Poly(aryloxyphosphazene) copolymer foams
Assignee: Armstrong World Industries Inc
•
Filing: 1977-05-13
•
Granted: 1978-02-28
•
Expires: 1997-05-13
Abstract
Abstract Poly(aryloxyphosphazene) copolymers and foams thereof having a significant portion of C 1 - C 4 alkoxyphenoxy groups are described. The copolymers consist of the units which occur in a nonregular fashion and are represented by the following general formulas: ##STR1## wherein R 1 represents a C 1 - C 4 linear or branched alkyl radical in the ortho-, meta-, or para-position, and R 2 represents hydrogen, a C 1 - C 10 linear or branched alkyl radical, or a C 1 - C 4 linear or branched alkoxy radical substituted on any sterically permissible position on the phenoxy group, with the proviso that when R 2 is alkoxy, OR 1 and R 2 are different. The copolymers of this invention may contain small amounts of randomly distributed units in addition to the repeating units described above, these additional units containing reactive sites enabling the properties of the copolymers to be modified by crosslinking and/or curing. The copolymers are elastomers, have desirable tensile strengths and may be used to form flexible or semirigid foams. The copolymers are extremely fire retardant and produce low smoke loads, or essentially no smoke, when heated in an open flame.
Inventors
- 👤 Ronald L. Dieck
- 👤 Edwin J. Quinn
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 04:01
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/04; C08J9/06; C08G; C08G79/00; C08G79/02; C08G79/025; C08L; C08L85/00; C08L85/02; C08J2385/00; C08J2385/02; Y; Y10; Y10S; Y10S521/00; Y10S521/903; Y10S521/907; Y10S521/921
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
109 words
A process of foaming the copolymers having randomly distributed repeating units represented by the formulas ##STR7## wherein R 1 is C 1 -C 4 linear or branched alkyl and R 2 is hydrogen, C 1 -C 10 linear or branched alkyl or C 1 -C 4 linear or branched alkoxyl with the proviso that when R 2 is alkoxy, OR 1 and R 2 are different, the ratio of (OC 6 H 4 OR.sub. 1):(OC 6 H 4 R 2 ) being from about 1:6 to about 6:1 wherein said copolymers are admixed with a chemical blowing agent and heated to a temperature sufficient to decompose said blowing agent.
Claim 2
Dependent Claim
109 words
A process of foaming the copolymers having randomly distributed repeating units represented by the formulas ##STR7## wherein R 1 is C 1 -C 4 linear or branched alkyl and R 2 is hydrogen, C 1 -C 10 linear or branched alkyl or C 1 -C 4 linear or branched alkoxyl with the proviso that when R 2 is alkoxy, OR 1 and R 2 are different, the ratio of (OC 6 H 4 OR.sub. 1):(OC 6 H 4 R 2 ) being from about 1:6 to about 6:1 wherein said copolymers are admixed with a chemical blowing agent and heated to a temperature sufficient to decompose said blowing agent.
Claim 3
Dependent Claim
11 words
the process of claim 1 wherein said blowing agent is 1,1'-bisazoformamide.
Claim 4
Dependent Claim
43 words
The process of foaming the copolymers of claim 1 which comprises mixing the copolymers with a chemical blowing agent and curing agent and heating the mixture to a temperature sufficient to decompose said blowing agent to foam the polymer and crosslink the polymer.
Claim 5
Dependent Claim
82 words
A foamed copolymer having the general formulas: ##STR8## wherein R 1 is C 1 -C 4 linear or branched alkyl, R 2 is hydrogen, C 1 -C 10 linear or branched alkyl or C 1 -C 4 linear or branched alkoxy, with the proviso that when R 2 is alkoxy, OR 1 and R 2 are different, and the ratio of (OC 6 H 4 -OR 1 ): (CO 6 H 4 -R 2 ) being from about 1:6 to about 6:1.
