US4076598A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method, electrolyte and additive for electroplating a cobalt brightened gold alloy
Assignee: TE Connectivity Corp
•
Filing: 1976-11-17
•
Granted: 1978-02-28
•
Expires: 1996-11-17
Abstract
Abstract Disclosed are methods and electrolytes for the electrodeposition of a gold alloy containing 0.05 to 0.4 per cent by weight of cobalt. The electrolytes comprise aqueous acidic solutions containing nitrilotriacetic acid.
Inventors
- 👤 Lewis Brian Lerner
- 👤 Thomas Francis Davis
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 06:48
CPC Classifications
C; C25; C25D; C25D3/00; C25D3/02; C25D3/56; C25D3/62
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
122 words
An aqueous bath for depositing from an electrolyzed solution thereof gold and, as an alloying additive to gold, variously closely controllable amounts of cobalt in an amount from 0.05 to 0.4 in percent by weight in the deposit based on amount of gold, said bath solution consisting essentially of: 1.0 - 4.0 troy oz/gal Au°, added as KAu(CN) 2 ; 50 - 150 g/l K 2 HPO 4 ; 50 - 200 g/l KH 2 PO 4 ; 5 - 60 g/l nitrilotriacetic acid; and 0.1 - 7.0 g/l Co°, as a soluble salt of cobalt, from at least one salt selected from the group consisting of cobalt sulfate, halide, nitrate and carbonate, said bath having a pH of 4.0 to 6.0.
Claim 2
Dependent Claim
122 words
An aqueous bath for depositing from an electrolyzed solution thereof gold and, as an alloying additive to gold, variously closely controllable amounts of cobalt in an amount from 0.05 to 0.4 in percent by weight in the deposit based on amount of gold, said bath solution consisting essentially of: 1.0 - 4.0 troy oz/gal Au°, added as KAu(CN) 2 ; 50 - 150 g/l K 2 HPO 4 ; 50 - 200 g/l KH 2 PO 4 ; 5 - 60 g/l nitrilotriacetic acid; and 0.1 - 7.0 g/l Co°, as a soluble salt of cobalt, from at least one salt selected from the group consisting of cobalt sulfate, halide, nitrate and carbonate, said bath having a pH of 4.0 to 6.0.
Claim 3
Dependent Claim
16 words
The bath as defined in claim 1 wherein the soluble salt of cobalt is cobalt sulfate.
Claim 4
Dependent Claim
32 words
A salt composition suitable for depositing gold and cobalt from an electrolyzed aqueous bath solution thereof, said composition consisting essentially of the salts as defined in claim 1, in the proportions thereof.
Claim 5
Dependent Claim
126 words
An aqueous bath for depositing from an electrolyzed solution thereof gold and, as an alloying additive to gold, variously closely controllable amounts of cobalt in an amount from 0.05 to 0.4 in percent by weight in the deposit based on amount of gold, said aqueous bath solution consisting essentially of: 1.0 - 4.0 troy oz/gal Au°, added as KAu(CN) 2 ; 50 - 100 g/l KH 2 PO 4 ; 50 - 100 g/l K 3 citrate; 5 - 30 g/l nitrilotriacetic acid; and 0.1 - 2.0 g/l Co° added as a bath soluble salt of cobalt, from at least one salt selected from the group consisting of cobalt sulfate, nitrate, chloride, carbonate, and mixtures of same, said bath having a pH of 3.5 to 6.0.
Claim 6
Dependent Claim
126 words
An aqueous bath for depositing from an electrolyzed solution thereof gold and, as an alloying additive to gold, variously closely controllable amounts of cobalt in an amount from 0.05 to 0.4 in percent by weight in the deposit based on amount of gold, said aqueous bath solution consisting essentially of: 1.0 - 4.0 troy oz/gal Au°, added as KAu(CN) 2 ; 50 - 100 g/l KH 2 PO 4 ; 50 - 100 g/l K 3 citrate; 5 - 30 g/l nitrilotriacetic acid; and 0.1 - 2.0 g/l Co° added as a bath soluble salt of cobalt, from at least one salt selected from the group consisting of cobalt sulfate, nitrate, chloride, carbonate, and mixtures of same, said bath having a pH of 3.5 to 6.0.
