Abstract
Abstract A high current density long life cathode for use in high power microwave e applications is made by: machining a porous tungsten pellet with copper in its pores to the desired cathode shape to form the emitting surface of the cathode and cleaning the porous pellet ultrasonically in trichloroethylene, then acetone, and then methanol; firing the tungsten pellet at about 1800° C in a reducing atmosphere; etching the tungsten pellet ultrasonically in a solution of 50 parts of concentrated nitric acid in 50 parts of water; ultrasonically cleaning the tungsten pellet for about five minutes in an aqueous alkaline solution; cleaning the tungsten pellet in hot deionized water and then air drying the tungsten pellet in an oven for five minutes at about 150° C; refiring the tungsten pellet in a reducing atmosphere at about 1800° C; impregnating the porous tungsten pellet with a mixture of Ba 3 WO 6 , Ba 2 SrWO 6 and ZrH 2 in a nonreducing, nonoxidizing atmosphere at about 1900° C to 2000° C; and firing the impregnated tungsten pellet in a reducing atmosphere of dry hydrogen at about 1840° C for about 2 to 5 minutes.
Inventors
- 👤 Bernard Smith
- 👤 Albert F. Newman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 20:15
CPC Classifications
H; H01; H01J; H01J23/00; H01J23/02; H01J23/04; H01J9/00; H01J9/02; H01J9/04
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
214 words
Method of making a high current density long life cathode for use in high power microwave tube applications said method including the steps of: (a) machining a porous tungsten pellet having a porosity ranging from about 11 percent to about 28 percent with copper in its pores to the desired cathode shape to form the emitting surface of the cathode and cleaning the porous pellet ultrasonically in trichloroethylene, then acetone, and then methanol, (b) firing the tungsten pellet at about 1800° C in a reducing atmosphere, (c) etching the tungsten pellet ultrasonically in a solution of 50 parts of concentrated nitric acid in 50 parts of water, (d) ultrasonically cleaning the tungsten pellet for about five minutes in an aqueous alkaline solution, (e) cleaning the tungsten pellet in hot water and then air drying the tungsten pellet in an oven for five minutes at about 150° F, (f) refiring the tungsten pellet in a reducing atmosphere at about 1800° C, (g) impregnating the porous tungsten pellet with a mixture of Ba 3 WO 6 , Ba 2 SrWO 6 and ZrH 2 in a nonreducing, nonoxidizing atmosphere at about 1900° C to 2000° C, and (h) firing the tungsten pellet in a reducing atmosphere at about 1840° C for about 2 to 5 minutes.
Claim 2
Dependent Claim
214 words
Method of making a high current density long life cathode for use in high power microwave tube applications said method including the steps of: (a) machining a porous tungsten pellet having a porosity ranging from about 11 percent to about 28 percent with copper in its pores to the desired cathode shape to form the emitting surface of the cathode and cleaning the porous pellet ultrasonically in trichloroethylene, then acetone, and then methanol, (b) firing the tungsten pellet at about 1800° C in a reducing atmosphere, (c) etching the tungsten pellet ultrasonically in a solution of 50 parts of concentrated nitric acid in 50 parts of water, (d) ultrasonically cleaning the tungsten pellet for about five minutes in an aqueous alkaline solution, (e) cleaning the tungsten pellet in hot water and then air drying the tungsten pellet in an oven for five minutes at about 150° F, (f) refiring the tungsten pellet in a reducing atmosphere at about 1800° C, (g) impregnating the porous tungsten pellet with a mixture of Ba 3 WO 6 , Ba 2 SrWO 6 and ZrH 2 in a nonreducing, nonoxidizing atmosphere at about 1900° C to 2000° C, and (h) firing the tungsten pellet in a reducing atmosphere at about 1840° C for about 2 to 5 minutes.
Claim 3
Dependent Claim
18 words
Method according to claim 1 wherein the reducing atmosphere in steps (b), (f) and (h) is dry hydrogen.
Claim 4
Dependent Claim
15 words
Method according to claim 1 wherein the nonreducing, nonoxidizing atmosphere in step (g) is argon.
Claim 5
Dependent Claim
36 words
Method according to claim 1 wherein the mixture of Ba 3 WO 6 , Ba 2 SrWO 6 and ZrH 2 in step (g) is used in an amount to fully impregnate the porous tungsten pellet.
Claim 6
Dependent Claim
84 words
Method according to claim 1 wherein the porous tungsten pellet with copper in its pores in step (a) measures about 3.9 millimeters in diameter and about 2.5 millimeters in thickness and has a porosity of about 20 percent, and wherein the mixture of Ba 3 WO 6 , Ba 2 SrWO 6 and ZrH 2 in step (g) is in the ratio of about 4.5 grams of Ba 3 WO 6 and Ba 2 SrWO 6 to about 0.2 gram of ZrH 2 .
Claim 7
Dependent Claim
84 words
Method according to claim 2 wherein the porous tungsten pellet with copper in its pores in step (a) measures about 3.9 millimeters in diameter and about 2.5 millimeters in thickness and has a porosity of about 20 percent, and wherein the mixture of Ba 3 WO 6 , Ba 2 SrWO 6 and ZrH 2 in step (g) is in the ratio of about 4.5 grams of Ba 3 WO 6 and Ba 2 SrWO 6 to about 0.2 gram of ZrH 2 .
Claim 8
Dependent Claim
84 words
Method according to claim 3 wherein the porous tungsten pellet with copper in its pores in step (a) measures about 3.9 millimeters in diameter and about 2.5 millimeters in thickness and has a porosity of about 20 percent, and wherein the mixture of Ba 3 WO 6 , Ba 2 SrWO 6 and ZrH 2 in step (g) is in the ratio of about 4.5 grams of Ba 3 WO 6 and Ba 2 SrWO 6 to about 0.2 gram of ZrH 2 .
References Cited (Backward Citations)
US3525135A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-03-13 | 1981-09-12 | 1982-03-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-03-13 | 1985-09-12 | 1986-03-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-03-13 | 1989-09-12 | 1990-03-14 | $7700.00 | Window Closed / Lapsed |