Claim 6
Dependent Claim
82 words
A foamed copolymer having the general formulas: ##STR8## wherein R 1 is C 1 -C 4 linear or branched alkyl, R 2 is hydrogen, C 1 -C 10 linear or branched alkyl or C 1 -C 4 linear or branched alkoxy, with the proviso that when R 2 is alkoxy, OR 1 and R 2 are different, and the ratio of (OC 6 H 4 -OR 1 ): (CO 6 H 4 -R 2 ) being from about 1:6 to about 6:1.
Claim 7
Dependent Claim
146 words
A foamed copolymer prepared by heating in admixture with a chemical blowing agent a copolymer having the general formulas: ##STR9## wherein R 1 is individually C 1 -C 4 linear or branched alkyl, R 2 is individually hydrogen, C 1 -C 10 linear or branched alkyl or C 1 -C 4 linear or branched alkoxy, with proviso that when R 2 is alkoxy, OR 1 and R 2 are different, and W represents a monovalent radical containing a group capable of a crosslinking chemical reaction at moderate temperatures, said group being attached to a P atom by a -O- linkage, the ratio of (OC 6 H 4 -OR 1 ):(OC 6 H 4 -R 2 ) being from about 1:6 to about 6:1 and the ratio of W: [(OC 6 H 4 -OR 1 )+(CO 6 H 4 -R 2 )] being less than about 1:5.
Claim 8
Dependent Claim
146 words
A foamed copolymer prepared by heating in admixture with a chemical blowing agent a copolymer having the general formulas: ##STR9## wherein R 1 is individually C 1 -C 4 linear or branched alkyl, R 2 is individually hydrogen, C 1 -C 10 linear or branched alkyl or C 1 -C 4 linear or branched alkoxy, with proviso that when R 2 is alkoxy, OR 1 and R 2 are different, and W represents a monovalent radical containing a group capable of a crosslinking chemical reaction at moderate temperatures, said group being attached to a P atom by a -O- linkage, the ratio of (OC 6 H 4 -OR 1 ):(OC 6 H 4 -R 2 ) being from about 1:6 to about 6:1 and the ratio of W: [(OC 6 H 4 -OR 1 )+(CO 6 H 4 -R 2 )] being less than about 1:5.
Claim 9
Dependent Claim
163 words
A process for foaming copolymers of the formula ##STR10## wherein R 1 is individually CH 3 or n-C 4 H 6 , R 2 is individually hydrogen, C 1 -C 10 alkyl or C 1 -C 4 alkoxy, with the proviso that when R 2 is alkoxy, OR 1 and R 2 are different, and W represents a monovalent radical containing a group capable of a crosslinking chemical reaction at moderate temperatures, said group being attached to a P atom by a -O- linkage, the ratio of (OC 6 H 4 -OR 1 ):(OC 6 H 4 -R 2 ) being from about 1:6 to about 6:1, and the ratio of W: [OC 6 H 4 -OR 1 )+(OC 6 H 4 -R 2 )] being less than about 1:5, wherein said polymers are admixed with a sulfur-type curing agent, and a chemical blowing agent, and said mixture is heated to a temperature sufficient to decompose said blowing agent and cure the copolymer.
Claim 10
Dependent Claim
163 words
A process for foaming copolymers of the formula ##STR10## wherein R 1 is individually CH 3 or n-C 4 H 6 , R 2 is individually hydrogen, C 1 -C 10 alkyl or C 1 -C 4 alkoxy, with the proviso that when R 2 is alkoxy, OR 1 and R 2 are different, and W represents a monovalent radical containing a group capable of a crosslinking chemical reaction at moderate temperatures, said group being attached to a P atom by a -O- linkage, the ratio of (OC 6 H 4 -OR 1 ):(OC 6 H 4 -R 2 ) being from about 1:6 to about 6:1, and the ratio of W: [OC 6 H 4 -OR 1 )+(OC 6 H 4 -R 2 )] being less than about 1:5, wherein said polymers are admixed with a sulfur-type curing agent, and a chemical blowing agent, and said mixture is heated to a temperature sufficient to decompose said blowing agent and cure the copolymer.
