A polyester-based urethane foam as claimed in claim 18 having from 25 to 50 cells per linear inch.

Claim 40

A polyester-based urethane foam as claimed in claim 18 having a density from 1.65 to 1.96 pounds per cubic foot.

Claim 41

A polyester-based urethane foam as claimed in claim 18 having a density from 1.65 to 1.96 pounds per cubic foot and having from 25 to 50 cells per linear inch.

Claim 42

A process for producing a diecuttable polyester urethane foam, useful in the production of hair curlers, characterized by improved diecuttability characteristics which comprises simultaneously reacting and foaming a reaction mixture consisting essentially of: (a) a polyester polyol reactant containing an average of at least two hydroxyl groups per molecule; (b) a polyisocyanate reactant containing an average of at least two isocyanate groups per molecule in an amount sufficient to produce an Isocyanate Index of from about 100 to about 125; (c) a blowing agent; (d) a catalyst for the reaction of (a) and (b); (e) a foam stabilizer; (f) as a diecuttability enhancing additive, a low molecular weight polyol selected from the groups consisting of (1) an aliphatic alcohol having the following structural formula: ##STR28## wherein R 1 is hydrogen, alkyl (C 1 - C 8 ), or cycloalkyl (C 4 - C 8 ); R 2 is hydrogen or alkyl (C 1 - C 4 ); m and p are zero or integers and the sum of m and p is 8 or less; and n is an integer from 1 to about 4; (2) a low molecular weight polymethylol compound having the following structural formula: ##STR29## wherein R 2 is hydrogen, lower alkyl (C 1 to about C 8 ) or methylol (CH 2 OH); (3) an alkanolamine having the following structural formula: ##STR30## wherein R 3 is H or alkyl (C 1 to about C 4 ) and p and q are zero or integers from 1 to about 4; (4) alkylene oxide adducts having a functionality greater than 2 and a minimum hydroxyl number of about 100, and (5) mixtures thereof, in an amount of from about 0.2 to about 3.0 parts per 100 parts by weight of the polyester polyol; and (g) a co-additive selected from the group consisting of (1) an alkylene oxide adduct with linear alcohols and phenols, the moles of alkylene oxide, per mole of the linear alcohols or phenols, being from about 3 to about 15, (2) sulfonated petroleum oils, (3) diethylammonium oleate, (4) cyanopropyl-substituted silicone-containing copolymers and (5) mixtures thereof, wherein the combined amount of additive and co-additive is from about 0.2 to about 10 parts per 100 parts by weight of the polyester polyol.

Claim 43

A process for producing a diecuttable polyester urethane foam, useful in the production of hair curlers, characterized by improved diecuttability characteristics which comprises simultaneously reacting and foaming a reaction mixture consisting essentially of: (a) a polyester polyol reactant containing an average of at least two hydroxyl groups per molecule; (b) a polyisocyanate reactant containing an average of at least two isocyanate groups per molecule in an amount sufficient to produce an Isocyanate Index of from about 100 to about 125; (c) a blowing agent; (d) a catalyst for the reaction of (a) and (b); (e) a foam stabilizer; (f) as a diecuttability enhancing additive, a low molecular weight polyol selected from the groups consisting of (1) an aliphatic alcohol having the following structural formula: ##STR28## wherein R 1 is hydrogen, alkyl (C 1 - C 8 ), or cycloalkyl (C 4 - C 8 ); R 2 is hydrogen or alkyl (C 1 - C 4 ); m and p are zero or integers and the sum of m and p is 8 or less; and n is an integer from 1 to about 4; (2) a low molecular weight polymethylol compound having the following structural formula: ##STR29## wherein R 2 is hydrogen, lower alkyl (C 1 to about C 8 ) or methylol (CH 2 OH); (3) an alkanolamine having the following structural formula: ##STR30## wherein R 3 is H or alkyl (C 1 to about C 4 ) and p and q are zero or integers from 1 to about 4; (4) alkylene oxide adducts having a functionality greater than 2 and a minimum hydroxyl number of about 100, and (5) mixtures thereof, in an amount of from about 0.2 to about 3.0 parts per 100 parts by weight of the polyester polyol; and (g) a co-additive selected from the group consisting of (1) an alkylene oxide adduct with linear alcohols and phenols, the moles of alkylene oxide, per mole of the linear alcohols or phenols, being from about 3 to about 15, (2) sulfonated petroleum oils, (3) diethylammonium oleate, (4) cyanopropyl-substituted silicone-containing copolymers and (5) mixtures thereof, wherein the combined amount of additive and co-additive is from about 0.2 to about 10 parts per 100 parts by weight of the polyester polyol.

Claim 44

A diecuttable polyester urethane foam produced by the process of claim 38.