Composition of matter comprising cellular aggregate distributed in a binder
Assignee: BFG Glassgroup GIE
•
Filing: 1976-11-10
•
Granted: 1978-04-25
•
Expires: 1996-11-10
Abstract
Abstract There is provided a composition of matter comprising a cellular aggregate distributed in a hardenable or hardened binder or matrix material, in which the aggregate consists of or includes (i) a fraction of cellular glass beads of mesh sizes up to 3 mm, individually containing one or more interior cells with a maximum cross-sectional dimension at least 0.3 times the mesh size of the bead and having a non-cellular or micro-cellular surface skin, and (ii) a fraction of cellular glass beads of mesh sizes above 3 mm, individually having a multicellular core with a cell population per unit volume substantially higher than the population of said interior cells in said fine fraction beads and likewise having a non-cellular or micro-cellular surface skin.
Inventors
- 👤 Daniel Le Ruyet
- 👤 Daniel De Vos
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 20:03
CPC Classifications
C; C04; C04B; C04B26/00; C04B26/02; C03; C03C; C03C11/00; C04B28/00; C04B28/02
Claims Analysis
Total Claims: 34
Claim 1
Independent Claim
162 words
A composition of matter comprising a cellular aggregate distributed in a hardenable or hardened binder or matrix material, characterised in that the aggregate comprises (1) a fine fraction of cellular glass beads of mesh sizes up to 3 mm, individually containing one or more interior cells with a maximum cross-sectional dimension at least 0.3 times the mesh size of the bead and having a non-cellular or micro-cellular surface skin, and (2) a fraction of coarse cellular glass beads of mesh sizes above 3 mm, individually having a multicellular core with a cell population per unit volume substantially higher than the population of said interior cells in said fine fraction beads and likewise having a non-cellular or micro-cellular surface skin, the ratio between the bulk volumes of the coarse fraction beads and the fine fraction beads being between 6:1 and 1:1, the volume of the combined fine and coarse fractions of beads being at least 50% of the dry volume of the composition.
Claim 2
Dependent Claim
162 words
A composition of matter comprising a cellular aggregate distributed in a hardenable or hardened binder or matrix material, characterised in that the aggregate comprises (1) a fine fraction of cellular glass beads of mesh sizes up to 3 mm, individually containing one or more interior cells with a maximum cross-sectional dimension at least 0.3 times the mesh size of the bead and having a non-cellular or micro-cellular surface skin, and (2) a fraction of coarse cellular glass beads of mesh sizes above 3 mm, individually having a multicellular core with a cell population per unit volume substantially higher than the population of said interior cells in said fine fraction beads and likewise having a non-cellular or micro-cellular surface skin, the ratio between the bulk volumes of the coarse fraction beads and the fine fraction beads being between 6:1 and 1:1, the volume of the combined fine and coarse fractions of beads being at least 50% of the dry volume of the composition.
Claim 3
Dependent Claim
153 words
A light-weight moulded composition, formed from a binder, and coarse and fine aggregates, characterised in that the fine aggregates have a granulometry between 0 and 4 mm, these aggregates being composed, at least in part, of granules of an expanded glass product, the granules having very small water absorbency and an apparent volume mass of not more than 350 kg/m 3 , and in that the coarse aggregates have a granulometry between 3 and 30 mm, these coarse aggregates being composed, at least in part, of granules of an expanded product, the granules having small water absorbency and an apparent volume mass of not more than 200 kg/m 3 , the ratio between the bulk volumes of the coarse fraction beads and the fine fraction beads being between 6:1 and 1:1, the volume of the combined fine and coarse fractions of beads being at least 50% of the dry volume of the composition.
Claim 4
Dependent Claim
153 words
A light-weight moulded composition, formed from a binder, and coarse and fine aggregates, characterised in that the fine aggregates have a granulometry between 0 and 4 mm, these aggregates being composed, at least in part, of granules of an expanded glass product, the granules having very small water absorbency and an apparent volume mass of not more than 350 kg/m 3 , and in that the coarse aggregates have a granulometry between 3 and 30 mm, these coarse aggregates being composed, at least in part, of granules of an expanded product, the granules having small water absorbency and an apparent volume mass of not more than 200 kg/m 3 , the ratio between the bulk volumes of the coarse fraction beads and the fine fraction beads being between 6:1 and 1:1, the volume of the combined fine and coarse fractions of beads being at least 50% of the dry volume of the composition.
Claim 5
Dependent Claim
19 words
A composition according to claim 1 wherein the fine and coarse fraction beads both have substantially water-impermeable surface skins.
Claim 6
Dependent Claim
23 words
A composition according to claim 3 wherein the said coarse fraction beads cover a size range extending up to at least 8 mm.
Claim 7
Dependent Claim
23 words
A composition according to claim 4 wherein the said coarse fraction beads cover a size range extending up to at least 16 mm.
Claim 8
Dependent Claim
21 words
A composition according to claim 4 wherein the fine fraction beads cover a size range extending down to below 1 mm.
