Process for recovering molybdenum values from spent catalysts
Assignee: Metaux Speciaux SA
•
Filing: 1977-01-31
•
Granted: 1978-02-21
•
Expires: 1997-01-31
Abstract
Abstract A process of recovering molybdenum in the form of molybdic acid from waste products and particularly from spent catalysts containing a support based on gamma-alumina wherein the molybdenum is in the form of molybdenum oxide or molybdenum sulfide comprising treating the waste products with sodium carbonate and heating to convert the molybdenum present to sodium molybdate, and converting the sodium molybdate to molybdic acid by treatment with concentrated nitric acid to produce molybdic acid high in purity that is suitable for the production of molybdenum compounds as well as for the recovery of the pure metal.
Inventors
- 👤 Herman Castagna
- 👤 Guy Gravey
- 👤 Andre Roth
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 06:50
CPC Classifications
C; C22; C22B; C22B34/00; C22B34/30; C22B34/34; C22B34/345; C22B7/00; C22B7/009; Y; Y02; Y02P; Y02P10/00; Y02P10/20
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
210 words
A process for recovering molybdenum in the form of molybdic acid from alumina containing spent catalysts containing molybdenum oxide or molybdenum sulfide comprising treating the alumina containing spent catalyst with an aqueous solution of sodium carbonate at a temperature of from 60° to 100° C, and in a quantity in excess of that stoichiometrically necessary for obtaining the molybdenum in the form of sodium molybdate and the sulfur in the form of sodium sulfate which excess expressed in weight of sodium carbonate does not exceed 10%, baking the sodium carbonate treated alumina containing spent catalysts at a temperature of from 600° to 800° C to convert the molybdenum present to sodium molybdate, cooling to a temperature of from 70° to 80° C, dissolving the sodium molybdate by washing in hot water at a temperature of from 60° to 100° C, cooling the dissolved sodium molybdate to a temperature not exceeding 30° C, neutralizing the cooled solution of sodium molybdate by continuously introducing concentrated nitric acid at a temperature not exceeding 30° C and at a rate of flow adjusted to achieve a pH value of 5 to 6 to convert the sodium molybdate to molybdic acid, further adding nitric acid to clarify the nitric acid solution, and precipitating molybdic acid.
Claim 2
Dependent Claim
210 words
A process for recovering molybdenum in the form of molybdic acid from alumina containing spent catalysts containing molybdenum oxide or molybdenum sulfide comprising treating the alumina containing spent catalyst with an aqueous solution of sodium carbonate at a temperature of from 60° to 100° C, and in a quantity in excess of that stoichiometrically necessary for obtaining the molybdenum in the form of sodium molybdate and the sulfur in the form of sodium sulfate which excess expressed in weight of sodium carbonate does not exceed 10%, baking the sodium carbonate treated alumina containing spent catalysts at a temperature of from 600° to 800° C to convert the molybdenum present to sodium molybdate, cooling to a temperature of from 70° to 80° C, dissolving the sodium molybdate by washing in hot water at a temperature of from 60° to 100° C, cooling the dissolved sodium molybdate to a temperature not exceeding 30° C, neutralizing the cooled solution of sodium molybdate by continuously introducing concentrated nitric acid at a temperature not exceeding 30° C and at a rate of flow adjusted to achieve a pH value of 5 to 6 to convert the sodium molybdate to molybdic acid, further adding nitric acid to clarify the nitric acid solution, and precipitating molybdic acid.
Claim 3
Dependent Claim
33 words
A process in accordance with claim 1 wherein the alumina containing spent catalysts are subjected to a preliminary oxidizing roasting to free the same from volatile materials, carbon and part of the sulfur.
Claim 4
Dependent Claim
46 words
A process in accordance with claim 1 wherein the hot water solution of sodium molybdate is cooled to a temperature not exceeding 30° C and then subjected to successive treatments with concentrated nitric acid at rates of flow resulting in a pH of 5 to 6.
Claim 5
Dependent Claim
30 words
A process in accordance with claim 1 wherein the molybdic acid precipitate is kept in suspension, filtered, washed with water containing 2% by volume of concentrated nitric acid, and dried.
Claim 6
Dependent Claim
75 words
A process in accordance with claim 1 wherein the sodium carbonate solubilizes the molybdenum present in the alumina containing spent catalysts and is added in a quantity in excess of that stoichiometrically necessary for obtaining the molybdenum in the form of sodium molybdate and the sulfur in the form of sodium sulfate, which excess expressed in weight of sodium carbonate is equal to between 1 and 3% of the total weight of the waste products.
Claim 7
Dependent Claim
40 words
A process in accordance with claim 1 wherein the baking of the sodium carbonate treated alumina containing spent catalysts is conducted at a temperature in the range from 650° to 750° C to convert the molybdenum present to sodium molybdate.
Claim 8
Dependent Claim
100 words
A process in accordance with claim 1 comprising cooling the hot water solution containing sodium aluminate as well as sodium molybdate to a temperature not exceeding 30° C, neutralizing the solution with nitric acid of a concentration of about 53% at a rate of flow adjusted so that the pH value is in the order of 5.2 to 5.5, clarifying the nitric acid solution by further addition of nitric acid, precipitating molybdic acid at a temperature of about 100° C, filtering, washing with water containing 2% by volume of concentrated nitric acid, and drying the filtered and washed molybdic acid.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-02-20 | 1981-08-22 | 1982-02-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-02-20 | 1985-08-22 | 1986-02-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-02-20 | 1989-08-22 | 1990-02-21 | $7700.00 | Window Closed / Lapsed |