Method of coating with water dispersible, low molecular weight polyamide resin particles of uniform sizes
Assignee: FMC Corp
•
Filing: 1976-04-30
•
Granted: 1978-02-21
•
Expires: 1996-04-30
Abstract
Abstract Finely-divided, water dispersible, low molecular weight, linear polyamide resin particles having a unique morphology and of uniform particle sizes are formed by preparing a linear polyamide of a predetermined low molecular weight in the presence of water followed by rapidly quenching the reaction mass with an aqueous medium below the freezing point of the polyamide and continuing the cooling of the mass to a temperature sufficiently low so as to prevent particle growth and structural alteration while regulating the pH of the quenched mass to provide particles of predetermined, uniform size dispersed in the aqueous medium. The particles vary from ultimate flaky sheets or lamellae to loosely packed, randomly oriented, clusters of flaky sheets. Spray dried products may be agglomerates which disintegrate readily in water to the original particles or aggregates depending upon intended uses. The dispersions and dried products are useful in the coating art and the polyamide may be polymerized to high molecular weights after application to a substrate.
Inventors
- 👤 Charles F. Ferraro
- 👤 Richard A. Javick
- 👤 James A. Robertson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 05:07
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/12; C08J3/122; C08G; C08G69/00; C08G69/46; C08J2377/00
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
205 words
In a method of providing a substrate with a self-adherent coating of a high molecular weight, linear polyamide wherein (1) the substrate is coated with a dispersion comprising water, finely-divided, water dispersible, low molecular weight, linear polyamide resin particles, between about 0.15% and about 0.8%, based upon the weight of the resin, of a catalyst consisting of a non-volatile, strong acid or a compound which upon heating is converted to a non-volatile, strong acid and between about 1% and 8%, based upon the weight of the resin, of a flow promoter, (2) the coated substrate is heated to at least the melting temperature of the polyamide resin and (3) the heated substrate is maintained at the temperature for a period sufficient to cause the polyamide resin to flow and to polymerize the resin to a predetermined high molecular weight, the improvement which comprises employing as the dispersed polyamide resin particles, finely-divided, water dispersible, low molecular weight, linear polyamide resin particles consisting of loosely packed, randomly oriented, clusters of flaky sheets, the mean particle size of the dispersed particles being between about 0.03 micron and about 6 microns and the particle size distribution being about d + 0.8 d, where d is the mean particle size.
Claim 2
Dependent Claim
205 words
In a method of providing a substrate with a self-adherent coating of a high molecular weight, linear polyamide wherein (1) the substrate is coated with a dispersion comprising water, finely-divided, water dispersible, low molecular weight, linear polyamide resin particles, between about 0.15% and about 0.8%, based upon the weight of the resin, of a catalyst consisting of a non-volatile, strong acid or a compound which upon heating is converted to a non-volatile, strong acid and between about 1% and 8%, based upon the weight of the resin, of a flow promoter, (2) the coated substrate is heated to at least the melting temperature of the polyamide resin and (3) the heated substrate is maintained at the temperature for a period sufficient to cause the polyamide resin to flow and to polymerize the resin to a predetermined high molecular weight, the improvement which comprises employing as the dispersed polyamide resin particles, finely-divided, water dispersible, low molecular weight, linear polyamide resin particles consisting of loosely packed, randomly oriented, clusters of flaky sheets, the mean particle size of the dispersed particles being between about 0.03 micron and about 6 microns and the particle size distribution being about d + 0.8 d, where d is the mean particle size.
Claim 3
Dependent Claim
46 words
The method as defined in claim 1 wherein the low molecular weight polyamide resin has a reduced viscosity betwween about 0.15 and about 0.26 and the coated substrate is heated to a temperature between 205° C. and 240° C. for from 5 minutes to 15 minutes.
Claim 4
Dependent Claim
13 words
The method as defined in claim 2 wherein the substrate is a metal.
Claim 5
Dependent Claim
12 words
The method as defined in claim 2 wherein the substrate is glass.
Claim 6
Dependent Claim
178 words
In a method of providing a substrate with a self-adherent coating of a high molecular weight, linear polyamide wherein (1) there is provided a fluidized bed of powder consisting essentially of low molecular weight, linear polyamide resin particles, between about 0.15% and about 0.8%, based upon the weight of the polyamide resin, of a catalyst consisting of a non-volatile, strong acid or a compound which upon heating is converted to a non-volatile, strong acid and between about 1% and 8%, based upon the weight of the polyamide resin, of a flow promoter, (2) a heated substrate at a temperature of at least the melting temperature of the polyamide resin is immersed into the fluidized bed and (3) the heated substrate is maintained at the temperature for a period sufficient to cause the resin in contact with the substrate to flow and to polymerize to a predetermined high molecular weight, the improvement comprises employing as the low molecular weight, linear polyamide resin particles, particles consisting essentially of loosely bound agglomerates of loosely packed, randomly oriented clusters of flaky sheets.
Claim 7
Dependent Claim
178 words
In a method of providing a substrate with a self-adherent coating of a high molecular weight, linear polyamide wherein (1) there is provided a fluidized bed of powder consisting essentially of low molecular weight, linear polyamide resin particles, between about 0.15% and about 0.8%, based upon the weight of the polyamide resin, of a catalyst consisting of a non-volatile, strong acid or a compound which upon heating is converted to a non-volatile, strong acid and between about 1% and 8%, based upon the weight of the polyamide resin, of a flow promoter, (2) a heated substrate at a temperature of at least the melting temperature of the polyamide resin is immersed into the fluidized bed and (3) the heated substrate is maintained at the temperature for a period sufficient to cause the resin in contact with the substrate to flow and to polymerize to a predetermined high molecular weight, the improvement comprises employing as the low molecular weight, linear polyamide resin particles, particles consisting essentially of loosely bound agglomerates of loosely packed, randomly oriented clusters of flaky sheets.
Claim 8
Dependent Claim
45 words
The method as defined in claim 5 wherein the low molecular weight polyamide resin has a reduced viscosity between about 0.15 and about 0.26 and the substrate is heated to a temperature between 205° C. and 240° C. for from 5 minutes to 15 minutes.
Claim 9
Dependent Claim
13 words
The method as defined in claim 6 wherein the substrate is a metal.
Claim 10
Dependent Claim
12 words
The method as defined in claim 6 wherein the substrate is glass.
References Cited (Backward Citations)
US2279774A
Cited
US2241322A
Cited
US2348751A
Cited
US2742440A
Cited
US2972553A
Cited
US3564599A
Cited
US3446782A
Cited
US3496002A
Cited
US3476711A
Cited
GB1180023A
Cited
US3481906A
Cited
US3536647A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-02-20 | 1981-08-22 | 1982-02-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-02-20 | 1985-08-22 | 1986-02-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-02-20 | 1989-08-22 | 1990-02-21 | $7700.00 | Window Closed / Lapsed |