Claim 9
Dependent Claim
41 words
A composition according to claim 6 characterized in that the fine fraction beads have a bulk density of not more than 350 kg/m 3 and the coarse fraction beads have a bulk density of not more than 200 kg/m 3 .
Claim 10
Dependent Claim
37 words
A composition according to claim 7 wherein the fine fraction beads have a bulk density between 250 and 350 kg/m 3 and the coarse fraction beads have a bulk density between 80 and 200 kg/m 3 .
Claim 11
Dependent Claim
15 words
A composition according to claim 1 wherein the binder or matrix material is Portland cement.
Claim 12
Dependent Claim
23 words
A composition according to claim 9 wherein the coarse fraction beads are wholly or predominantly in the size range 8 to 16 mm.
Claim 13
Dependent Claim
65 words
A composition according to claim 10 wherein the coarse fraction beads are classifiable into two sub-fractions, sub-fraction (a) containing beads above 8 mm and sub-fraction (b) containing beads 3 and 8 mm in size, the bulk volume of the sub-fraction (b) beads being less than the bulk volume of the beads of sub-fraction (a) but greater than the bulk volume of the fine fraction beads.
Claim 14
Dependent Claim
36 words
A composition according to claim 1 wherein the proportions by volumes of said fine and coarse fractions of beads in the composition is such that the dry composition has a thermal conductivity below 0.25 kcal/mh° C.
Claim 15
Dependent Claim
51 words
A composition according to claim 1 wherein the proportions by volumes of said fine and coarse fractions in the composition and their size distribution are such that the dry composition 28 days after setting has a density below 950kg/m 3 and a compression resistance of more than 60 kg/cm 2 .
Claim 16
Dependent Claim
12 words
A composition according to claim 9 wherein the cement also contains sand.
Claim 17
Dependent Claim
16 words
A composition according to claim 1 wherein the binder or matrix material comprises a synthetic polymer.
Claim 18
Dependent Claim
21 words
A composition according to claim 15 wherein the binder or matrix material comprises a polyurethane, a phenol-aldehyde, epoxy or polyester resin.
Claim 19
Dependent Claim
23 words
A light-weight composition according to claim 2 wherein the apparent volume mass of the aggregates decreases as the diameter of the aggregates increases.
Claim 20
Dependent Claim
23 words
A light-weight composition according to claim 17 wherein the volume mass of the fine aggregates is between 80 and 250 kg/m 3 .
Claim 21
Dependent Claim
31 words
A light-weight composition according to claim 17 wherein the volume mass of the coarse aggregates is between 80 and 200 kg/m 3 and is lower than that of the fine aggregates.
Claim 22
Dependent Claim
18 words
A composition according to claim 19 wherein the coarse aggregates have a granulometry between 3 and 16 mm.
Claim 23
Dependent Claim
17 words
A composition according to claim 20 wherein the expanded product is at least partially in vitrified state.
Claim 24
Dependent Claim
17 words
A composition according to claim 21 wherein the granules are mono or multi-cellular granules with closed pores.
Claim 25
Dependent Claim
16 words
A composition according to claim 22 wherein the granules are of substantially spherical or ellipsoidal form.
Claim 26
Dependent Claim
12 words
A composition according to claim 22 wherein the binder is Portland cement.
Claim 27
Dependent Claim
22 words
A composition according to claim 22 wherein the binder is plaster, bitumen, a rigid or alveolate thermoplastic resin, or a thermosetting resin.
Claim 28
Dependent Claim
27 words
A composition according to claim 22 wherein the expanded product is, at least in part, expanded obsidian, expanded basalt, expanded rhyolite, expanded perlite, expanded slag or clinker.
Claim 29
Dependent Claim
45 words
A composition according to claim 22 wherein it has a volume mass, at the end of 28 days, below 950 kg/m 3 , a thermal conductivity below 0.25 kcal/h/m/° C and a compressiion resistance, at the end of 28 days, above 60 kg/cm 2 .
Claim 30
Dependent Claim
28 words
A composition according to claim 27 wherein it has a compression resistance, at the end of 28 days of the order of 70 to 120 kg/cm 2 .
Claim 31
Dependent Claim
23 words
A composition according to claim 1 wherein the binder or matrix comprises Portland cement, gypsum, a thermoplastic resin, a thermosetting resin or bitumen.
Claim 32
Dependent Claim
18 words
A composition according to claim 29 wherein the fine and coarse fraction beads both have substantially water-impermeable surfaces.
Claim 33
Dependent Claim
21 words
A composition according to claim 30 wherein the binder or matrix is hardenable and the composition comprises Portland cement and water.
Claim 34
Dependent Claim
16 words
A composition according to claim 30 wherein the binder or matrix is in the hardened state.
References Cited (Backward Citations)
US3562370A
Cited
US3503771A
Cited
US3764357A
Cited
US3804058A
Cited
US3823021A
Cited
US4002482A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-04-24 | 1981-10-24 | 1982-04-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-04-24 | 1985-10-24 | 1986-04-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-04-24 | 1989-10-24 | 1990-04-25 | $7700.00 | Window Closed / Lapsed |