Catalyst carrier, its method of preparation and a reforming catalyst supported on the carrier
Assignee: Chevron USA Inc
•
Filing: 1976-08-23
•
Granted: 1978-04-04
•
Expires: 1996-08-23
Abstract
Abstract A method is provided for preparing a porous catalyst carrier having a pore volume of at least 0.5 cc/g, a content of micropores in which the pore diameter is between 80 and 150 A. which constitutes at least 70% of the pore volume and a content of macropores which constitutes less than 3% of the pore volume. In the method, a powdered solid comprised of predominantly alpha-alumina monohydrate and sized in the range below 500 microns is treated with a particular amount of a monobasic acid. The acid in the resulting mixture is then at least partially neutralized by admixing with a nitrogen base such as aqueous ammonia. The treated and neutralized feed is converted into a novel catalyst carrier by shaping as desired, drying, and calcining. Further aspects of the invention are a catalytic reforming catalyst containing the present carrier.
Inventors
- 👤 Paul W. Tamm
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 22:59
CPC Classifications
B; B01; B01J; B01J21/00; B01J21/02; B01J21/04; B01J23/00; B01J23/70; B01J23/76; B01J23/84; B01J23/85; B01J23/88; B01J27/00; B01J27/14; B01J27/186; B01J27/188; B01J27/19; B01J35/00; B01J35/60; B01J37/00; B01J37/0009; B01J35/63; B01J35/635; B01J35/66; C; C10; C10G; C10G2300/00; C10G2300/10; C10G2300/107
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
282 words
A method for preparing a porous catalyst carrier which comprises: (a) treating a peptizable particulate solid comprising predominantly alpha-alumina monohydrate sized in the range below about 500 microns by admixing the solid with an aqueous solution of at least one acid selected from the group consisting of nitric, hydrochloric, hydrofluoric and hydrobromic acids, said solution containing an amount of the acid in the range from about 0.02 ot 0.20 equivalent per formula weight of the alumina; (b) neutralizing at least a portion of the admixed acid by admixing into the treated solid an aqueous solution of a nitrogen base selected from the group of the formula R 3 N and the corresponding hydroxide R 3 HNOH, wherein said R groups are the same or different and are selected from the group consisting of hydrogen and of alkyl groups having a carbon atom content in the range from 1 to 3, inclusive, said solution containing an amount of the base in the range from about 0.1 to 1.2 equivalents per equivalent of said acid; (c) shaping the neutralized or partially neutralized solid; and (d) drying and calcining the shaped solid in a dry or humid atmosphere at a temperature in the range from about 150° to 1700° F, said dried and calcined carrier having (1) a pore volume of at least 0.5 cc/g, (2) a content of micropores in the range between about 80 and 150 A in diameter constituting at least 70% of said pore volume, and (3) a content of pores having a diameter greater than 1000 A constituting from about 0.1 to less than 3% of said pore volume, said pore-sizes corresponding to sizes determined by the mercury porosimetry method.
Claim 2
Independent Claim
282 words
A method for preparing a porous catalyst carrier which comprises: (a) treating a peptizable particulate solid comprising predominantly alpha-alumina monohydrate sized in the range below about 500 microns by admixing the solid with an aqueous solution of at least one acid selected from the group consisting of nitric, hydrochloric, hydrofluoric and hydrobromic acids, said solution containing an amount of the acid in the range from about 0.02 ot 0.20 equivalent per formula weight of the alumina; (b) neutralizing at least a portion of the admixed acid by admixing into the treated solid an aqueous solution of a nitrogen base selected from the group of the formula R 3 N and the corresponding hydroxide R 3 HNOH, wherein said R groups are the same or different and are selected from the group consisting of hydrogen and of alkyl groups having a carbon atom content in the range from 1 to 3, inclusive, said solution containing an amount of the base in the range from about 0.1 to 1.2 equivalents per equivalent of said acid; (c) shaping the neutralized or partially neutralized solid; and (d) drying and calcining the shaped solid in a dry or humid atmosphere at a temperature in the range from about 150° to 1700° F, said dried and calcined carrier having (1) a pore volume of at least 0.5 cc/g, (2) a content of micropores in the range between about 80 and 150 A in diameter constituting at least 70% of said pore volume, and (3) a content of pores having a diameter greater than 1000 A constituting from about 0.1 to less than 3% of said pore volume, said pore-sizes corresponding to sizes determined by the mercury porosimetry method.
Claim 3
Dependent Claim
64 words
A method in accordance with claim 1 wherein said particulate solid is sized in the range below about 150 microns, said acid is nitric acid which is admixed in an amount in the range from about 0.03 to 0.10 equivalent per formula weight of alumina, said base is aqueous ammonia, and said resulting carrier has a pore volume of at least about 0.65 cc/g.