Claim 7
Dependent Claim
16 words
The bath as defined in claim 4, wherein the soluble salt of cobalt is cobalt sulfate.
Claim 8
Dependent Claim
86 words
A salt composition suitable for depositing gold and cobalt from an electrolyzed aqueous bath solution said composition consisting essentially in the proportions, when added to water, of gold as potassium gold cyanide 1.0 to 4.0 troy oz/gal, calculated as elemental gold; potassium dihydrogen phosphate, 50 to 100 grams/liter; tripotassium citrate, 50 to 100 grams/liter; nitrilotriacetate acid, 5 to 30 grams/liter; and as a cobalt salt, 0.1 to 2.0 grams/liter of cobalt; selected from the group consisting of cobalt sulfate, chloride, nitrate, carbonate and mixtures of same.
Claim 9
Dependent Claim
86 words
A salt composition suitable for depositing gold and cobalt from an electrolyzed aqueous bath solution said composition consisting essentially in the proportions, when added to water, of gold as potassium gold cyanide 1.0 to 4.0 troy oz/gal, calculated as elemental gold; potassium dihydrogen phosphate, 50 to 100 grams/liter; tripotassium citrate, 50 to 100 grams/liter; nitrilotriacetate acid, 5 to 30 grams/liter; and as a cobalt salt, 0.1 to 2.0 grams/liter of cobalt; selected from the group consisting of cobalt sulfate, chloride, nitrate, carbonate and mixtures of same.
Claim 10
Independent Claim
133 words
A method for deposition from an electrolyzed aqueous bath solution gold cobalt alloys, the steps comprising: electrolyzing a bath solution of: 1.0 - 4.0 troy oz/gal Au°, added as KAu(CN) 2 ; 50 - 150 g/l K 2 HPO 4 ; 50 - 200 g/l KH 2 PO 4 ; 5 - 60 g/l nitrilotriacetic acid; and 0.1 - 7.0 g/l Co° added as a bath soluble salt of cobalt sulfate, nitrate, chloride, or carbonate; wherein the solution is at a pH of 3.6 to 6.0 and at a temperature from 80° F to 150° F; passing a current between a cathode and an anode, wherein the current density ranges from 1 to 100 ASF; and depositing a gold-cobalt on a substrate of closely controllable proportions of gold to cobalt in said deposit.
Claim 11
Independent Claim
133 words
A method for deposition from an electrolyzed aqueous bath solution gold cobalt alloys, the steps comprising: electrolyzing a bath solution of: 1.0 - 4.0 troy oz/gal Au°, added as KAu(CN) 2 ; 50 - 150 g/l K 2 HPO 4 ; 50 - 200 g/l KH 2 PO 4 ; 5 - 60 g/l nitrilotriacetic acid; and 0.1 - 7.0 g/l Co° added as a bath soluble salt of cobalt sulfate, nitrate, chloride, or carbonate; wherein the solution is at a pH of 3.6 to 6.0 and at a temperature from 80° F to 150° F; passing a current between a cathode and an anode, wherein the current density ranges from 1 to 100 ASF; and depositing a gold-cobalt on a substrate of closely controllable proportions of gold to cobalt in said deposit.
Claim 12
Dependent Claim
14 words
The method as defined in claim 7, wherein the cobalt salt is cobalt sulfate.
Claim 13
Dependent Claim
31 words
The method as defined in claim 7, wherein the pH of the bath is of about 4.2, the temperature of about 110° F, and current density from 1 to 50 ASF.
Claim 14
Independent Claim
15 words
A method for depositing from an electrolyzed aqueous bath solution gold-cobalt alloys, the steps comprising:
Claim 15
Independent Claim
15 words
A method for depositing from an electrolyzed aqueous bath solution gold-cobalt alloys, the steps comprising:
Claim 16
Dependent Claim
108 words
electrolyzing a bath solution of 1.0 - 4.0 troy oz/gal Au°, added as KAu(CN) 2 ; 50 - 100 g/l KH 2 PO 4 ; 50 - 100 g/l K 3 citrate; 10 - 30 g/l nitrilotriacetic acid; and 0.1 - 2.0 g/l Co° added as a bath soluble cobalt salt; wherein the solution is at a pH of 3.6 to 6.0 and a temperature from 80° F to 150° F, passing a current between a cathode and an anode, whereby the current density ranges from 1 to 100 ASF; and depositing on a substrate a deposit of closely controllable proportions of gold to cobalt in said deposit.