Claim 11
Dependent Claim
111 words
The process of foaming the copolymers of claim 6 which comprises mixing the copolymers with a chemical blowing agent and a mixture of curing agents, at least one of said curing agents having an initiation temperature below the temperature at which said chemical blowing agent decomposes; heating and foamable mass to a temperature below the decomposition temperature of said blowing agent, but above the initiation temperature of at least one of said curing agents, for a sufficient time to partially pre-cure the copolymers; and heating the partially pre-cured mass to a temperature above the decomposition temperature of said blowing agent to foam the copolymers and to effect a further cure thereof.
Claim 12
Dependent Claim
66 words
The process of claim 7, wherein the partial pre-cure is accomplished by heating the foamable mass for about 6 to about 30 minutes at a temperature of from about 200° to about 250° F., and the foaming and further curing is accomplished by heating the partially pre-cured mass for about 30 to about 60 minutes at a temperature of from about 300° to about 350° F.
Claim 13
Dependent Claim
40 words
A process for foaming copolymers of the formula ##STR11## comprising mixing the copolymers with a chemical blowing agent and a peroxide curing agent and heating the mixture to a temperature sufficient to decompose said blowing agent and cure the copolymer.
Claim 14
Dependent Claim
40 words
A process for foaming copolymers of the formula ##STR11## comprising mixing the copolymers with a chemical blowing agent and a peroxide curing agent and heating the mixture to a temperature sufficient to decompose said blowing agent and cure the copolymer.
Claim 15
Dependent Claim
158 words
A process for foaming copolymers of the formula [NP(OC.sub.6 H.sub.4 -OR.sub.1).sub.a (OC.sub.6 H.sub.4 -R.sub.2).sub.b (W).sub.c ].sub.n wherein R 1 is individually C 1 -C 4 linear or branched alkyl; R 2 is individually hydrogen, C 1 -C 10 linear or branched alkyl or C 1 -C 4 linear or branched alkoxy, with the proviso that when R 2 is alkoxy, OR 1 and R 2 are different; W represents a monovalent radical containing a group capable of a crosslinking chemical reaction at moderate temperatures, said group being attached to a P atom by a -O- linkage; n is from 20 to 2000, c < o, a + b + c = 2, the ratio of a:b is from about 1:6 to about 6:1, and the ratio of c:(a + b) is less than about 1:5, wherein said copolymers are admixed with a chemical blowing agent and the mixture heated to a temperature sufficient to decompose said blowing agent.
Claim 16
Dependent Claim
158 words
A process for foaming copolymers of the formula [NP(OC.sub.6 H.sub.4 -OR.sub.1).sub.a (OC.sub.6 H.sub.4 -R.sub.2).sub.b (W).sub.c ].sub.n wherein R 1 is individually C 1 -C 4 linear or branched alkyl; R 2 is individually hydrogen, C 1 -C 10 linear or branched alkyl or C 1 -C 4 linear or branched alkoxy, with the proviso that when R 2 is alkoxy, OR 1 and R 2 are different; W represents a monovalent radical containing a group capable of a crosslinking chemical reaction at moderate temperatures, said group being attached to a P atom by a -O- linkage; n is from 20 to 2000, c < o, a + b + c = 2, the ratio of a:b is from about 1:6 to about 6:1, and the ratio of c:(a + b) is less than about 1:5, wherein said copolymers are admixed with a chemical blowing agent and the mixture heated to a temperature sufficient to decompose said blowing agent.
References Cited (Backward Citations)
US3370020A
Cited
US3515688A
Cited
US3702833A
Cited
US3844983A
Cited
US3888799A
Cited
US3700629A
Cited
US3856712A
Cited
US3856713A
Cited
US3883451A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-02-27 | 1981-08-29 | 1982-02-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-02-27 | 1985-08-29 | 1986-02-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-02-27 | 1989-08-29 | 1990-02-28 | $7700.00 | Window Closed / Lapsed |