Claim 4
Dependent Claim
38 words
A method in accordance with claim 2 wherein said neutralized or partially neutralized solid has a volatiles content in the range from about 50 to about 70 weight percent, and said shaping is effected by extruding the solid.
Claim 5
Dependent Claim
16 words
A method in accordance with claim 2 wherein said particulate solid consists essentially of alpha-alumina monohydrate.
Claim 6
Dependent Claim
43 words
A method in accordance with claim 1 wherein the resulting carrier has a pore volume of at least 0.5 cc/g in which at least 80% of the pore volume constitutes pores having a pore diameter in the range between 100 and 140 A.
Claim 7
Dependent Claim
32 words
A method in accordance with claim 5 wherein less than about 1.0 volume percent of the pore volume of the resulting carrier constitutes pores having a pore diameter greater than 1000 A.
Claim 8
Dependent Claim
11 words
A predominantly alumina carrier prepared by the method of claim 1.
Claim 9
Dependent Claim
11 words
A predominantly alumina carrier prepared by the method of claim 5.
Claim 10
Dependent Claim
168 words
A catalytic reforming catalyst composition comprising a carrier component and a catalytic component, said carrier component comprising predominantly alumina having (1) a pore volume of at least 0.65 cc/g, (2) a content of micropores sized in the range between 80 and 150 A in diameter constituting at least 70% of said pore volume and (3) a content of pores having a diameter greater than 1000 A constituting from about 0.1 to 3% of said pore volume, said pore-sizes corresponding to sizes determined by the mercury porosimetry method; said catalytic component being at least one Group VIII noble metal promoted and/or stabilized by at least one material selected from the metals, oxides and halides of the group of elements consisting of rhenium, manganese, germanium, tin, zinc and titanium; said composition containing on a dry basis and calculated as metal, in addition to said alumina, an amount in the range from about 0.1 to 3 weight percent of said noble metal, and an amount in said range of said promoter.
Claim 11
Dependent Claim
168 words
A catalytic reforming catalyst composition comprising a carrier component and a catalytic component, said carrier component comprising predominantly alumina having (1) a pore volume of at least 0.65 cc/g, (2) a content of micropores sized in the range between 80 and 150 A in diameter constituting at least 70% of said pore volume and (3) a content of pores having a diameter greater than 1000 A constituting from about 0.1 to 3% of said pore volume, said pore-sizes corresponding to sizes determined by the mercury porosimetry method; said catalytic component being at least one Group VIII noble metal promoted and/or stabilized by at least one material selected from the metals, oxides and halides of the group of elements consisting of rhenium, manganese, germanium, tin, zinc and titanium; said composition containing on a dry basis and calculated as metal, in addition to said alumina, an amount in the range from about 0.1 to 3 weight percent of said noble metal, and an amount in said range of said promoter.
Claim 12
Dependent Claim
21 words
A composition as in claim 9 further characterized in that said micropores are sized in the range 100 to 140 A.
Claim 13
Dependent Claim
26 words
A composition as in claim 10 further characterized in that said carrier consists essentially of alumina, said noble metal is platinum and said promoter is rhenium.
Claim 14
Dependent Claim
91 words
A catalyst carrier suitable for use in preparing an improved catalytic hydrocarbon reforming catalyst, said carrier consisting essentially of alumina having (1) a pore volume of at least 0.5 cc/g, (2) a content of micropores sized in the diameter range between 80 and 150 A. constituting at least 70% of said pore volume, and (3) a content of pores sized in the diameter range above 1000 A. constituting at least 0.1 and less than 3% of said pore volume, said pore sizes corresponding to sizes determined by the mercury porosimetry method.
Claim 15
Dependent Claim
91 words
A catalyst carrier suitable for use in preparing an improved catalytic hydrocarbon reforming catalyst, said carrier consisting essentially of alumina having (1) a pore volume of at least 0.5 cc/g, (2) a content of micropores sized in the diameter range between 80 and 150 A. constituting at least 70% of said pore volume, and (3) a content of pores sized in the diameter range above 1000 A. constituting at least 0.1 and less than 3% of said pore volume, said pore sizes corresponding to sizes determined by the mercury porosimetry method.
Claim 16
Dependent Claim
21 words
A carrier as in claim 12 further characterized in that said micropores are sized in the 100 to 140 A. range.
Claim 17
Dependent Claim
22 words
A method as in claim 3 wherein said volatiles content is in the range of from about 55 to 65 weight percent.
Claim 18
Dependent Claim
17 words
A carrier as in claim 12 wherein said content of said micropores is at least 85 percent.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-04-03 | 1981-10-03 | 1982-04-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-04-03 | 1985-10-03 | 1986-04-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-04-03 | 1989-10-03 | 1990-04-04 | $7700.00 | Window Closed / Lapsed |