US4080317A
Expired / Lapsed
US
⏱️ 0.0 years remaining
High molecular weight polycondensates from solid phase condensation
Assignee: Novartis AG
•
Filing: 1975-11-26
•
Granted: 1978-03-21
•
Expires: 1995-11-26
Abstract
Abstract Polyester precondensates are catalytically polycondensed in solid phase at a constant temperature with a linear increase (during polycondensation) in intrinsic viscosity. The linear increase makes possible an accurate advance determination of reaction time required to produce thermoplastic polycondensate of the desired intrinsic viscosity.
Inventors
- 👤 Gottfried Morawetz
- 👤 Lothar Buxbaum
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 19:53
CPC Classifications
C; C08; C08G; C08G63/00; C08G63/78; C08G63/80; C08G63/82
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
162 words
A process for solid-phase polycondensation of an intimate admixture of a catalytic amount of polyester-polycondensation catalyst with polyester precondensate, which has a. a maximum degree of crystallinity of 66.5 percent and b. a maximum moisture content of 0.02 percent by weight, under solid-phase polycondensation conditions which comprise an essentially constant temperature of from 5° to 50° C below the melting point of said precondensate and under vacuum, under streaming inert gas or under vacuum and streaming inert gas, the process being characterized by polycondensing said intimate admixture, having a maximum carboxylic acid value of 1.4 equivalents per gram mol, for a period sufficient to yield, at an essentially constant rate of increasing viscosity, a high-molecular-weight polycondensate having an intrinsic viscosity between 0.90 and 1.80 dl/g and a degree of crystallinity of at most 80 percent, the polyester-polycondensation catalyst being catalytic means for limiting the degree of crystallinity of the high-molecular-weight polycondensate produced under the solid-phase polycondensation conditions to at most 80 percent.
Claim 2
Dependent Claim
162 words
A process for solid-phase polycondensation of an intimate admixture of a catalytic amount of polyester-polycondensation catalyst with polyester precondensate, which has a. a maximum degree of crystallinity of 66.5 percent and b. a maximum moisture content of 0.02 percent by weight, under solid-phase polycondensation conditions which comprise an essentially constant temperature of from 5° to 50° C below the melting point of said precondensate and under vacuum, under streaming inert gas or under vacuum and streaming inert gas, the process being characterized by polycondensing said intimate admixture, having a maximum carboxylic acid value of 1.4 equivalents per gram mol, for a period sufficient to yield, at an essentially constant rate of increasing viscosity, a high-molecular-weight polycondensate having an intrinsic viscosity between 0.90 and 1.80 dl/g and a degree of crystallinity of at most 80 percent, the polyester-polycondensation catalyst being catalytic means for limiting the degree of crystallinity of the high-molecular-weight polycondensate produced under the solid-phase polycondensation conditions to at most 80 percent.
Claim 3
Dependent Claim
17 words
A process according to claim 1 wherein the polyester precondensate has from 20 to 66.5 percent crystallinity.
Claim 4
Dependent Claim
91 words
A process according to claim 1 wherein the catalytic amount is from 0.001 to 2 percent by weight and the polyester-polycondensation catalyst is a member selected from the group consisting of a. antimony, lead and calcium, b. antimony, lead and zinc, c. antimony, lead and manganese, d. antimony, lead, calcium and manganese, e. antimony, lead, calcium and zinc, f. antimony and zinc, g. antimony, lead and lithium, h. antimony and manganese, i. titanium and calcium, j. polymeric germanium hydride and calcium, k. polymeric germanium hydride and zinc, and l. potassium germanide.
Claim 5
Dependent Claim
24 words
A process according to claim 3 wherein the rate of increasing viscosity at a polymerisation temperature of 235° C is at least 0.010 dl/gh.
Claim 6
Dependent Claim
42 words
A process according to claim 3 wherein the precondensate is a granuled polycondensate which has a degree of crystallinity between 33 and 58 percent, an intrinsic viscosity between 0.60 and 0.80 dl/g and a carboxylic acid value of at most 1.2 val/mol.
