Non-stressed, high strength, cement-containing pipe and its production
Assignee: Cement Asbestos Products Co
•
Filing: 1976-02-04
•
Granted: 1978-03-07
•
Expires: 1996-02-04
Abstract
Abstract Non-stressed, high strength, substantially inflexible, rigid, cement-containing pipe, for example, asbestos-cement pipe well adapted as high pressure water pipe, comprising a tubular article body of spirally wound up layers of asbestos-cement, and a plurality of helical windings of a continuous filament of an aromatic polyamide fiber known and obtainable as KEVLAR aramid fiber about one or more of the asbestos-cement layers within the interior of the pipe without being stretched and without being in tension. The aromatic polyamide fiber of the continuous filament is of high tensile strength of about 390,000 psi or higher and a low elongation capability of no more than 7%, and the continuous filament of the belical windings is maintained about the cement-containing composition within the interior of the pipe without being stretched and without being in tension. Non-stressed, high strength concrete pipe is also embodied in the invention. The outer exposed main surface of the pipe is usually free or substantially free of the continuous filament.
Inventors
- 👤 James Wright
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 07:25
CPC Classifications
B; B28; B28B; B28B21/00; B28B21/56; B28B21/42; B28B21/48; B28B21/60; B28B21/62; F; F16; F16L; F16L9/00; F16L9/08; F16L9/14; F16L9/16
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
165 words
A method for producing non-stressed, reinforced, rigid, substantially inflexible, asbestos-cement pipe well adapted for conveying water under pressure which comprises forming a wet asbestos-cement sheet from an aqueous asbestos fiber-cement slurry, removing water from the wet asbestos-cement sheet, winding the de-watered, still wet sheet on a pipe-forming mandrel as a plurality of spirally wound, wet asbestos-cement layers thereon while applying pressure to the wet sheet on the mandrel, winding a continuous filament of an aromatic polyamide fiber taut about at least one of the spirally wound, wet asbestos-cement layers within the interior of the ultimate pipe on the mandrel during the winding of the wet asbestos-cement layers on the mandrel without stretching the continuous filament and substantially without placing the continuous filament in tension, the aromatic polyamide fiber of the continuous filament characterized by having high tensile strength and a low elongation capability, separating the mandrel from the inner surface of the thus-formed pipe, extracting the mandrel from within the pipe, and curing the pipe.
Claim 2
Independent Claim
165 words
A method for producing non-stressed, reinforced, rigid, substantially inflexible, asbestos-cement pipe well adapted for conveying water under pressure which comprises forming a wet asbestos-cement sheet from an aqueous asbestos fiber-cement slurry, removing water from the wet asbestos-cement sheet, winding the de-watered, still wet sheet on a pipe-forming mandrel as a plurality of spirally wound, wet asbestos-cement layers thereon while applying pressure to the wet sheet on the mandrel, winding a continuous filament of an aromatic polyamide fiber taut about at least one of the spirally wound, wet asbestos-cement layers within the interior of the ultimate pipe on the mandrel during the winding of the wet asbestos-cement layers on the mandrel without stretching the continuous filament and substantially without placing the continuous filament in tension, the aromatic polyamide fiber of the continuous filament characterized by having high tensile strength and a low elongation capability, separating the mandrel from the inner surface of the thus-formed pipe, extracting the mandrel from within the pipe, and curing the pipe.
Claim 3
Dependent Claim
30 words
The method of claim 1 wherein the pipe is pre-cured subsequent to separating the mandrel from the pipe inner surface and prior to extracting the mandrel from within the pipe.
Claim 4
Dependent Claim
13 words
The method of claim 2 wherein the asbestos fiber-cement slurry also contains silica.
Claim 5
Dependent Claim
25 words
The method of claim 3 wherein the fiber has tensile strength of at least about 390,000 psi and an elongation of no more than 7%.
Claim 6
Dependent Claim
29 words
The method of claim 4 wherein the fiber has tensile strength of about 400,000 psi to about 525,000 psi and an elongation capability of about 2 to about 4%.
Claim 7
Dependent Claim
19 words
The method of claim 5 wherein the fiber has tensile strength of about 520,000 psi to about 525,000 psi.
Claim 8
Dependent Claim
11 words
The method of claim 4 wherein the continuous filament is yarn.
Claim 9
Dependent Claim
11 words
The method of claim 5 wherein the continuous filament is yarn.
Claim 10
Dependent Claim
118 words
The method of claim 3 wherein the wet asbestos-cement sheet is formed by at least one rotating sieve cylinder partially immersed in the slurry, the sieve cylinder picking up the slurry as a water-laid, thin, wet asbestos-cement sheet on its sieve surface, water being removed from the wet asbestos-cement sheet on the sieve cylinder surace by being forced through the sieve openings of said sieve cylinder, the still wet asbestos-cement sheet being transferred from the rotating sieve cylinder onto a moving, continuous, water-permeable member and said asbestos-cement sheet being transported on the moving, permeable member to the pipe-forming mandrel for winding thereon while additional water is removed from the asbestos-cement sheet during its transport on the permeable member.
Claim 11
Dependent Claim
13 words
The method of claim 9 wherein the permeable member is a porous felt.
