Process for separation of non-magnetic particles with ferromagnetic media

Claim 2

Process for separating solid particles from admixture which comprises providing a homogeneous ferrohydrodynamic medium containing a colloidal suspension of superparamagnetic particles therein, said medium being in the molten state and also containing a mixture of at least two non-colloidal non-magnetic particles of differing densities both of which are greater than the actual density of the medium, imposing a non-uniform magnetic field upon said particles and said ferrohydrodynamic medium whereby the said particles are moved within said medium and segregated into different zones thereof in accodance with the respective densities of the particles, solidifying the liquid medium constituting at least one of said zones to immobilize the particles as segregated therein and to prevent the introduction thereinto of extraneous particles.

Claim 3

Process according to claim 1 wherein a sufficient portion of the ferrohydrodynamic liquid is solidified that the solid portion contains at least two zones, one of which contains a predominance of particles having densities less than that of the predominance of particles in the second zone.

Claim 4

Process according to claim 1 wherein the mixture of particles being separated consists essentially of particles having diameters of from about 0.03 to 1.0 millimeters and the diameter of the largest particles is not greater than five times that of the smallest particles.

Claim 5

Process for separating solid particles from admixture which comprises providing a homogeneous ferrohydrodynamic medium containing a colloidal suspension of superparamagnetic particles therein, said medium being a wax in which the transition from the liquid state to the solid state occurs above 40° and below 100° C, said medium being in the molten state and also containing a mixture of at least two non-colloidal non-magnetic particles of differing densities both of which are greater than the actual density of the medium, imposing an non-uniform magnetic field upon said particles and said ferrohydrodynamic medium whereby the said particles are moved within said medium and segregated into different zones thereof in accordance with the respective densities of the particles, solidifying the liquid medium constituting at least one of said zones to immobilize the particles as segregated therein and to prevent the introduction thereinto of extraneous particles.

Claim 6

Process for separating solid particles from admixture which comprises providing a homogeneous ferrohydrodynamic medium containing a colloidal suspension of superparamagnetic particles therein, said medium being a wax in which the transition from the liquid state to the solid state occurs above 40° and below 100° C, said medium being in the molten state and also containing a mixture of at least two non-colloidal non-magnetic particles of differing densities both of which are greater than the actual density of the medium, imposing an non-uniform magnetic field upon said particles and said ferrohydrodynamic medium whereby the said particles are moved within said medium and segregated into different zones thereof in accordance with the respective densities of the particles, solidifying the liquid medium constituting at least one of said zones to immobilize the particles as segregated therein and to prevent the introduction thereinto of extraneous particles.

Claim 7

Process according to claim 4 wherein the temperature range over which the transition from the solid to the liquid state occurs is less than 10° C.

Claim 8

Process according to claim 4 wherein the wax contains from 10 to 90 weight percent hydrocarbon wax and from 10 to 90 weight percent oxygenated wax.