Composition board with improved polymeric skin

Claim 2

A process for preparing a nonfrangible sheet material suitable for use as a surface covering, which process consists essentially of: a. providing a single, thin, cellulosic, fibrous sheet material adapted for use as a face sheet material, the material impregnated throughout its depth with from about 20 to 70% by weight of a curable, thermosetting resin, and having a basis weight of from about 15 to 180 gsm; b. applying onto one surface of the resin-impregnated sheet material a layer of an adhesive material compatible with the curable resin; and c. subjecting the curable resin-impregnated adhesive sheet material to high pressures of over about 20 kilos per centimeter square at a resin-curing temperature for a period of time to force and impregnate the adhesive material from the one surface into the sheet material during the high-pressure curing-resin cycle, the amount of adhesive material and its depth of impregnation sufficient to provide a nonfrangible thin sheet material characterized by a nonporous, cured, resin-rich, face surface free of adhesive, and an impregnated adhesive-rich back surface, the sheet material being flexible and capable of being handled without fracture thereof.

Claim 3

A process for preparing a composition board, which process comprises bonding the adhesive-rich surface of the non-frangible sheet material produced by the process of claim 1 without sanding thereof to at least one surface of a composition board.

Claim 4

The process of claim 2 wherein the composition board is a particle board having a surface variation of up to about ± 0.3 mm.

Claim 5

The process of claim 2 wherein the adhesive is polyvinyl-acetate resin and the resin is a melamine-formaldehyde resin.

Claim 6

The process of claim 2 wherein the board surface is coated prior to bonding with a coating layer of an adhesive, and the bonding is carried out at low contact pressure.

Claim 7

The process of claim 5 wherein the coating of the adhesive on the substrate is a polyvinyl-acetate resin, urea-formaldehyde resin or a combination thereof.

Claim 8

The process of claim 1 wherein the thermosetting resin is a melamine-formaldehyde resin.

Claim 9

The process of claim 1 wherein the adhesive is a vinyl-acetate resin.

Claim 10

The process of claim 1 wherein the resin-impregnated coated sheet material is subject to a pressure of from about 30 to 100 k/cm 2 .

Claim 11

The process of claim 1 wherein the curing temperature is from about 115° to 180° C.

Claim 12

The process of claim 1 wherein the period of time for the heat cycle is from about 3 to 40 minutes.

Claim 13

The process of claim 1 wherein the adhesive is impregnated into the surface of the sheet material of up to 50% in depth.

Claim 14

The process of claim 1 which includes applying the adhesive material by coating a layer of from about 1 to 20 mils of the adhesive material onto the one surface.

Claim 15

The process of claim 1 which includes placing a plurality of the resin-impregnated adhesive sheet materials separated by release sheets into the cavity of a high-pressure mold, and subjecting the sheet materials to high-pressure and resin-curing temperatures in the mold.

Claim 16

The process of claim 1 wherein the fibrous sheet material includes a top transparent sheet material and an underlying printed sheet material.

Claim 17

The process of claim 1 wherein the alpha cellulosic sheet material is a transparent or translucent sheet material.

Claim 18

The process of claim 1 wherein the adhesive material is forced into the sheet material from 10 up to about 40% in depth.

Claim 19

The process of claim 1 which includes coating a layer of an aqueous emulsion or solution of polyvinyl-acetate resin adhesive onto the one surface, and drying the coated layer to remove water or solvents prior to the high-pressure curing of the resin-impregnated dried adhesive sheet material.

Claim 20

The process of claim 1 wherein the sheet material is an alpha cellulosic sheet material having a thickness of from about 0.1 to 0.3 mm.

Claim 21

The process of claim 1 wherein the sheet material is an alpha cellulosic sheet, the resin is a melamine-formaldehyde resin and the adhesive material is polyvinyl-acetate resin.

Claim 22

A process for preparing a non-frangible sheet material suitable for use as a surface covering, which process consists essentially of: a. providing a thin, alpha cellulosic, fibrous sheet material, adapted for use as a face material, and having a basis weight of about 35 to 200 gsm and a thickness of from about 0.1 to 0.3 mm, impregnated throughout its depth with from about 20 to 70%, by weight of a heat-curable, melamine-formaldehyde thermosetting resin; b. applying onto one surface of the resin-impregnated sheet material a layer of a vinyl-acetate adhesive resin material; and c. subjecting the curable resin-impregnated adhesive-coated sheet material to high pressures of from about 30 to 100 kilos per centimeter square at a resin-curing temperature of from about 95° to 150° C for a heat cycle time from about 3 to 40 minutes, to force and impregnate the adhesive material from the one surface into the sheet material during the high-pressure curing-resin cycle, to provide a thin sheet material characterized by a nonporous, cured, resin-rich, face surface free of adhesive, and an adhesive-rich back surface, the vinyl acetate present in a depth of up to 50% of the sheet material, the sheet material being flexible and capable of being handled without fracture thereof, and the adhesive-rich surface adapted to be bonded to a substrate without sanding.

Claim 23

A process for preparing a non-frangible sheet material suitable for use as a surface covering, which process consists essentially of: a. providing a thin, alpha cellulosic, fibrous sheet material, adapted for use as a face material, and having a basis weight of about 35 to 200 gsm and a thickness of from about 0.1 to 0.3 mm, impregnated throughout its depth with from about 20 to 70%, by weight of a heat-curable, melamine-formaldehyde thermosetting resin; b. applying onto one surface of the resin-impregnated sheet material a layer of a vinyl-acetate adhesive resin material; and c. subjecting the curable resin-impregnated adhesive-coated sheet material to high pressures of from about 30 to 100 kilos per centimeter square at a resin-curing temperature of from about 95° to 150° C for a heat cycle time from about 3 to 40 minutes, to force and impregnate the adhesive material from the one surface into the sheet material during the high-pressure curing-resin cycle, to provide a thin sheet material characterized by a nonporous, cured, resin-rich, face surface free of adhesive, and an adhesive-rich back surface, the vinyl acetate present in a depth of up to 50% of the sheet material, the sheet material being flexible and capable of being handled without fracture thereof, and the adhesive-rich surface adapted to be bonded to a substrate without sanding.