Claim 12
Dependent Claim
19 words
The method of claim 9 wherein the fiber has tensile strength of about 520,000 psi to about 525,000 psi.
Claim 13
Dependent Claim
13 words
The method of claim 11 wherein the permeable member is a porous felt.
Claim 14
Dependent Claim
26 words
The method of claim 3 wherein the continuous filament is helically wound about at least one of the asbestos-cement layers within the interior of the pipe.
Claim 15
Dependent Claim
13 words
The method of claim 13 wherein the asbestos fiber-cement slurry also contains silica.
Claim 16
Dependent Claim
11 words
The method of claim 14 wherein the continuous filament is yarn.
Claim 17
Dependent Claim
25 words
The method of claim 14 wherein the continuous filament is helically wound about each of a plurality of the asbestos-cement layers within the pipe interior.
Claim 18
Dependent Claim
28 words
The method of claim 14 wherein the continuous filament is helically wound about a central portion of one or more of the asbestos-cement layers within the pipe interior.
Claim 19
Dependent Claim
11 words
The method of claim 2 wherein the continuous filament is yarn.
Claim 20
Dependent Claim
11 words
The method of claim 3 wherein the continuous filament is yarn.
Claim 21
Independent Claim
165 words
A method for producing non-stressed, reinforced, rigid, substantially inflexible, asbestos-cement pipe well adapted for conveying water under pressure which comprises forming a wet asbestos-cement sheet from an aqueous asbestos fiber-cement slurry, removing water from the wet asbestos-cement sheet, winding the de-watered, still wet sheet on a pipe-forming mandrel as a plurality of convolutely wound, wet asbestos-cement layers thereon while applying pressure to the wet sheet on the mandrel, winding a continuous filament of an aromatic polyamide fiber taut about at least one of the convolutely wound, wet asbestos-cement layers within the interior of the ultimate pipe on the mandrel during the winding of the wet asbestos-cement layers on the mandrel without stretching the continuous filament and substantially without placing the continuous filament in tension, the aromatic polyamide fiber of the continuous filament characterized by having high tensile strength and a low elongation capability, separating the mandrel from the inner surface of the thus-formed pipe, extracting the mandrel from within the pipe, and curing the pipe.
Claim 22
Independent Claim
165 words
A method for producing non-stressed, reinforced, rigid, substantially inflexible, asbestos-cement pipe well adapted for conveying water under pressure which comprises forming a wet asbestos-cement sheet from an aqueous asbestos fiber-cement slurry, removing water from the wet asbestos-cement sheet, winding the de-watered, still wet sheet on a pipe-forming mandrel as a plurality of convolutely wound, wet asbestos-cement layers thereon while applying pressure to the wet sheet on the mandrel, winding a continuous filament of an aromatic polyamide fiber taut about at least one of the convolutely wound, wet asbestos-cement layers within the interior of the ultimate pipe on the mandrel during the winding of the wet asbestos-cement layers on the mandrel without stretching the continuous filament and substantially without placing the continuous filament in tension, the aromatic polyamide fiber of the continuous filament characterized by having high tensile strength and a low elongation capability, separating the mandrel from the inner surface of the thus-formed pipe, extracting the mandrel from within the pipe, and curing the pipe.
Claim 23
Independent Claim
140 words
A method for producing non-stressed, reinforced, rigid, substantially inflexible, asbestos-cement pipe well adapted for conveying water under pressure which comprises forming a wet asbestos-cement sheet from an aqueous asbestos fiber-cement slurry, removing water from the wet asbestos-cement sheet, applying the de-watered, still wet sheet on the surface of a pipe-forming mandrel, winding a continuous filament of an aromatic polyamide fiber about the wet asbestos-cement and within the interior of the ultimate pipe on the mandrel during the application of the wet asbestos-cement on the mandrel without stretching the continuous filament and substantially without placing the continuous filament in tension, the aromatic polyamide fiber of the continuous filament characterized by having high tensile strength and a low elongation capability, separating the mandrel from the inner surface of the thus-formed pipe, extracting the mandrel from within the pipe, and curing the pipe.
Claim 24
Independent Claim
140 words
A method for producing non-stressed, reinforced, rigid, substantially inflexible, asbestos-cement pipe well adapted for conveying water under pressure which comprises forming a wet asbestos-cement sheet from an aqueous asbestos fiber-cement slurry, removing water from the wet asbestos-cement sheet, applying the de-watered, still wet sheet on the surface of a pipe-forming mandrel, winding a continuous filament of an aromatic polyamide fiber about the wet asbestos-cement and within the interior of the ultimate pipe on the mandrel during the application of the wet asbestos-cement on the mandrel without stretching the continuous filament and substantially without placing the continuous filament in tension, the aromatic polyamide fiber of the continuous filament characterized by having high tensile strength and a low elongation capability, separating the mandrel from the inner surface of the thus-formed pipe, extracting the mandrel from within the pipe, and curing the pipe.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-03-06 | 1981-09-05 | 1982-03-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-03-06 | 1985-09-05 | 1986-03-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-03-06 | 1989-09-05 | 1990-03-07 | $7700.00 | Window Closed / Lapsed |