Production of non-carcinogenic large particle carbon black

Claim 2

A process for the production of a non-carcinogenic large particle carbon black comprising a. pyrolytically in a carbon black furnace decomposing a hydrocarbon feedstock having a low carbon residue of less than 0.2 weight % such as to form a smoke containing a carbon black having a CTAB surface area of less than about 80 m 2 /g, b. severly aftertreating said smoke by subjecting it to at least one of the steps of late quenching and secondary air injection such as to produce a smoke containing a carbon black having a photelometer of about 100% and a pitting degree defined as the difference between the nitrogen surface area in square meters per gram and the CTAB surface in square meters per gram of 0.2 m 2 /g or more, c. oxidizing said carbon black and pelleting the carbon black with an aqueous pelleting liquid, and d. drying the wet carbon black pellets at a temperature of about 500° to about 600° F.

Claim 3

A process in accordance with claim 1 wherein said feedstock is selected from the group consisting of toluene, SO 2 extract oil and mixtures thereof.

Claim 4

A process in accordance with claim 1 wherein said carbon black is oxidized by contacting the carbon black with an aqueous solution of HNO 3 as the pelleting liquid so that the mixture of carbon black and pelleting liquid contains about 2-10 wt. % of HNO 3 based on carbon black as 100%.

Claim 5

A process in accordance with claim 1 wherein said aftertreating of said carbon black-containing smoke is carried out by a late quench step and/or by the introduction of secondary air into the furnace between the main carbon black forming reaction zone and a quench location.

Claim 6

A non-carcinogenic carbon black obtained by pyrolytically in a carbon black furnace decomposing a hydrocarbon feedstock having a carbon residue of less than 0.2 weight percent such as to form a smoke containing a carbon black, severely aftertreating said smoke by subjecting it to at least one of the steps of late quenching and secondary air injection, oxidizing said carbon black and pelleting the carbon black and an aqueous pelleting liquid and drying the wet carbon black pellets at a temperature of about 500° to about 600° F., said carbon black being characterized by having a CTAB surface area of less than 80 square meters per gram, a pitting degree of 0.2 square meters per gram or more, said pitting degree being defined as the difference between the nitrogen surface area in square meters per gram and the CTAB surface area in square meters per gram, a photelometer of 100% and a content of benzene extractables of less than 0.05 weight percent.

Claim 7

A non-carcinogenic carbon black obtained by pyrolytically in a carbon black furnace decomposing a hydrocarbon feedstock having a carbon residue of less than 0.2 weight percent such as to form a smoke containing a carbon black, severely aftertreating said smoke by subjecting it to at least one of the steps of late quenching and secondary air injection, oxidizing said carbon black and pelleting the carbon black and an aqueous pelleting liquid and drying the wet carbon black pellets at a temperature of about 500° to about 600° F., said carbon black being characterized by having a CTAB surface area of less than 80 square meters per gram, a pitting degree of 0.2 square meters per gram or more, said pitting degree being defined as the difference between the nitrogen surface area in square meters per gram and the CTAB surface area in square meters per gram, a photelometer of 100% and a content of benzene extractables of less than 0.05 weight percent.

Claim 8

A polymer composition consisting essentially of 100 parts by weight of a polymer selected from the group of rubbers and thermoplastic polymers and 1 to 200 parts by weight of carbon black of claim 5 per 100 parts by weight of rubber and 0.1 to 50 parts by weight of carbon black per 100 parts by weight of thermoplastic polymer.

Claim 9

A composition in accordance with claim 6 comprising 20 to 80 parts by weight of carbon black and 100 parts by weight of rubber.