US4088607A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Catalyst and method of preparing same
Assignee: Kali Chemie AG
•
Filing: 1976-08-25
•
Granted: 1978-05-09
•
Expires: 1996-08-25
Abstract
Abstract Disclosed is an improved catalyst having a high thermal stability including a solid catalyst support having a layer of catalytically active carrier material, either as a coating on a non-catalytically active support or as particles of catalytically active carrier material, and a catalytically active metal component upon the carrier, wherein the improved aspect resides in between about 0.2 and 15% by weight of zinc in the form of zinc oxide contained in the catalytically active carrier material. Also disclosed are a method for preparing the improved catalyst and a method for utilizing the catalyst for purifying automobile exhaust gas and industrial waste gas.
Inventors
- 👤 Guenther Weidenbach
- 👤 Karl H. Koepernik
- 👤 Hans Brautigam
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 06:09
CPC Classifications
B; B01; B01D; B01D53/00; B01D53/34; B01D53/92; B01D53/94; B01D53/9445; B01D53/945; B01J; B01J23/00; B01J23/06; B01J23/38; B01J23/54; B01J23/56; B01J23/60; B01J37/00; B01J37/02; B01J37/024; Y; Y02; Y02A; Y02A50/00; Y02A50/20; Y02T; Y02T10/00; Y02T10/10; Y02T10/12
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
61 words
In a catalyst having a high thermal stability, including a solid catalytically active carrier material and a catalytically active metal component consisting essentially of at least one noble metal upon said carrier, the improvement which comprises said catalytically active carrier material consisting essentially of aluminum oxide and having admixed therewith between about 0.5 and 8% by weight of preformed zinc oxide.
Claim 2
Dependent Claim
61 words
In a catalyst having a high thermal stability, including a solid catalytically active carrier material and a catalytically active metal component consisting essentially of at least one noble metal upon said carrier, the improvement which comprises said catalytically active carrier material consisting essentially of aluminum oxide and having admixed therewith between about 0.5 and 8% by weight of preformed zinc oxide.
Claim 3
Dependent Claim
25 words
The catalyst as defined by claim 1, wherein said solid catalyst support comprises a bed of discrete solid particles comprising said catalytically active carrier material.
Claim 4
Dependent Claim
24 words
The catalyst as defined in claim 1, wherein said catalytically active metal component comprises about 0.01 and 1% by weight of platinum or palladium.
Claim 5
Dependent Claim
29 words
The catalyst as defined in claim 3, wherein said catalytically active metal comprises a mixture of platinum and palladium in a ratio of between about 9:5 to 4:3, respectively.
Claim 6
Dependent Claim
42 words
The catalyst as defined in claim 1, wherein said active metal component comprises between about 0.01 and 1.0% of platinum in combination with up to 0.5% ruthenium, said platinum and ruthenium being present in a ratio from about 1:3 to 1:0.15, respectively.
Claim 7
Dependent Claim
32 words
The catalyst as defined in claim 1, wherein said catalytically active metal comprises a mixture of platinum, ruthenium, rhodium and rhenium in a ratio of from about 1:1:1:1 to about 1:0.25:0.25:0.25, respectively.
Claim 8
Dependent Claim
22 words
The catalyst as defined by claim 1 which comprises a solid catalyst support bearing a layer of the catalytically active carrier material.
Claim 9
Dependent Claim
30 words
The catalyst as defined by claim 7, wherein said solid catalyst support comprises a solid reticulated structure of catalytically inert material bearing a layer of the catalytically active carrier material.
Claim 10
Dependent Claim
16 words
The catalyst as defined by claim 8, wherein said reticulated structure is a ceramic honey-comb structure.
Claim 11
Dependent Claim
16 words
The catalyst as defined by claim 8, wherein said reticulated structure is a metallic honey-comb structure.
Claim 12
Dependent Claim
85 words
A process for the preparation of the catalyst defined in claim 7, comprising the steps of mixing together in the presence of water a finely divided precursor of the catalytically active carrier material and an amount of finely divided zinc oxided, sufficient to obtain the catalytically active carrier material containing between about 0.5 and 8% by weight of zinc oxide, forming a layer of said zinc oxide-containing carrier material on a solid catalyst support and depositing thereon a layer of said catalytically active metal component.
Claim 13
Dependent Claim
35 words
The process as defined by claim 11, wherein said drying is conducted at a temperature between about 100° and 250° C and said calcining is conducted at a temperature between about 600° and 1200° C.
Claim 14
Dependent Claim
20 words
The process as defined by claim 11, wherein said precursor of the catalytically active carrier material is aluminum oxide hydrate.
Claim 15
Dependent Claim
64 words
The process as defined by claim 13, wherein said mixture of zinc oxide and aluminum oxide hydrate comprises an aqueous suspension of said components in highly dispersed form, said components having a particle size of about 0.5 to about 5μ, and said step of forming a layer of carrier material on a solid support comprises coating a catalytically inert support with said aqueous suspension.
Claim 16
Dependent Claim
22 words
The process as defined in claim 14, wherein the particle size of the dispersed components is between about 1 and about 3μ.
Claim 17
Dependent Claim
35 words
The process as defined by claim 11, wherein said step of forming the layer of carrier material on a solid support comprises forming discrete solid particles from said mixture of carrier material and zinc oxide.
Claim 18
Dependent Claim
19 words
The process as defined by claim 16, wherein said precursor of the catalytically active carrier material is aluminum oxide.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-05-08 | 1981-11-07 | 1982-05-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-05-08 | 1985-11-07 | 1986-05-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-05-08 | 1989-11-07 | 1990-05-09 | $7700.00 | Window Closed / Lapsed |