Claim 17
Dependent Claim
108 words
electrolyzing a bath solution of 1.0 - 4.0 troy oz/gal Au°, added as KAu(CN) 2 ; 50 - 100 g/l KH 2 PO 4 ; 50 - 100 g/l K 3 citrate; 10 - 30 g/l nitrilotriacetic acid; and 0.1 - 2.0 g/l Co° added as a bath soluble cobalt salt; wherein the solution is at a pH of 3.6 to 6.0 and a temperature from 80° F to 150° F, passing a current between a cathode and an anode, whereby the current density ranges from 1 to 100 ASF; and depositing on a substrate a deposit of closely controllable proportions of gold to cobalt in said deposit.
Claim 18
Dependent Claim
30 words
The method as defined in claim 10, wherein the pH of the bath is about 4.2, the temperature about 100° F, and the current density of 1 to 50 ASF.
Claim 19
Dependent Claim
95 words
An aqueous bath for depositing from an elctrolyzed solution thereof gold and, as an alloying additive to gold, variously closely controllable amounts of cobalt, in an amount of 0.05 to 0.4 in percent by weight in the gold deposit, said aqueous solution consisting essentially of: 1.0 - 4.0 troy oz/gal Au° as elemental gold (added as KAu(CN) 2 ; 3.0 - 100 g/l nitrilotriacetic acid; 50 - 100 g/l K 3 citrate; 0.1 - 2.0 g/l Co°, added as cobalt sulfate, and, for pH adjustment, citric acid, said bath having pH of 4.0 to 5.0.
Claim 20
Dependent Claim
95 words
An aqueous bath for depositing from an elctrolyzed solution thereof gold and, as an alloying additive to gold, variously closely controllable amounts of cobalt, in an amount of 0.05 to 0.4 in percent by weight in the gold deposit, said aqueous solution consisting essentially of: 1.0 - 4.0 troy oz/gal Au° as elemental gold (added as KAu(CN) 2 ; 3.0 - 100 g/l nitrilotriacetic acid; 50 - 100 g/l K 3 citrate; 0.1 - 2.0 g/l Co°, added as cobalt sulfate, and, for pH adjustment, citric acid, said bath having pH of 4.0 to 5.0.
Claim 21
Dependent Claim
80 words
A salt composition suitable for depositing gold and cobalt from an electrolyzed aqueous bath solution thereof said composition consisting essentially of, in the proportions, when added to water, gold as potassium gold cyanide 1.0 to 4.0 troy oz/gal, calculated as elemental gold, tripotassium citrate 50 to 100 grams/liter, nitrilotriacetic acid 3.0 to 100 grams/liter and 0.1 to 2.0 grams/liter of cobalt, as a cobalt salt, selected from the group consisting of cobalt sulfate, chloride, nitrate, carbonate, and mixtures of same.
Claim 22
Dependent Claim
80 words
A salt composition suitable for depositing gold and cobalt from an electrolyzed aqueous bath solution thereof said composition consisting essentially of, in the proportions, when added to water, gold as potassium gold cyanide 1.0 to 4.0 troy oz/gal, calculated as elemental gold, tripotassium citrate 50 to 100 grams/liter, nitrilotriacetic acid 3.0 to 100 grams/liter and 0.1 to 2.0 grams/liter of cobalt, as a cobalt salt, selected from the group consisting of cobalt sulfate, chloride, nitrate, carbonate, and mixtures of same.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-02-27 | 1981-08-29 | 1982-02-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-02-27 | 1985-08-29 | 1986-02-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-02-27 | 1989-08-29 | 1990-02-28 | $7700.00 | Window Closed / Lapsed |