Process for the production of nonflammable laminated materials
Assignee: Dynamit Nobel AG
•
Filing: 1975-06-04
•
Granted: 1978-02-14
•
Expires: 1995-06-04
Abstract
Abstract A process for producing nonflammable laminated materials which includes the steps of impregnating a cellulose-containing material with an impregnating solution containing a phenolic-resol resin solution, at least one plasticizer for the resin and optionally flameproofing agents, subsequently drying the impregnated material to effect preliminary condensation of the resin and thereafter curing superimposed layers of the impregnated and preliminary condensed material by the application of heat and pressure. The phenol-resol resin solution used contains 50-80% by weight of an ammonia alkaline-condensed phenol-resol resin with a solids content of 65-80% by weight and with a molecular weight distribution determined by gel chromatography of: dimers 20-26%; tri- and tetramers 6-12%; penta- and oligomers 24-36%; expressed in percent per unit area and hexamethylenetetramine in amounts of 1-15% by weight based on the weight of the impregnating solution.
Inventors
- 👤 Arnold Franz
- 👤 Siegfried Koepnick
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 23:50
CPC Classifications
C; C08; C08G; C08G8/00; C08G8/04; C08G8/08; C08G8/10; B; B32; B32B; B32B29/00; B32B29/002; B32B29/005; C08L; C08L1/00; C08L1/02; D; D21; D21H; D21H17/00; D21H17/71; D21H17/74; D21H21/00; D21H21/14; D21H21/34; D21H27/00; D21H27/30; D21H5/00; D21H5/0002; B32B2260/00; B32B2260/02; B32B2260/028; B32B2260/04; B32B2260/046; B32B2307/00; B32B2307/30; B32B2307/306; B32B2307/3065; B32B2317/00; B32B2317/12; B32B2317/125; H; H05; H05K; H05K1/00; H05K1/02; H05K1/03; H05K1/0313; H05K1/032; H05K1/0326; Y; Y10; Y10S; Y10S428/00; Y10S428/92; Y10S428/921; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31942; Y10T428/31949; Y10T428/31964; Y10T428/31967; Y10T428/31971; Y10T428/31975; Y10T428/31978; Y10T428/31982
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
149 words
In a process for the production of nonflammable laminated materials by the impregnation of cellulose-containing material with an impregnating solution containing a phenolic-resol resin solution, and at least one plasticizer, subsequently drying the thus-impregnated material under preliminary condensation of the resin, and thereafter curing superimposed layers of this impregnated and preliminarily condensed material with the use of heat and pressure, the improvement wherein there is used an impregnating solution containing: a. 50 to 80% by weight of an ammonia alkaline-condensed aqueous phenol-resol resin with a solids content of 65-80% by weight and with following molecular weight distribution determined by gel chromatography (expressed in percent per unit area): dimers 20-26%; tri- and tetramers 6-12%; penta- and oligomers 24-36%; b. hexamethylenetetramine in amounts of 1-15% by weight and c. between 15 and 35% by weight of a phosphoric acid ester as the plasticizer, based on the weight of the impregnating solution.
Claim 2
Dependent Claim
149 words
In a process for the production of nonflammable laminated materials by the impregnation of cellulose-containing material with an impregnating solution containing a phenolic-resol resin solution, and at least one plasticizer, subsequently drying the thus-impregnated material under preliminary condensation of the resin, and thereafter curing superimposed layers of this impregnated and preliminarily condensed material with the use of heat and pressure, the improvement wherein there is used an impregnating solution containing: a. 50 to 80% by weight of an ammonia alkaline-condensed aqueous phenol-resol resin with a solids content of 65-80% by weight and with following molecular weight distribution determined by gel chromatography (expressed in percent per unit area): dimers 20-26%; tri- and tetramers 6-12%; penta- and oligomers 24-36%; b. hexamethylenetetramine in amounts of 1-15% by weight and c. between 15 and 35% by weight of a phosphoric acid ester as the plasticizer, based on the weight of the impregnating solution.
