Multilevel embossing of foamed-sheet materials
Assignee: Armstrong World Industries Inc
•
Filing: 1975-02-28
•
Granted: 1978-02-28
•
Expires: 1995-02-28
Abstract
Abstract The process herein is used for achieving multilevel mechanical embossing of an expanded foam having a fused or cured wear layer in register with a print on the foam. The expansion of the decorative foam and fusion of the wear layer are carried out and then the back of the foam is cooled by back wetting with or without drum cooling. The wear layer is maintained at a high temperature for embossing and is embossed with registry between the embossed pattern and the printed pattern on the foam.
Inventors
- 👤 Walter J. Lewicki, Jr.
- 👤 William M. McQuate
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 02:14
CPC Classifications
B; B32; B32B; B32B37/00; B32B37/0038; B32B27/00; B32B27/06; B32B27/065; B32B3/00; B32B3/26; B32B3/30; B32B38/00; B32B38/06; B32B5/00; B32B5/18; B41; B41M; B41M1/00; B41M1/26; B41M1/30; B41M3/00; D; D06; D06N; D06N7/00; D06N7/0005; D06N7/0007; D06N7/001; D06N7/0028; B32B41/00; B32B2041/04; B32B2471/00; Y; Y10; Y10T; Y10T156/00; Y10T156/10; Y10T156/1002; Y10T156/1007; Y10T156/1023; Y10T156/1039; Y10T156/1041; Y10T428/00; Y10T428/24; Y10T428/24479; Y10T428/24496; Y10T428/24504
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
188 words
In a process for embossing a web of material wherein said material is composed of a composite structure having a carrier, a non-foamed embossable wear layer and a foamed layer therebetween, said foamed layer on the surface thereof adjacent the wear layer having a decorative pattern printed thereon, said above composite structure being in the form of a web which is first heated to a temperature of about 250° F. to 350° F., the improvement comprising: a. then after heating, wetting the carrier of the web, which is the back surface of the web, so as to lower the temperature of the back surface of the foam and the backing approximately 100° below the temperature of the top surface of the web, which is the non-foamed embossable layer, b. embossing the top surface of the web wherein the embossing means and its resulting embossing deeply penetrate the web, both the land areas and valley areas of the embossing means contact and impress a pattern on the top surface of the web, and c. cooling the embossed surface of the web to set the embossed pattern in the web.
Claim 2
Dependent Claim
188 words
In a process for embossing a web of material wherein said material is composed of a composite structure having a carrier, a non-foamed embossable wear layer and a foamed layer therebetween, said foamed layer on the surface thereof adjacent the wear layer having a decorative pattern printed thereon, said above composite structure being in the form of a web which is first heated to a temperature of about 250° F. to 350° F., the improvement comprising: a. then after heating, wetting the carrier of the web, which is the back surface of the web, so as to lower the temperature of the back surface of the foam and the backing approximately 100° below the temperature of the top surface of the web, which is the non-foamed embossable layer, b. embossing the top surface of the web wherein the embossing means and its resulting embossing deeply penetrate the web, both the land areas and valley areas of the embossing means contact and impress a pattern on the top surface of the web, and c. cooling the embossed surface of the web to set the embossed pattern in the web.
Claim 3
Dependent Claim
36 words
The process of claim 1 wherein there is the further step of: a. controlling the registry of the embossed pattern with the printed pattern of the web so that the two patterns will be in registry.
Claim 4
Dependent Claim
31 words
The process of claim 1 wherein: a. a heating means applies heat to the embossable top surface of the web just prior to the time the embossing step is carried out.
Claim 5
Dependent Claim
49 words
The process of claim 1 wherein: a. the web of material, after back wetting, is passed partly around a cooled drum which engages the carrier or back surface of the web to cool said surface of the web prior to the time that the embossing step is carried out.
Claim 6
Dependent Claim
29 words
The process of claim 1 wherein: a. the embossing step is carried out with a cold embossing roll and the web of material is wrapped partially around the roll.
References Cited (Backward Citations)
GB1230378A
Cited
US3619344A
Cited
US3816233A
Cited
US3741851A
Cited
US3887409A
Cited
US3887678A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-02-27 | 1981-08-29 | 1982-02-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-02-27 | 1985-08-29 | 1986-02-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-02-27 | 1989-08-29 | 1990-02-28 | $7700.00 | Window Closed / Lapsed |