High tensile strength elastomeric adhesive cements and laminates therefrom

Assignee: ExxonMobil Technology and Engineering Co
•
Filing: 1974-09-12
•
Granted: 1978-02-07
•
Expires: 1994-09-12
📄 Original PDF 🌐 Google Patents 🔄 Sync Now

Abstract

Abstract Adhesive contact cements of sulfonated olefinically unsaturated elastomers (sulfobutyl rubber) containing from about 0.1 to about 5.0 mol % SO3H neutralized, partially neutralized, or unneutralized, are admixed with tackifiers, i.e. phenolformaldehyde resins, polyisobutylene, alkylphenol formaldehyde resins, petroleum resins, etc. in an amount of between about 5 and about 90 phr in between about 10 and about 50 wt. % solids concentration in organic solvents. These cements are used for adhering porous or non-porous materials such as textiles, wood, cloth, sheets or strip of metals, plastics, etc. to each other. High green strength, high tensile strength, high resistance to peel, even at elevated temperatures, water impermeability, etc. characterize such adhesive layers in laminates. A preferred solvent, 90% toluene, 10% isopropyl alcohol is used in compounding the cement and preferably an organic amine, e.g. ethylamine, is used to partially or completely neutralize the sulfonated elastomer although inorganic bases may also be used for neutralization.

Inventors

  • 👤 Charles P. O'Farrell
  • 👤 John J. Higgins

Bibliographic Details

Application Number —
Jurisdiction US
Data Source google_patents
Last Synchronized 2026-11-03 20:06
CPC Classifications
B; B32; B32B; B32B7/00; B32B7/04; B32B7/12; C; C09; C09J; C09J123/00; C09J123/26; C09J123/32; B32B27/00; B32B27/12; B32B2305/00; B32B2305/02; B32B2305/026; B32B2305/10; B32B2305/18; B32B2311/00; B32B2311/24; B32B2317/00; B32B2317/10; B32B2323/00; B32B2323/10; B32B2367/00; C08; C08L; C08L2666/00; C08L2666/02; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31855; Y10T428/3188; Y10T442/00; Y10T442/30; Y10T442/3382; Y10T442/3415

Claims Analysis

Total Claims: 8
Claim 1
Independent Claim 118 words
A liquid adhesive elastomeric contact cement composition consisting of a sulfo derivative of an olefinically unsaturated butyl rubber having a viscosity average molecular weight of about 100,000 to about 450,000 containing between about 0.1 and about 5.0 mole percent of sulfo groups, and, as a tackifier, between about 5 and about 90 parts by weight of at least one organo thermoplastic resin having a softening or melting point of above 50° C., per hundred parts by weight of butyl rubber, dissolved in an organic solvent or mixture of organic solvents, said cement composition containing about 10 to about 50 weight % solids, said solvent or solvents being sufficiently volatile to substantially all evaporate at ambient temperatures and pressures.
Claim 2
Dependent Claim 118 words
A liquid adhesive elastomeric contact cement composition consisting of a sulfo derivative of an olefinically unsaturated butyl rubber having a viscosity average molecular weight of about 100,000 to about 450,000 containing between about 0.1 and about 5.0 mole percent of sulfo groups, and, as a tackifier, between about 5 and about 90 parts by weight of at least one organo thermoplastic resin having a softening or melting point of above 50° C., per hundred parts by weight of butyl rubber, dissolved in an organic solvent or mixture of organic solvents, said cement composition containing about 10 to about 50 weight % solids, said solvent or solvents being sufficiently volatile to substantially all evaporate at ambient temperatures and pressures.
Claim 3
Dependent Claim 24 words
A cement composition as in claim 1 wherein the solvent is a mixture of solvents at least one of which is a polar solvent.
Claim 4
Dependent Claim 38 words
A cement composition as in claim 2 wherein the sulfobutyl rubber has an Mv of between about 300,000 and about 450,000 and the solvent is a mixture of solvents at least one of which is a polar solvent.
Claim 5
Dependent Claim 25 words
A cement composition as in claim 1 wherein the sulfo butyl rubber is at least partially neutralized with an organic amine or an inorganic base.
Claim 6
Dependent Claim 15 words
A cement composition as in claim 4 wherein the tackifier is a phenol formaldehyde resin.
Claim 7
Dependent Claim 26 words
A cement composition as in claim 4 wherein the tackifier is a petroleum hydrocarbon resin and the solvent is a mixture of toluene and isopropyl alcohol.
Claim 8
Dependent Claim 40 words
A cement composition as in claim 5 wherein the butyl rubber contains between about 0.05 and about 2.0 mol % sulfo groups, is fully neutralized with ethyl amine, and contains about 60 parts phr of a phenol formaldehyde resin tackifier.

References Cited (Backward Citations)

US3484405A Cited
US3642728A Cited
US3801531A Cited

USPTO Annuity & Maintenance Windows

Annuity Stage Window Opens Payment Deadline Surcharge Period Until Estimated Fee Status
3.5 Years (Year 4) 1981-02-06 1981-08-08 1982-02-07 $2000.00 Window Closed / Lapsed
7.5 Years (Year 8) 1985-02-06 1985-08-08 1986-02-07 $3760.00 Window Closed / Lapsed
11.5 Years (Year 12) 1989-02-06 1989-08-08 1990-02-07 $7700.00 Window Closed / Lapsed

Assigned Categories & Tags

No categories assigned to this patent yet.

Assign Category Tag