Heat resistant radar absorber

Claim 2

A radar absorber adapted for heat resistance comprising a ceramic thermal barrier bonded to an organic RAM substrate, said thermal barrier consisting of a foamed ceramic slab and said substrate consisting of a layered polyimide RAM.

Claim 3

The absorber in claim 1, said foamed ceramic slab having a thickness substantially no greater than 0.5 inches, and said polyimide substrate having a thickness substantially no greater than 0.8 inches, to provide heat protection up to 3000° F for 80 seconds and radar absorptivity of at least 10db over the range 3 to at least 10 GHt.

Claim 4

In the process of making a heat-resistant radar absorber, the process of bonding formed ceramic blocks to a polyimide RAM substrate, comprising the steps of: a. hand-mixing a ceramic adhesive consisting of 63% by weight of a mixed oxide powder (SiO 2 , ZrO 2 ), 33% by weight of a 30% solution of sodium silicate, and 4% by weight of Kaowool fibers; b. covering with a removable plastic film the polyimide substrate surface to which said ceramic blocks are to be bonded; c. positioning said ceramic blocks on said plastic film so as to approximate a single slab; d. beveling the adjoining surfaces of said ceramic blocks to fit said ceramic blocks into a single slab having approximately the same contour as said substrate surface; e. applying said ceramic adhesive in excess to two of said adjoining beveled ceramic block surfaces, squeezing said blocks together to form a 1/16 inch ceramic adhesive joint, and scraping off the excess; f. repeating step 5 until all of said ceramic blocks are joined together into a single slab; g. placing the substrate-plastic film-ceramic slab assembly into a vacuum bag, applying vacuum pressure, and curing for 16 hours at room temperature and 3 hours at 150° F; h. removing said assembly from said vacuum bag and separating said ceramic slab, plastic film, and substrate; i. cleaning the ceramic slab surface which is to be bonded to said substrate, lightly sanding said ceramic slab surface and wiping off the resulting dust; j. cleaning and wiping with solvent said substrate surface; k. applying thixotropic polyimide adhesive to said ceramic slab surface, working said thixotropic polyimide adhesive into the pores of said ceramic slab surface, scraping off the excess, and curing for 2 hours at room temperature, 1 hour at 15° F, 1 hour at 350° F, and 1/2 hour at 400° F; l. applying a thin film of said thixotropic polyimide adhesive to said substrate surface and curing as in step k; m. applying at least one layer of said thixotropic polyimide adhesive to said substrate surface; n. positioning said ceramic slab on said polyimide substrate in the same relation as in step d; o. placing said polyimide substrate with said ceramic slab in said position into a vacuum bag and curing at 26 inches Hg pressure for 1/2 hour at 200° F, 1/2 hour at 250° F, 1/2 hour at 300° F, and 1 hour at 400° F; p. post-curing the product of step o in a restraining press for 1/2 hour at 400° F, 1 hour at 500° F, 2 hours at 600° F, 1 hour at 650° F, and 1 hour at 700° F, and cooling to room temperature in said press.

Claim 5

In the process of making a heat-resistant radar absorber, the process of bonding formed ceramic blocks to a polyimide RAM substrate, comprising the steps of: a. hand-mixing a ceramic adhesive consisting of 63% by weight of a mixed oxide powder (SiO 2 , ZrO 2 ), 33% by weight of a 30% solution of sodium silicate, and 4% by weight of Kaowool fibers; b. covering with a removable plastic film the polyimide substrate surface to which said ceramic blocks are to be bonded; c. positioning said ceramic blocks on said plastic film so as to approximate a single slab; d. beveling the adjoining surfaces of said ceramic blocks to fit said ceramic blocks into a single slab having approximately the same contour as said substrate surface; e. applying said ceramic adhesive in excess to two of said adjoining beveled ceramic block surfaces, squeezing said blocks together to form a 1/16 inch ceramic adhesive joint, and scraping off the excess; f. repeating step 5 until all of said ceramic blocks are joined together into a single slab; g. placing the substrate-plastic film-ceramic slab assembly into a vacuum bag, applying vacuum pressure, and curing for 16 hours at room temperature and 3 hours at 150° F; h. removing said assembly from said vacuum bag and separating said ceramic slab, plastic film, and substrate; i. cleaning the ceramic slab surface which is to be bonded to said substrate, lightly sanding said ceramic slab surface and wiping off the resulting dust; j. cleaning and wiping with solvent said substrate surface; k. applying thixotropic polyimide adhesive to said ceramic slab surface, working said thixotropic polyimide adhesive into the pores of said ceramic slab surface, scraping off the excess, and curing for 2 hours at room temperature, 1 hour at 15° F, 1 hour at 350° F, and 1/2 hour at 400° F; l. applying a thin film of said thixotropic polyimide adhesive to said substrate surface and curing as in step k; m. applying at least one layer of said thixotropic polyimide adhesive to said substrate surface; n. positioning said ceramic slab on said polyimide substrate in the same relation as in step d; o. placing said polyimide substrate with said ceramic slab in said position into a vacuum bag and curing at 26 inches Hg pressure for 1/2 hour at 200° F, 1/2 hour at 250° F, 1/2 hour at 300° F, and 1 hour at 400° F; p. post-curing the product of step o in a restraining press for 1/2 hour at 400° F, 1 hour at 500° F, 2 hours at 600° F, 1 hour at 650° F, and 1 hour at 700° F, and cooling to room temperature in said press.