Abstract
Abstract Boron nitride-boron nitride composite bodies may be produced by combining pure boron nitride fibers with partially nitrided fibers consisting essentially of B, N, O, and H, and hot pressing the composite at elevated temperatures and pressure. The partially nitrided material serves as a source of matrix material for the boron nitride fibers, and when fiber orientation is properly controlled, bodies of extremely high strength may be obtained. Densities in excess of 1.5 g./cc. may be obtained, in a one-step process which overcomes difficulties inherent in multiple-step nitriding and re-nitriding processes.
Inventors
- 👤 James Economy
- 👤 Choll K. Jun
- 👤 Ruey Y. Lin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 21:38
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/583; C04B35/622; C04B35/62227; C04B35/64; C04B35/645; C04B35/71; C04B35/78; C04B35/80
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
153 words
A process for the preparation of boron nitride-boron nitride composite bodies, comprising the steps of: a. forming a blend of from about 10 to about 90 percent of essentially pure polycrystalline boron nitride fibers with from about 90 to about 10 percent of partially nitrided boric oxide fibers, said boron nitride fibers and said partially nitrided boric oxide fibers having a maximum diameter of 10 microns, and said partially nitrided fibers consisting essentially of boron, oxygen, hydrogen, and from about 30 percent to about 55 percent by weight of nitrogen; b. forming a composite body of said blended fibers; c. heating said composite body, at a pressure of from about 200 to about 500 psi in an inert atmosphere, to a first elevated temperature at which essentially all boric oxide present is decomposed; and d. further heating said body to a second elevated temperature of from about 2000° C to about 2200° C.
Claim 2
Dependent Claim
153 words
A process for the preparation of boron nitride-boron nitride composite bodies, comprising the steps of: a. forming a blend of from about 10 to about 90 percent of essentially pure polycrystalline boron nitride fibers with from about 90 to about 10 percent of partially nitrided boric oxide fibers, said boron nitride fibers and said partially nitrided boric oxide fibers having a maximum diameter of 10 microns, and said partially nitrided fibers consisting essentially of boron, oxygen, hydrogen, and from about 30 percent to about 55 percent by weight of nitrogen; b. forming a composite body of said blended fibers; c. heating said composite body, at a pressure of from about 200 to about 500 psi in an inert atmosphere, to a first elevated temperature at which essentially all boric oxide present is decomposed; and d. further heating said body to a second elevated temperature of from about 2000° C to about 2200° C.
Claim 3
Dependent Claim
37 words
A process as set forth in claim 1 wherein said partially nitrided fiber comprises from about 40 to about 45 weight percent nitrogen, and said first elevated temperature is from about 1400° C to about 1600° C.
Claim 4
Independent Claim
133 words
A method for the preparation of shaped boron nitride-boron nitride composite bodies, said method comprising the steps of: a. forming a body of boron nitride fibers and partially nitrided boric oxide fibers, said boron nitride fibers and said partially nitrided boric oxide fibers having a maximum diameter of about 10 microns, said partially nitrided fibers consisting essentially of boron, nitrogen, oxygen, and hydrogen, wherein said nitrogen constitutes from about 30 percent to about 55 percent by weight of said partially nitrided fibers; b. placing said body in a mold of the desired configuration; and c. hot pressing said body, in an inert atmosphere at a pressure of from about 25 psi to about 1000 psi, at a temperature in excess of the decomposition temperature of boric oxide but less than about 2200° C.
Claim 5
Independent Claim
133 words
A method for the preparation of shaped boron nitride-boron nitride composite bodies, said method comprising the steps of: a. forming a body of boron nitride fibers and partially nitrided boric oxide fibers, said boron nitride fibers and said partially nitrided boric oxide fibers having a maximum diameter of about 10 microns, said partially nitrided fibers consisting essentially of boron, nitrogen, oxygen, and hydrogen, wherein said nitrogen constitutes from about 30 percent to about 55 percent by weight of said partially nitrided fibers; b. placing said body in a mold of the desired configuration; and c. hot pressing said body, in an inert atmosphere at a pressure of from about 25 psi to about 1000 psi, at a temperature in excess of the decomposition temperature of boric oxide but less than about 2200° C.
Claim 6
Dependent Claim
29 words
A method as set forth in claim 3, wherein said hot-pressing elevates the temperature of said body to a temperature of from about 1400° C to about 1600° C.
Claim 7
Dependent Claim
20 words
A method as set forth in claim 4, wherein said pressure is from about 200 psi to about 500 psi.
Claim 8
Dependent Claim
29 words
A method as set forth in claim 3, wherein said hot-pressing elevates the temperature of said body to a temperature of from about 2000° C to about 2200° C.
Claim 9
Dependent Claim
25 words
A method as set forth in claim 6, wherein said partially nitrided fiber contains from about 40 percent to about 50 percent by weight nitrogen.
Claim 10
Dependent Claim
44 words
A method as set forth in claim 3, wherein said body is a laminate formed by depositing alternate layers of boron nitride fibers and partially nitrided boric oxide fibers in said mold, each said layer being oriented approximately 90° from the previously deposited layer.
Claim 11
Dependent Claim
86 words
In a process for the production of boron nitride bodies by hot pressing boron nitride fibers, the improvement which comprises forming a blend of such boron nitride fibers with from about 10 to about 90 weight percent of partially nitrided boric oxide fibers consisting essentially of boron, hydrogen, oxygen, and nitrogen, wherein said nitrogen constitutes from about 30 to about 55 percent by weight of said partially nitrided fibers, and hot pressing at a temperature between the decomposition temperature of boric oxide and about 2200° C.
Claim 12
Dependent Claim
86 words
In a process for the production of boron nitride bodies by hot pressing boron nitride fibers, the improvement which comprises forming a blend of such boron nitride fibers with from about 10 to about 90 weight percent of partially nitrided boric oxide fibers consisting essentially of boron, hydrogen, oxygen, and nitrogen, wherein said nitrogen constitutes from about 30 to about 55 percent by weight of said partially nitrided fibers, and hot pressing at a temperature between the decomposition temperature of boric oxide and about 2200° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-02-20 | 1981-08-22 | 1982-02-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-02-20 | 1985-08-22 | 1986-02-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-02-20 | 1989-08-22 | 1990-02-21 | $7700.00 | Window Closed / Lapsed |