Claim 7
Dependent Claim
59 words
A process according to claim 3 wherein the catalyst comprises antimony, lead and calcium, the amount of antimony is up to 0.05 percent by weight, the amount of lead is up to 0.02 percent by weight and the amount of calcium is from 0.005 to 0.1 percent by weight, the percentages by weight being based on the precondensate weight.
Claim 8
Dependent Claim
16 words
A process according to claim 3 wherein polycondensing is effected in vacuo and streaming inert gas.
Claim 9
Dependent Claim
43 words
A process according to claim 3 wherein polycondensing is effected in a vacuum of from 0.01 to 1 torr and at a positive streaming rate of the inert gas of less than 2 liters per hour and per kg of solid phase condensate.
Claim 10
Dependent Claim
45 words
A process according to claim 3 wherein the polycondensate is an acid/diol reaction product, at least 85 mol percent of acid radicals of which are those of terephthalic acid and at least 85 mol percent of diol radicals of which are those of ethylene glycol.
Claim 11
Dependent Claim
7 words
A batch process according to claim 1.
Claim 12
Dependent Claim
59 words
A process which comprises removing surface moisture from quenched crystalline polyester precondensate at a temperature below 80° C over a period of several hours, then drying the resulting precondensate for several hours in vacuo at increased temperature of a residual moisture content below 0.02 percent by weight and subsequently solid-phase polycondensing thus predried polyester precondensate according to claim 1.
Claim 13
Dependent Claim
128 words
A solid-phase process which comprises catalytically polycondensing crystalline polyester precondensate at an essentially constant temperature and at an essentially constant rate of increasing viscosity for a period sufficient to yield a high-molecular-weight thermoplastic polycondensate having an intrinsic viscosity between 0.90 and 1.80 dl/g and a degree of crystallinity of at most 80 percent, and polyester precondensate having: a. a maximum carboxylic acid value of 1.4 equivalents per gram mol, b. a maximum degree of crystallinity of 66.5 percent and c. a maximum moisture content of 0.02 percent by weight, and being in intimate admixture with a catalytic amount of polyester-polycondensation catalyst, the polyester-polycondensation catalyst being catalytic means for limiting the degree of crystallinity of the high-molecular-weight polycondensate produced under the solid-phase polycondensation conditions to at most 80 percent.
Claim 14
Dependent Claim
128 words
A solid-phase process which comprises catalytically polycondensing crystalline polyester precondensate at an essentially constant temperature and at an essentially constant rate of increasing viscosity for a period sufficient to yield a high-molecular-weight thermoplastic polycondensate having an intrinsic viscosity between 0.90 and 1.80 dl/g and a degree of crystallinity of at most 80 percent, and polyester precondensate having: a. a maximum carboxylic acid value of 1.4 equivalents per gram mol, b. a maximum degree of crystallinity of 66.5 percent and c. a maximum moisture content of 0.02 percent by weight, and being in intimate admixture with a catalytic amount of polyester-polycondensation catalyst, the polyester-polycondensation catalyst being catalytic means for limiting the degree of crystallinity of the high-molecular-weight polycondensate produced under the solid-phase polycondensation conditions to at most 80 percent.
Claim 15
Dependent Claim
54 words
A process according to claim 12 which comprises determining the rate of intrinsic-viscosity increase, which is a straight line function, during solid-phase polycondensation and terminating the solid-phase polycondensation at a time which is based upon the rate of intrinsic-viscosity increase and the intrinsic viscosity which corresponds to the high-molecular weight of said high-molecular-weight polycondensate.
References Cited (Backward Citations)
US2921052A
Cited
US2901466A
Cited
US3405098A
Cited
NL6807708A
Cited
US3544525A
Cited
US3551386A
Cited
US3657388A
Cited
US3544523A
Cited
US3816377A
Cited
US3801547A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-03-20 | 1981-09-19 | 1982-03-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-03-20 | 1985-09-19 | 1986-03-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-03-20 | 1989-09-19 | 1990-03-21 | $7700.00 | Window Closed / Lapsed |