Composition for the activation of resinous bodies for adherent metallization
Assignee: AMP-AKZO Corp A CORP OF
•
Filing: 1977-02-28
•
Granted: 1978-02-14
•
Expires: 1997-02-28
Abstract
Abstract Securely bonded layers of electroless metals on bodies having a resinous surface are provided after first contacting the surface of the body with a highly active, easily controllable, readily disposable composition comprising water, permanganate ion and manganate ion, the molar ratio of manganate to permanganate being up to about 1.2 and the composition having a pH controlled in the range of 11 to 13. Means to regenerate the composition and a temperature controlled in the range of 20° C. to 100° C. are also described.
Inventors
- 👤 Joseph Polichette
- 👤 Edward J. Leech
- 👤 John G. Branigan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 19:58
CPC Classifications
C; C23; C23C; C23C18/00; C23C18/16; C23C18/18; C23C18/20; C23C18/28; C23C18/30; C23C18/2006; C23C18/2026; C23C18/2033; C23C18/2046; C23C18/2073; C23C18/208; C23C18/285; H; H05; H05K; H05K3/00; H05K3/38; H05K3/381
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
54 words
A stable, readily disposable composition for treating a resinous surface to receive an adherent deposit of electrolessly formed metal, said composition comprising water, permanganate ion and manganate ion in the molar ratio of manganate ion to permanganate ion of up to 1.2, said composition having a pH in the range of 11 to 13.
Claim 2
Dependent Claim
54 words
A stable, readily disposable composition for treating a resinous surface to receive an adherent deposit of electrolessly formed metal, said composition comprising water, permanganate ion and manganate ion in the molar ratio of manganate ion to permanganate ion of up to 1.2, said composition having a pH in the range of 11 to 13.
Claim 3
Dependent Claim
35 words
A composition as defined in claim 1 wherein the ratio of manganate ion to permanganate ion and the pH are controlled either (i) by buffering or (ii) by adding a pH adjustor semicontinuously or continuously.
Claim 4
Dependent Claim
13 words
A composition as defined in claim 1 wherein the pH is about 12.5.
Claim 5
Dependent Claim
108 words
A stable, readily disposable composition for treating a resinous surface to receive an adherent deposit of electrolessly formed metal, said composition comprising water, permanganate ion and manganate ion in the molar ratio of manganate ion to permanganate ion of up to 1.2 and a buffering agent in the range of from about 2 to about 60 grams per liter selected from the group consisting of phosphorus-containing compounds, boron-containing compounds, carbonate-containing compounds, bicarbonate-containing compounds and mixtures of the foregoing in an amount at least sufficient to maintain said molar ratio of manganate ion to permanate ion and the pH of said composition within the range of 11 to 13.
Claim 6
Dependent Claim
108 words
A stable, readily disposable composition for treating a resinous surface to receive an adherent deposit of electrolessly formed metal, said composition comprising water, permanganate ion and manganate ion in the molar ratio of manganate ion to permanganate ion of up to 1.2 and a buffering agent in the range of from about 2 to about 60 grams per liter selected from the group consisting of phosphorus-containing compounds, boron-containing compounds, carbonate-containing compounds, bicarbonate-containing compounds and mixtures of the foregoing in an amount at least sufficient to maintain said molar ratio of manganate ion to permanate ion and the pH of said composition within the range of 11 to 13.
Claim 7
Dependent Claim
13 words
A composition as defined in claim 4 wherein the pH is about 12.5.
Claim 8
Dependent Claim
78 words
A stable, readily disposable composition for treating a resinous surface to receive an adherent deposit of electrolessly formed metal, said composition comprising water, permanganate ion and manganate ion in the molar ratio of manganate ion to permanganate ion of up to 1.2, the salt from which said permanganate ion is derived being in the range of from 1 gram per liter to 60 grams per liter, said composition having a pH in the range of 11 to 13.
Claim 9
Dependent Claim
78 words
A stable, readily disposable composition for treating a resinous surface to receive an adherent deposit of electrolessly formed metal, said composition comprising water, permanganate ion and manganate ion in the molar ratio of manganate ion to permanganate ion of up to 1.2, the salt from which said permanganate ion is derived being in the range of from 1 gram per liter to 60 grams per liter, said composition having a pH in the range of 11 to 13.
Claim 10
Dependent Claim
129 words
A stable, readily disposable composition for treating a resinous surface to receive an adherent deposit of electrolessly formed metal, said composition comprising water, permanganate ion and manganate ion in the molar ratio of manganate ion to permanganate ion of up to 1.2, the salt from which said permanganate ion is derived being in the range of from 1 gram per liter to 60 grams per liter, and a buffering agent in the range of from about 2 to 60 grams per liter, selected from the group consisting of phosphorus-containing compounds, boron-containing compounds, carbonate-containing compounds and mixtures of the foregoing in an amount at least sufficient to maintain said molar ratio of manganate ion to permanganate ion, the pH of said composition being within the range of 11 to 13.
Claim 11
Dependent Claim
129 words
A stable, readily disposable composition for treating a resinous surface to receive an adherent deposit of electrolessly formed metal, said composition comprising water, permanganate ion and manganate ion in the molar ratio of manganate ion to permanganate ion of up to 1.2, the salt from which said permanganate ion is derived being in the range of from 1 gram per liter to 60 grams per liter, and a buffering agent in the range of from about 2 to 60 grams per liter, selected from the group consisting of phosphorus-containing compounds, boron-containing compounds, carbonate-containing compounds and mixtures of the foregoing in an amount at least sufficient to maintain said molar ratio of manganate ion to permanganate ion, the pH of said composition being within the range of 11 to 13.
Claim 12
Dependent Claim
21 words
A composition as defined in claim 1 wherein the composition comprises from about 20 to about 50 grams/liter of potassium permanganate.
Claim 13
Dependent Claim
17 words
A composition as defined in claim 1 wherein the temperature is between about 60° and 80° C.
Claim 14
Dependent Claim
16 words
A composition as defined in claim 1 wherein the temperature is about 70° to 75° C.
Claim 15
Dependent Claim
122 words
A process for restoring the activity after extended use of a composition as defined in claim 1 and having a pH of not substantially less than about 12.5, said process comprising passing carbon dioxide into the composition until the pH is lowered to the range of about 11 to 11.5, heating the composition at a temperature of from about 80° C. to about the boiling point of said composition for a period of time sufficient to decompose any residual organic compounds which may be present and also to complete the disproportionation of manganate ion to permanganate ion and manganese dioxide, cooling the composition and adding a precipitant for carbonate ion, and removing the manganese dioxide and precipitated carbonate ion from the composition.
Claim 16
Dependent Claim
38 words
A process as defined in claim 11 wherein the precipitant for carbonate ion is calcium hydroxide or calcium oxide, and said precipitant is added in a quantity sufficient to raise the pH of said composition to about 12.5.
References Cited (Backward Citations)
US3650859A
Cited
US3652351A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-02-13 | 1981-08-15 | 1982-02-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-02-13 | 1985-08-15 | 1986-02-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-02-13 | 1989-08-15 | 1990-02-14 | $7700.00 | Window Closed / Lapsed |