Abstract
Abstract A method of making a duo density article of silicon nitride is disclosed. A first element is formed by hot pressing silicon nitride particles. The general shape of a second element is formed by injection molding silicon metal particles and a binder and subsequently burning out the binder. The second element is nitrided in a nitriding operation. Facing surface areas of the first element and the second element are bonded together by applying heat to both elements and pressure to one of the elements while the other element is held in a fixed position.
Inventors
- 👤 Eugene A. Fisher
- 👤 Michael U. Goodyear
- 👤 Arthur F. McLean
- 👤 Karsten H. Styhr
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 20:01
CPC Classifications
F; F01; F01D; F01D5/00; F01D5/12; F01D5/28; F01D5/284; C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/584; C04B35/591; C04B35/593
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
222 words
A method of making a duo density article of silicon nitride which comprises the steps of: compacting a mixture consisting of from about 95 to 99.5% by weight silicon nitride particles and from about 5 to 0.5% by weight of a densification aid to at least 98% of theoretical density by use of heat and pressure thereby to form a first element of silicon nitride; forming the general shape of a second element by (a) injection molding silicon metal particles and a carrier to fform the general shape of said second element, and (b) heating said second element to burn out said carrier; nitriding said second element so that said element is converted substantially to pure silicon nitride; bringing a surface area of said first element into close association with a surface area of said second element; holding said associated surfaces of said first and said second elements so they do not move with respect to one another; and forming a bond between said associated surfaces of said first and said second elements by applying heat on both elements and pressure on one of said elements while the other of said elements is held thereby to force a portion of the silicon nitride forming said surface area of said one element into bonding relationship with said surface area of the other element.
Claim 2
Independent Claim
222 words
A method of making a duo density article of silicon nitride which comprises the steps of: compacting a mixture consisting of from about 95 to 99.5% by weight silicon nitride particles and from about 5 to 0.5% by weight of a densification aid to at least 98% of theoretical density by use of heat and pressure thereby to form a first element of silicon nitride; forming the general shape of a second element by (a) injection molding silicon metal particles and a carrier to fform the general shape of said second element, and (b) heating said second element to burn out said carrier; nitriding said second element so that said element is converted substantially to pure silicon nitride; bringing a surface area of said first element into close association with a surface area of said second element; holding said associated surfaces of said first and said second elements so they do not move with respect to one another; and forming a bond between said associated surfaces of said first and said second elements by applying heat on both elements and pressure on one of said elements while the other of said elements is held thereby to force a portion of the silicon nitride forming said surface area of said one element into bonding relationship with said surface area of the other element.
Claim 3
Dependent Claim
34 words
The method of claim 1 wherein: said first element is the one element to which pressure is applied to force its surface area into bonding relationship with said surface area of said second element.
Claim 4
Dependent Claim
12 words
The method of claim 1 wherein: said densification aid is magnesium oxide.
Claim 5
Dependent Claim
41 words
The method of claim 1 wherein: said compacting operation takes place at a temperature from of about 1650° C to about 1800° C at a pressure of from at least 3000 psi and for a time of at least 1.5 hours.
Claim 6
Dependent Claim
41 words
The method of claim 1 wherein: said bond forming operation takes place at a temperature of from about 1625° C to about 1700° C at a pressure of at least 1000 psi and for a time of at least 1.5 hours.
Claim 7
Dependent Claim
21 words
The method of claim 1 wherein: said suitable carrier used in the formation of said second element is a thermoplastic resin.
References Cited (Backward Citations)
US2195297A
Cited
US2434271A
Cited
US3399979A
Cited
JPS434515Y1
Cited
GB1092637A
Cited
DE1949587A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-05-01 | 1981-10-31 | 1982-05-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-05-01 | 1985-10-31 | 1986-05-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-05-01 | 1989-10-31 | 1990-05-02 | $7700.00 | Window Closed / Lapsed |