Claim 3
Dependent Claim
37 words
A process according to claim 1, wherein the improvement further comprises curing the layers for a time ranging from 30 to 90 minutes at a temperature of 130°-180° C. and a pressure of 70-180 kp./cm 2 .
Claim 4
Dependent Claim
11 words
A nonflammable laminated material produced by the process of claim 1.
Claim 5
Dependent Claim
24 words
A process according to claim 1, wherein the phosphoric acid ester is an ester of phosphoric acid with an aliphatic alcohol or a phenol.
Claim 6
Dependent Claim
30 words
A process according to claim 4, wherein the aliphatic alcohol is a mono- or poly- hydric alcohol containing 4-18 carbon atoms and the phenol is phenol or a methyl phenol.
Claim 7
Dependent Claim
23 words
A process according to claim 1, wherein said phosphoric acid ester is tributyl phosphate, tri (2-ethylhexyl)phosphate, triphenyl phosphate, tricresyl phosphate, or diphenylcresyl phosphate.
Claim 8
Dependent Claim
26 words
A process according to claim 1, wherein said impregnating solution further contains a flameproofing agent, the amount of phosphoric acid ester being from 15-25% by weight.
Claim 9
Dependent Claim
13 words
A process according to claim 7, wherein the flameproofing agent is pentabromodiphenyl ether.
Claim 10
Dependent Claim
22 words
A process according to claim 1, wherein said impregnating solution contains from 25 to 35% by weight of said phosphoric acid ester.
Claim 11
Dependent Claim
177 words
In a process for the production of nonflammable laminated materials by the impregnation of cellulose-containing material with an impregnating solution containing a phenol-resol resin solution and at least one plasticizer, subsequently drying the thus-impregnated material under preliminary condensation of the resin and thereafter securing superimposed layers of this impregnated and preliminarily condensed material with the use of heat and pressure, the improvement wherein said impregnating solution consists essentially of: a. 50 to 80% by weight of an ammonia alkaline-condensed aqueous phenol-resol resin with a solids content of 65-80% by weight and with the following molecular weight distribution determined by gel chromatography (expressed in percent per unit area): dimers 20-26%; tri- and tetramers 6-12%; penta- and oligomers 24-36%; b. 1-15% by weight of hexamethylenetetramine; c. between 15 and 35% by weight of a phosphoric acid ester as the plasticizer, based on the weight of the impregnating solution, and curing of said superimposed layers is effected for a time ranging from 30 to 90 minutes at a temperature of 130°-180° C. at a pressure of 7-180 kp./cm 2 .
Claim 12
Dependent Claim
177 words
In a process for the production of nonflammable laminated materials by the impregnation of cellulose-containing material with an impregnating solution containing a phenol-resol resin solution and at least one plasticizer, subsequently drying the thus-impregnated material under preliminary condensation of the resin and thereafter securing superimposed layers of this impregnated and preliminarily condensed material with the use of heat and pressure, the improvement wherein said impregnating solution consists essentially of: a. 50 to 80% by weight of an ammonia alkaline-condensed aqueous phenol-resol resin with a solids content of 65-80% by weight and with the following molecular weight distribution determined by gel chromatography (expressed in percent per unit area): dimers 20-26%; tri- and tetramers 6-12%; penta- and oligomers 24-36%; b. 1-15% by weight of hexamethylenetetramine; c. between 15 and 35% by weight of a phosphoric acid ester as the plasticizer, based on the weight of the impregnating solution, and curing of said superimposed layers is effected for a time ranging from 30 to 90 minutes at a temperature of 130°-180° C. at a pressure of 7-180 kp./cm 2 .
References Cited (Backward Citations)
US2193941A
Cited
US2801672A
Cited
US2817386A
Cited
US2941918A
Cited
US2937159A
Cited
US2956037A
Cited
US3133034A
Cited
US3377317A
Cited
US3843575A
Cited
US3715310A
Cited
US3922459A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-02-13 | 1981-08-15 | 1982-02-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-02-13 | 1985-08-15 | 1986-02-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-02-13 | 1989-08-15 | 1990-02-14 | $7700.00 | Window Closed / Lapsed |