Fixation of multivalent metal salts of carboxyl-containing vinyl monomers on fibrous substrates
Assignee: United States Department of Agriculture
•
Filing: 1976-04-09
•
Granted: 1978-02-07
•
Expires: 1996-04-09
Abstract
Abstract Water-soluble multivalent metal salts of carboxyl-containing vinyl monomers are polymerized in situ in fibrous substrates and fixed therein as network polymeric structures. This finish is useful for development of flame retardance, sanitizing characteristics, and other special performance qualities in fibrous compositions and fabrics.
Inventors
- 👤 Vidabelle O. Cirino
- 👤 Stanley P. Rowland
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 05:25
CPC Classifications
D; D06; D06M; D06M15/00; D06M15/19; D06M15/21; D06M15/263; Y; Y10; Y10S; Y10S428/00; Y10S428/907; Y10S428/92; Y10S428/921; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31855; Y10T428/3188; Y10T428/31895; Y10T428/31909
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
123 words
A process for preparing cellulosic or synthetic fibers having anti-bacterial properties, flame retardancy and sanitizing characteristics comprising: (a) immersing a cellulosic or synthetic fiber in an aqueous solution containing about 1-40 weight percent of a water soluble polyvalent metal salt of a carboxyl containing acrylic or vinyl monomer, about 0-3 weight percent of a water soluble polyfunctional vinyl monomer, about 0-15 weight percent of a monofunctional vinyl comomomer and about 0.03 to 3.0 weight percent of a free radical initiator; (b) squeezing the immersed fiber from step (a) to remove the excess solution; (c) curing the squeezed fiber from step (b) at a temperature of 120°-160° C.; (d) washing the cured fiber from step (c); and (e) drying the washed fiber from (d).
Claim 2
Dependent Claim
123 words
A process for preparing cellulosic or synthetic fibers having anti-bacterial properties, flame retardancy and sanitizing characteristics comprising: (a) immersing a cellulosic or synthetic fiber in an aqueous solution containing about 1-40 weight percent of a water soluble polyvalent metal salt of a carboxyl containing acrylic or vinyl monomer, about 0-3 weight percent of a water soluble polyfunctional vinyl monomer, about 0-15 weight percent of a monofunctional vinyl comomomer and about 0.03 to 3.0 weight percent of a free radical initiator; (b) squeezing the immersed fiber from step (a) to remove the excess solution; (c) curing the squeezed fiber from step (b) at a temperature of 120°-160° C.; (d) washing the cured fiber from step (c); and (e) drying the washed fiber from (d).
Claim 3
Dependent Claim
9 words
The product prepared by the process of claim 1.
Claim 4
Dependent Claim
21 words
The process of claim 1 wherein said fibers are incorporated into a woven textile prior to being wetted in step (a).
Claim 5
Dependent Claim
40 words
The process of claim 1 wherein the polyvalent metal salt is formed from an ion selected from the group consisting of calcium, barium, aluminum, vanadium, zinc, zirconium, molybdenum, cadmium, beryllium, tungsten, mercury, lead, bismuth, yttrium, and rare earth elements ions.
Claim 6
Dependent Claim
27 words
The process of claim 1 wherein the carboxyl containing acrylic or vinyl monomer is selected from the group consisting of acrylic acid, methacrylic acid and itaconic acid.
Claim 7
Dependent Claim
20 words
The process of claim 1 wherein the polyfunctional vinyl monomer is selected from the group consisting of methylenebisacrylamide, and 1,3,5-triaryloylhexahydro-s-triazine.
Claim 8
Dependent Claim
30 words
The process of claim 1 wherein the monofunctional vinyl comonomer is selected from the group consisting of acrylamide, methacrylamide, N-methylolacrylamide, N-methylolmethacrylamide, dimethyl-2-hydroxypropylaminemethacrylamide, diacetoneacrylamide, methylolated diacetone acrylamide, N-vinyl-2-pyrrolidone, hydroxyethylacrylamide, and hydroxyethylmethacrylamide.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-02-06 | 1981-08-08 | 1982-02-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-02-06 | 1985-08-08 | 1986-02-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-02-06 | 1989-08-08 | 1990-02-07 | $7700.00 | Window Closed / Lapsed |