Wood lamination method utilizing emulsified phenol-formaldehyde resins

Claim 1

A method of forming a panel board, which comprises: reacting formaldehyde and phenol at a mole ratio of formaldehyde to phenol greater than about 1.7:1 in an aqueous reaction medium in the presence of a metal carboxylate catalyst therefor to form a resin having a viscosity of about 1,000 to 40,000 cps at about 24° C, adding to said resin at least one strong acid in a catalyzing amount for thermosetting said resin at elevated temperature to form a room temperature-stable acid-catalyzed and mobile thermosetting phenol-formaldehyde resin capable of rapid cure at elevated temperature, emulsifying the latter resin to form a stable resin-in-water emulsion by dispersing the latter resin in water at a temperature below the curing temperature of the latter resin, applying said emulsion to a plurality of panel board-forming elements to provide a substantially even distribution of resin over part of the surfaces of said elements, assembling the coated elements, heating said resin to above its curing temperature while maintaining said coated elements in said assembled condition to adhesively join said elements together by thermoset resins, and recovering a panel board.

Claim 2

A method of forming a panel board, which comprises: reacting formaldehyde and phenol at a mole ratio of formaldehyde to phenol greater than about 1.7:1 in an aqueous reaction medium in the presence of a metal carboxylate catalyst therefor to form a resin having a viscosity of about 1,000 to 40,000 cps at about 24° C, adding to said resin at least one strong acid in a catalyzing amount for thermosetting said resin at elevated temperature to form a room temperature-stable acid-catalyzed and mobile thermosetting phenol-formaldehyde resin capable of rapid cure at elevated temperature, emulsifying the latter resin to form a stable resin-in-water emulsion by dispersing the latter resin in water at a temperature below the curing temperature of the latter resin, applying said emulsion to a plurality of panel board-forming elements to provide a substantially even distribution of resin over part of the surfaces of said elements, assembling the coated elements, heating said resin to above its curing temperature while maintaining said coated elements in said assembled condition to adhesively join said elements together by thermoset resins, and recovering a panel board.