US4081315A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Cermet etch technique
Assignee: TRW LSI Products Inc
•
Filing: 1976-05-25
•
Granted: 1978-03-28
•
Expires: 1996-05-25
Abstract
Abstract An etching process for patterning cermet thin film resistors includes the provision of a layer of molybdenum over the cermet layer to provide a good adherent surface for a photoresist layer subsequently deposited thereon. After the photoresist and molybdenum layers are patterned in separate steps, the cermet is preferentially etched with hot phosphoric acid to produce the desired cermet resistance pattern.
Inventors
- 👤 Alan S. Templin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 14:06
CPC Classifications
H; H10; H10D; H10D1/00; H10D1/40; H10D1/47; H10D1/474; C; C23; C23F; C23F1/00; C23F1/10; C23F1/14; C23F1/16; C23F1/26; H01; H01C; H01C17/00; H01C17/06; H10P; H10P50/00; H10P50/60; H10P50/66; H10P50/663; H10P50/667; Y; Y10; Y10S; Y10S438/00; Y10S438/942; Y10S438/945
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
84 words
The method of manufacturing thin film cermet resistance patterns, on a dielectric substrate, comprising the steps of: (a) forming on said substrate a layer of cermet comprising primarily a resistive compound of silicon and chromium; (b) forming a masking layer over said cermet layer so as to expose selected areas of said cermet layer; and (c) etching away the cermet at said selected areas by subjecting said areas to an etchant comprising primarily phosphoric acid at a temperature of the order of 180° C.
Claim 2
Independent Claim
84 words
The method of manufacturing thin film cermet resistance patterns, on a dielectric substrate, comprising the steps of: (a) forming on said substrate a layer of cermet comprising primarily a resistive compound of silicon and chromium; (b) forming a masking layer over said cermet layer so as to expose selected areas of said cermet layer; and (c) etching away the cermet at said selected areas by subjecting said areas to an etchant comprising primarily phosphoric acid at a temperature of the order of 180° C.
Claim 3
Dependent Claim
79 words
In a method of manufacturing thin film resistors involving the deposition on a dielectric substrate of a layer comprising primarily a compound of silicon and chromium and subsequent removal of selected portions of said layer to form a predetermined cermet resistor pattern, the improvement comprising: subjecting said selected portions to phosphoric acid at a temperature of about 180° C for a time sufficient to chemically remove said selected portions and expose the underlying substrate without substantially eroding said substrate.
Claim 4
Dependent Claim
79 words
In a method of manufacturing thin film resistors involving the deposition on a dielectric substrate of a layer comprising primarily a compound of silicon and chromium and subsequent removal of selected portions of said layer to form a predetermined cermet resistor pattern, the improvement comprising: subjecting said selected portions to phosphoric acid at a temperature of about 180° C for a time sufficient to chemically remove said selected portions and expose the underlying substrate without substantially eroding said substrate.
Claim 5
Independent Claim
91 words
A method of forming thin film resistive elements on a dielectric substrate comprising: (a) depositing a layer of cermet material comprising primarily compounds of silicon and chromium on said substrate; (b) depositing a masking member on said cermet layer so as to expose selected areas of said cermet layer corresponding to a desired pattern; and (c) subjecting the exposed areas of said cermet layer to phosphoric acid at a temperature of about 180° C for a sufficient time to chemically remove said exposed cermet layer areas without removing the masked areas.
Claim 6
Independent Claim
91 words
A method of forming thin film resistive elements on a dielectric substrate comprising: (a) depositing a layer of cermet material comprising primarily compounds of silicon and chromium on said substrate; (b) depositing a masking member on said cermet layer so as to expose selected areas of said cermet layer corresponding to a desired pattern; and (c) subjecting the exposed areas of said cermet layer to phosphoric acid at a temperature of about 180° C for a sufficient time to chemically remove said exposed cermet layer areas without removing the masked areas.
Claim 7
Dependent Claim
23 words
The invention according to claim 3 wherein said masking member includes a layer of material that is chemically resistant to hot phosphoric acid.
Claim 8
Dependent Claim
20 words
The invention according to claim 3 wherein said phosphoric acid is maintained gently boiling at about 175° to 180° C.
Claim 9
Dependent Claim
15 words
The invention according to claim 4 wherein said masking member includes a layer of molybdenum.
Claim 10
Dependent Claim
21 words
The invention according to claim 4 wherein said masking member includes a layer of molybdenum followed by a layer of photoresist.
Claim 11
Dependent Claim
21 words
The invention according to claim 3 wherein said cermet layer is formed by depositing a mixture of silicon monoxide and chromium.
Claim 12
Dependent Claim
20 words
The invention according to claim 8 wherein said mixture includes 35 to 50% silicon monoxide and 65 to 50% chromium.
Claim 13
Dependent Claim
21 words
The invention according to claim 3 wherein said cermet layer has a thickness in the range of 50 to 10,000 angstroms.
Claim 14
Independent Claim
115 words
A method of forming thin film resistive elements on a dielectric substrate, comprising: (a) forming on said substrate, a layer of cermet material comprising primarily resistive compounds of silicon and chromimum; (b) depositing a layer of molybdenum on said cermet layer; (c) forming a layer of photoresist material on said molybdenum layer according to a desired pattern including voids in the photoresist layer that expose portions of said molybdenum layer; (d) etching the exposed portions of said molybdenum layer to remove the same and to expose the underlying portions of said cermet layer; and (e) etching the exposed portions of said cermet layer with phosphoric acid at a temperature of the order of 180° C.
Claim 15
Independent Claim
115 words
A method of forming thin film resistive elements on a dielectric substrate, comprising: (a) forming on said substrate, a layer of cermet material comprising primarily resistive compounds of silicon and chromimum; (b) depositing a layer of molybdenum on said cermet layer; (c) forming a layer of photoresist material on said molybdenum layer according to a desired pattern including voids in the photoresist layer that expose portions of said molybdenum layer; (d) etching the exposed portions of said molybdenum layer to remove the same and to expose the underlying portions of said cermet layer; and (e) etching the exposed portions of said cermet layer with phosphoric acid at a temperature of the order of 180° C.
Claim 16
Dependent Claim
17 words
The invention according to claim 11, and further including removing said photoresist pattern prior to step (e).
Claim 17
Dependent Claim
19 words
The invention according to claim 11, and further including step (f) removing said photoresist pattern subsequent to step (e).
Claim 18
Dependent Claim
28 words
The invention according to claim 12 and further including, following step (e), removing the remainder of said molybdenum layer to leave remaining the desired pattern of cermet material.
Claim 19
Dependent Claim
28 words
The invention according to claim 13 and further including, following step (f), removing the remainder of said molybdenum layer to leave remaining the desired pattern of cermet material.
Claim 20
Dependent Claim
23 words
The invention according to claim 11, wherein during step (e) said phosphoric acid is maintained gently boiling at about 175° to 180° C.
Claim 21
Dependent Claim
19 words
The invention according to claim 16, wherein said phosphoric acid is present with a small quantity of sulphuric acid.
Claim 22
Dependent Claim
22 words
The invention according to claim 17, wherein the ratio of phosphoric acid to sulphuric acid is about 10 to 1 by volume.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-03-27 | 1981-09-26 | 1982-03-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-03-27 | 1985-09-26 | 1986-03-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-03-27 | 1989-09-26 | 1990-03-28 | $7700.00 | Window Closed / Lapsed |